UMA BOA BIOCOMPATIBILIDADE E RESISTêNCIA à CORROSãO ALIADAS A PROPRIEDADES MECâNICAS ADEQUADAS TORNAM O TITâNIO (TI) COMERCIALMENTE PURO (CP) EM UM MATERIAL AMPLAMENTE UTILIZADO NA ENGENHARIA BIOMéDICA E NA INDúSTRIA. AS PLACAS DE TI DE ALTA PUREZA POSSUEM MENOR RESISTêNCIA MECâNICA DO QUE AS LIGAS DESTE METAL. ASSIM, MATERIAIS COM MICROESTRUTURA HETEROGêNEA CONSTITUEM UM CAMPO EMERGENTE E PROMISSOR PARA O PROJETO DE PROPRIEDADES MECâNICAS ATRAVéS DE ROTAS ECONôMICAS. A FIM DE APRIMORAR AS PROPRIEDADES MECâNICAS DESSES MATERIAIS, NESTE TRABALHO FOI UTILIZADA A RECRISTALIZAçãO PARCIAL PARA AUMENTAR A DUCTILIDADE E RESISTêNCIA DO TI CP. APóS O RECOZIMENTO POR 30 MIN, DE UMA MICROESTRUTURA LAMINADA A FRIO EM 66%, OCORREU O AUMENTO DAS PROPRIEDADES MECâNICAS PARA TEMPERATURAS DE RECOZIMENTO 600°C-700°C. O TI CP APRESENTA MAIOR DUREZA PARA A CONDIçãO RECOZIDA EM RELAçãO à AMOSTRA FORNECIDA. A PARTIR DE CURVAS DE TENSãO-DEFORMAçãO DE ENGENHARIA E ANáLISE DA MICROESTRUTURA é EXPLICADO O COMPORTAMENTO MECâNICO DO MATERIAL.
GOOD BIOCOMPATIBILITY AND CORROSION RESISTANCE COUPLED WITH SUITABLE MECHANICAL PROPERTIES MAKE PURE TITANIUM (TI) A WIDELY USED MATERIAL IN BIOMEDICAL ENGINEERING AND INDUSTRY. HIGH-PURITY TI PLATES HAVE LOWER MECHANICAL STRENGTH THAN TI ALLOYS. THUS, HETEROSTRUCTURED MATERIALS CONSTITUTE AN EMERGING AND PROMISING FIELD TO DRIVE MECHANICAL PROPERTIES THROUGH ECONOMIC ROUTES. TO IMPROVE THE MECHANICAL PROPERTIES OF THIS MATERIAL, IN THIS WORK IT WAS USED THE PARTIAL RECRYSTALLIZATION TO IMPROVE THE DUCTILITY AND STRENGTH OF THE METAL. AFTER ANNEALING FOR 30 MIN OF A COLD-ROLLED MICROSTRUCTURE AT 66%, THE MECHANICAL PROPERTIES INCREASED FOR TEMPERATURES OF 600°C-800°C. CP TI HAD A HIGHER HARDNESS FOR THE ANNEALED CONDITION COMPARED TO THE SAMPLE AS RECEIVED. FROM ENGINEERING STRESS-STRAIN CURVES, TWO ANNEALING CONDITIONS ALLOWED TO OBTAIN A HIGH UNIFORM STRAIN, HIGH DUCTILITY, AND A MODERATE STRENGTH.
Palavras-chave
Titânio; Laminação a frio; Transformação de fase; Martensíta
Commercially pure titanium; Cold rolling; Phase transformation; Martensite; Annealing
Como citar
OLIVEIRA, ANNA JÚLIA CASSIMIRO PRADO MITRE DE;
SAKAI, ARTHUR BARREIRO;
OLIVEIRA, ISABELA GIOVANA;
SOUZA, SOFIA DA CRUZ;
CORREIA, RICARDO OLIVEIRA;
JESUS, ANDERSON CAIRES DE;
SANTOS, DAGOBERTO BRANDÃO.
EFEITO DA LAMINAÇÃO A FRIO E RECOZIMENTO NA MICROESTRUTURA DO TITÂNIO COMERCIALMENTE PURO DE GRAU II CONTENDO MARTENSITA αLFA'
,
p. 91-104.
In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas,
São Paulo, Brasil,
2024.
ISSN: 2594-4711
, DOI 10.5151/2594-4711-40651