EFEITO DA CINZA DE BIOMASSA EM SUBSTITUIÇÃO PARCIAL DO CIMENTO E DO AGREGADO NA PRODUÇÃO DE ARGAMASSAS

EFFECT OF BIOMASS ASH IN PARTIAL REPLACEMENT OF CEMENT AND AGGREGATE IN MORTAR PRODUCTION

DOI

10.5151/2594-5327-40470

Downloads

Baixar Artigo 3 Downloads

Resumo

A DEMANDA POR MATéRIAS-PRIMAS E A CONSEQUENTE REDUçãO DOS RECURSOS NATURAIS DEMONSTRARAM A NECESSIDADE DE NOVAS ABORDAGENS PARA OS MATERIAIS DE CONSTRUçãO. A OPçãO QUE TEM SE TORNADO VIáVEL é A UTILIZAçãO DE RESíDUOS EM MATERIAIS CIMENTíCIOS, POR MEIO DA INCORPORAçãO, SUBSTITUIçãO OU ADIçãO. NESSE SENTIDO, O PRESENTE TRABALHO TEM COMO OBJETIVO AVALIAR O POTENCIAL DE APROVEITAMENTO DA CINZA DE BIOMASSA - BBA PARA A PRODUçãO DE ARGAMASSAS. A BBA FOI CARACTERIZADA POR GRANULOMETRIA A LASER, FRX, DRX E MEV. AS ARGAMASSAS FORAM PRODUZIDAS COM CIMENTO PORTLAND CPV ARI E AREIA DE JAZIDA NO TRAçO 1:3, COM OS PERCENTUAIS DE SUBSTITUIçãO DO CIMENTO 5%, 10% E 15% E SUBSTITUIçãO DE AGREGADO MIúDO EM 2%, 4% E 6%. OS RESULTADOS AOS 28 DIAS NO ESTADO ENDURECIDO MOSTRAM QUE, CONSIDERANDO à RESISTêNCIA à TRAçãO NA FLEXãO, é POSSíVEL REDUZIR EM ATé 15% NO CONSUMO DE CIMENTO. Já A RESISTêNCIA à COMPRESSãO, CONSIDERANDO SUBSTITUIçãO PARCIAL DO CIMENTO PELA BBA, APRESENTOU NA ARGAMASSA COM SUBSTITUIçãO DE 10% O MELHOR PERCENTUAL DENTRE OS ESTUDADOS. NA ARGAMASSA QUE FOI SUBSTITUíDA PARCIALMENTE O AGREGADO, HOUVE REDUçãO DA RESISTêNCIA à COMPRESSãO QUANDO COMPARADO COM A ARGAMASSA DE REFERêNCIA. O MóDULO DE ELASTICIDADE DINâMICO NãO FOI AFETADO SIGNIFICATIVAMENTE.

 

THE DEMAND FOR RAW MATERIALS AND THE CONSEQUENT REDUCTION OF NATURAL RESOURCES HAVE DEMONSTRATED THE NEED FOR NEW APPROACHES TO BUILDING MATERIALS. THE OPTION THAT HAS BECOME VIABLE IS THE USE OF WASTE IN CEMENTITIOUS MATERIALS, THROUGH INCORPORATION, SUBSTITUTION OR ADDITION. IN THIS SENSE, THE PRESENT WORK AIMS TO EVALUATE THE POTENTIAL OF USING BIOMASS ASH - BBA FOR THE PRODUCTION OF MORTARS. BBA WAS CHARACTERIZED BY LASER PARTICLE SIZE, XRF, XRD, AND SEM. THE MORTARS WERE PRODUCED WITH CPV ARI PORTLAND CEMENT AND QUARRY SAND IN A 1:3 PATTERN, WITH CEMENT REPLACEMENT PERCENTAGES OF 5%, 10% AND 15% AND FINE AGGREGATE SUBSTITUTION IN 2%, 4% AND 6%. THE RESULTS AT 28 DAYS IN THE HARDENED STATE SHOW THAT, CONSIDERING THE TENSILE STRENGTH IN FLEXURAL, IT IS POSSIBLE TO REDUCE CEMENT CONSUMPTION BY UP TO 15%. ON THE OTHER HAND, THE COMPRESSIVE STRENGTH, CONSIDERING THE PARTIAL REPLACEMENT OF CEMENT BY BBA, PRESENTED THE BEST PERCENTAGE AMONG THOSE STUDIED IN THE MORTAR WITH 10% REPLACEMENT. IN THE MORTAR THAT WAS PARTIALLY REPLACED THE AGGREGATE, THERE WAS A REDUCTION IN COMPRESSIVE STRENGTH WHEN COMPARED TO THE REFERENCE MORTAR. THE DYNAMIC MODULUS OF ELASTICITY WAS NOT SIGNIFICANTLY AFFECTED.

Palavras-chave

Cinza de biomassa; Argamassa; Substituição parcial; Cinza inferior de madeira.

Biomass ash; Mortar; Partial replacement; Wood bottom ash.

Como citar

JUNIOR, GERCYR BAPTISTA; NASCIMENTO, LEILA CELIN; XAVIER, GUSTAVO DE CASTRO; AZEVEDO, AFONSO RANGEL GARCEZ DE; VIEIRA, CARLOS MAURÍCIO FONTES. EFEITO DA CINZA DE BIOMASSA EM SUBSTITUIÇÃO PARCIAL DO CIMENTO E DO AGREGADO NA PRODUÇÃO DE ARGAMASSAS , p. 137-148. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.