EFEITO DA DECOMPOSIÇÃO ESPINODAL NA DUREZA E RESISTÊNCIA À CORROSÃO DO AÇO INOXIDÁVEL DUPLEX 2304

EFFECT OF SPINODAL DECOMPOSITION ON HARDNESS AND CORROSION RESISTANCE OF DUPLEX STAINLESS STEEL 2304

Autoria

CAMPIDELI, VICTOR CARDOSO; INÁCIO, LÓREN KELLY DE PAULA; ASSUMPÇÃO, RAPHAEL FRANÇA; SANTOS, DAGOBERTO BRANDÃO; SICUPIRA, DALILA CHAVES

CAMPIDELI, VICTOR CARDOSO

Eu sou esse autor

INÁCIO, LÓREN KELLY DE PAULA

Eu sou esse autor

ASSUMPÇÃO, RAPHAEL FRANÇA

Eu sou esse autor

SANTOS, DAGOBERTO BRANDÃO

Eu sou esse autor

SICUPIRA, DALILA CHAVES

Eu sou esse autor

DOI

10.5151/2594-5327-40583

Downloads

Resumo

O AçO INOXIDáVEL DUPLEX POSSUI UMA MICROESTRUTURA COMPOSTA POR APROXIMADAMENTE PARTES IGUAIS DE AUSTENITA E FERRITA. ESSA COMBINAçãO CONFERE A ESSE MATERIAL PROPRIEDADES INTERESSANTES COMO ALTA RESISTêNCIA MECâNICA E BOA RESISTêNCIA à CORROSãO. PARA SE OBTER ESSAS PROPRIEDADES O MATERIAL SOFRE UMA LAMINAçãO, SEGUIDA DE TRATAMENTO TéRMICO DE RECOZIMENTO. O TRATAMENTO TéRMICO PODE CAUSAR A FORMAçãO DE NOVAS FASES OU UMA DECOMPOSIçãO DE CONSTITUINTES. ESTE TRABALHO TEM COMO OBJETIVO INVESTIGAR O FENôMENO DA DECOMPOSIçãO ESPINODAL EM AMOSTRAS DE AçOS DUPLEX 2304, NAS CONDIçõES COMO FORNECIDAS E LAMINADAS, SUBMETIDAS A UM PROCESSO DE ENVELHECIMENTO TéRMICO A 500°C POR 0,5 HORAS, 24 HORAS E 48 HORAS. PARA AVALIAR O EFEITO NA DUREZA E NA RESISTêNCIA à CORROSãO FORAM REALIZADAS ANáLISES MICROESTRUTURAIS, TESTES ELETROQUíMICOS E ENSAIOS DE DUREZA VICKERS. OS RESULTADOS DEMONSTRARAM QUE A LAMINAçãO A FRIO LEVOU à FORMAçãO DE UMA ESTRUTURA PANQUECADA, DE BANDAS ALTERNADAS DE FERRITA E AUSTENITA, Já O ENVELHECIMENTO LEVOU à FORMAçãO DE ESTRUTURA COM UM ASPECTO DADO COMO “MOTTLED” QUE CARACTERIZA A DECOMPOSIçãO ESPINODAL. AS AMOSTRAS MOSTRARAM MAIOR DUREZA E MAIOR GRAU DE SENSITIZAçãO PARA TEMPOS DE ENVELHECIMENTO MAIS LONGOS. TODAS AS AMOSTRAS APRESENTARAM EXCELENTE RESISTêNCIA à FORMAçãO DE PITE NO MEIO DE BORATO

DUPLEX STAINLESS STEEL HAS A MICROSTRUCTURE COMPOSED OF APPROXIMATELY EQUAL PARTS AUSTENITE AND FERRITE. THIS COMBINATION GIVES THIS MATERIAL INTERESTING PROPERTY SUCH AS HIGH MECHANICAL STRENGTH AND GOOD CORROSION RESISTANCE. TO ACHIEVE THESE PROPERTIES, THE MATERIAL UNDERGOES ROLLING, FOLLOWED BY ANNEALING HEAT TREATMENT. THE HEAT TREATMENT CAN CAUSE THE FORMATION OF NEW PHASES OR DECOMPOSITION OF CONSTITUENTS. THIS STUDY AIMS TO INVESTIGATE THE PHENOMENON OF SPINODAL DECOMPOSITION IN SAMPLES OF DUPLEX STEEL 2304, IN BOTH AS-SUPPLIED AND ROLLED CONDITIONS, SUBJECTED TO THERMAL AGING AT 500°C FOR 0.5 HOURS, 24 HOURS, AND 48 HOURS TO EVALUATE ITS INFLUENCE ON HARDNESS AND CORROSION RESISTANCE, USING MICROSTRUCTURAL ANALYSIS, ELECTROCHEMISTRY, AND VICKERS HARDNESS TESTS. THE RESULTS SHOWED THAT COLD ROLLING LED TO THE FORMATION OF A PANCAKED STRUCTURE, WITH ALTERNATING BANDS OF FERRITE AND AUSTENITE. AGING RESULTED IN THE FORMATION OF A STRUCTURE WITH A MOTTLED APPEARANCE CHARACTERISTIC OF SPINODAL DECOMPOSITION. THE SAMPLES EXHIBITED A TREND OF INCREASED HARDNESS WITH LONGER AGING TIMES AND DEGREE OF SENSITIZATION, AND ALL SAMPLES SHOWED RESISTANCE TO PITTING CORROSION IN BORATE SOLUTION

Palavras-chave

Aços duplex; Decomposição Espinodal; Envelhecimento térmico; Corrosão.

Duplex steels; Spinodal Decomposition; thermal aging; Corrosion.