EFEITO DA ESTAMPAGEM A QUENTE NA RESISTÊNCIA À CORROSÃO DO AÇO AO BORO GALVANIZADO

HOT STAMPING EFFECT ON CORROSION RESISTANCE OF GALVANIZED BORON STEEL

Autoria

Gomes, Bhetina Cunha; Martins, Thiago de Souza; Ximenes, Daniel Alexandre da Costa; Ferreira, Elivelton Alves; Moreira, Luciano Pessanha

DOI

10.5151/2594-5327-34961

Downloads

Baixar Artigo 13 Downloads

Resumo

OS AÇOS AVANÇADOS DE ALTA RESISTÊNCIA (AHSS) VÊM SENDO UTILIZADO NA INDÚSTRIA AUTOMOBILÍSTICA POR OFERECEREM RESISTÊNCIAS MECÂNICAS EM UMA CONSTRUÇÃO LEVE. PORÉM ESSES AÇOS POSSUEM PROPRIEDADES MECÂNICAS ELEVADAS E QUE COMPROMETEM AS OPERAÇÕES DE ESTAMPAGEM A FRIO. UMA SOLUÇÃO PARA ESSAS LIMITAÇÕES SERIA UTILIZAR AÇOS AO BORO COM REVESTIMENTOS GALVANIZADOS DE ZN-FE ESTAMPADOS A QUENTE. NO PROCESSO DE ESTAMPAGEM A QUENTE AS CHAPAS SÃO AUSTENITIZADAS E POSTERIORMENTE, ESTAMPADAS E TEMPERADAS SIMULTANEAMENTE. ESTE TRABALHO TEM COMO OBJETIVO AVALIAR A RESISTÊNCIA À CORROSÃO DO AÇO AO BORO COM REVESTIMENTOS GALVANIZADO A QUENTE DE ZN-FE ANTES E APÓS A ESTAMPAGEM A QUENTE. ATRAVÉS DOS ENSAIOS DE POTENCIAL EM CIRCUITO ABERTO (OCP) EM FUNÇÃO DO TEMPO EM SOLUÇÃO DE HCL 4% (M/M) FOI POSSÍVEL AVALIAR A DISSOLUÇÃO DAS DIFERENTES FASES PRESENTES NO REVESTIMENTO E A PARTIR DOS ENSAIOS DE ESPECTROSCOPIA DE IMPEDÂNCIA ELETROQUÍMICA (EIS) EM SOLUÇÃO DE NACL 0,1 MOL/L FOI POSSÍVEL AVALIAR A RESISTÊNCIA À CORROSÃO DAS DIFERENTES AMOSTRAS REVESTIDAS. OS RESULTADOS DE EIS MOSTRARAM QUE O PROCESSO DE ESTAMPAGEM DIMINUI A RESISTÊNCIA À CORROSÃO E QUE O REVESTIMENTO COM MAIOR TEOR DE ZN APRESENTOU MAIOR RESISTÊNCIA À CORROSÃO ANTES E APÓS A ESTAMPAGEM A QUENTE.

 

ADVANCED HIGH-STRENGTH STEELS (AHSS) ARE NOW WIDELY USED IN THE AUTOMOTIVE INDUSTRY FOR BODY-CAR LIGHTWEIGHT SOLUTIONS TO MEET THE ENVIRONMENTAL REQUIREMENTS OF REDUCING CO2 EMISSIONS. HOT STAMPING BORON STEELS WITH ZN-FE GALVANIZED COATINGS ARE AN ALTERNATIVE TO THE ISSUES ARISING FROM THE REDUCED FORMABILITY OF OTHER AHSS GRADES. THE BLANK IS FIRST AUSTENITIZED AND SUBSEQUENTLY STAMPED AND TEMPERED SIMULTANEOUSLY IN THIS PROCESS. THIS WORK AIMS TO INVESTIGATE THE CORROSION RESISTANCE OF A HOT-DIP GALVANIZED ZN-FE BORON STEEL SHEET BEFORE AND AFTER HOT STAMPING CONDITIONS. OPEN CIRCUIT POTENTIAL TESTING IN 4 WT.% HCL SOLUTION ALLOWED TO EVALUATE THE DISSOLUTION OF DIFFERENT PHASES PRESENT IN THE ZN-FE COATING. ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY TESTS IN 0.1 MOL/L NACL SOLUTION PERMITTED TO ASSESS THE CORROSION RESISTANCE OF DIFFERENT COATED SAMPLES. THE EIS RESULTS SHOWED THAT THE STAMPING PROCESS DECREASES CORROSION RESISTANCE AND THAT THE COATING WITH HIGHER ZN CONTENT SHOWED SUPERIOR CORROSION RESISTANCE BEFORE AND AFTER HOT STAMPING.