Título

EFEITO DA GRANULOMETRIA DO CARBURETO DE CáLCIO NO REFINO SECUNDáRIO

EFFECT OF THE CALCIUM CARBIDE GRANULOMETRY AT THE SECONDARY STEELMAKING

Autoria

Gomes, Francisco Willian da Silva

Gomes, Francisco Willian da Silva

Eu sou esse autor

DOI

10.5151/2594-5300-34975

Downloads

Resumo

NAS úLTIMAS DéCADAS, O USO DE CARBURETO DE CáLCIO, UM CONHECIDO AGENTE REDUTOR NA SIDERURGIA SECUNDáRIA, FOI AMPLAMENTE ABORDADO POR MUITOS ESTUDOS. AS PRINCIPAIS CARACTERíSTICAS BUSCADAS NESTE MATERIAL, ENTRE MUITAS OUTRAS, SãO SEU EFEITO NA REDUçãO DO POTENCIAL DE OXIDAçãO DA ESCóRIA DE PANELA, AUMENTANDO A TAXA DE RECUPERAçãO DA LIGA E REDUZINDO O NúMERO DE INCLUSõES NãO METáLICAS NO PRODUTO SEMI-ACABADO. NESTE ESTUDO FORAM TESTADOS DOIS TIPOS DE CARBURETO DE CáLCIO, UM COM GRANULOMETRIA VARIANDO DE 0-4 MM, E OUTRO VARIANDO DE 2-10 MM. O OBJETIVO FOI AVALIAR SEU EFEITO NA DESSULFURAçãO E DESOXIDAçãO, DURANTE O VAZAMENTO DO FORNO ELéTRICO A ARCO PARA A PANELA, E SOB O TRATAMENTO DO AçO NA ESTAçãO DO FORNO PANELA. OS RESULTADOS MOSTRARAM UM POTENCIAL PARA O CARBURETO DE CáLCIO DE GRãO FINO COMO AGENTE DE DESSULFURAçãO DURANTE O VAZAMENTO, CHEGANDO A 13% DE REMOçãO DE ENXOFRE DA AMOSTRA DO FORNO PARA A AMOSTRA DA PANELA, COMO DESTAQUE EM ESTUDOS ANTERIORES, DEVIDO à SUA MORFOLOGIA DO Pó. O RESULTADO DA DESOXIDAçãO FOI MELHOR RELATADO DURANTE O AJUSTE DA COMPOSIçãO QUíMICA, PARA AMBOS OS MATERIAIS, NA ESTAçãO DE PANELAS, OBTEVE-SE REDUçãO DE APROXIMADAMENTE 5 E 8 KG NAS ADIçõES DE SILíCIO E LIGA DE SILíCIO-MANGANêS, RESPECTIVAMENTE.

FOR THE PAST DECADES, THE USE OF CALCIUM CARBIDE, A WELL-KNOWN REDUCING AGENT AT THE SECONDARY STEELMAKING, WAS EXTENSIVELY COVERED BY MANY STUDIES. THE MAIN FEATURES SOUGHT ON THIS MATERIAL, AMONG MANY OTHERS, ARE ITS EFFECT ON LOWERING THE OXIDATION POTENTIAL OF THE LADLE SLAG, INCREASING THE ALLOY RECOVERY RATE, AND REDUCING THE NUMBER OF NONMETALLIC INCLUSIONS ON THE SEMI-FINISHED PRODUCT. ON THIS STUDY, TWO TYPES OF CALCIUM CARBIDE WERE TESTED, ONE WITH A GRANULOMETRY VARYING FROM 0-4 MM, AND THE OTHER VARYING FROM 2-10 MM. THE OBJECTIVE WAS TO EVALUATE THEIR EFFECT ON THE DESULFURIZATION AND DEOXIDATION, DURING THE TAPPING FROM THE ELECTRIC ARC FURNACE TO THE LADLE, AND UNDER THE STEEL TREATMENT AT THE LADLE FURNACE STATION. THE RESULTS SHOWED A POTENTIAL FOR THE FINE GRAIN CALCIUM CARBIDE AS A DESULFURIZATION AGENT DURING TAPPING, REACHING 13 % OF SULFUR REMOVAL FROM THE FURNACE SAMPLE TO THE LADLE SAMPLE, AS HIGHLIGHT BY PAST STUDIES, DUE TO ITS POWDER MORPHOLOGY. THE DEOXIDATING RESULT WAS BETTER REPORTED DURING THE CHEMICAL COMPOSITION ADJUSTMENT, FOR BOTH MATERIALS, AT THE LADLE STATION, OBTAINED REDUCTION OF APPROXIMATELY 5 AND 8 KG IN THE SILICON AND SILICON-MANGANESE ALLOY ADDICTIONS, RESPECTIVELY.

Palavras-chave

Carbureto de Cálcio; Granulometria; Desoxidação;Dessulfuração.

Calcium carbide; Granulometry; Deoxidating; Desulfurization.