Título

EFEITO DA TEMPERATURA DE AUSTENITIZAÇÃO INTERCRÍTICA NAS TEMPERATURAS CRÍTICAS DE TRANSFORMAÇÃO MARTENSÍTICA DE UM AÇO INOXIDÁVEL UNS S41003

EFFECT OF INTERCRITICAL AUSTENITIZING TEMPERATURE ON THE CRITICAL MARTENSITIC TRANSFORMATION TEMPERATURES IN A UNS S41003 STAINLESS STEEL

Autoria

Faria, Geraldo Lucio de; Oliveira, Daynara Faustina Moreira de; Moreira, Paulo Sérgio

Faria, Geraldo Lucio de

Eu sou esse autor

Oliveira, Daynara Faustina Moreira de

Eu sou esse autor

Moreira, Paulo Sérgio

Eu sou esse autor

DOI

10.5151/2594-5327-34827

Downloads

Resumo

O AÇO INOXIDÁVEL FERRÍTICO UNS S41003 (410D) ESTÁ SENDO OFERECIDO NO MERCADO COMO UMA SOLUÇÃO PRÁTICA DE DESEMPENHO PARA DIVERSAS APLICAÇÕES. RECENTEMENTE, FOI OBSERVADO QUE A COMBINAÇÃO DE UMA MICROESTRUTURA BIFÁSICA, COMPOSTA POR FERRITA E MARTENSITA FOI CONSIDERADA UMA ALTERNATIVA INTERESSANTE PARA A MELHORIA DO DESEMPENHO MECÂNICO DESSE AÇO. SENDO ASSIM, ESTE TRABALHO SE PROPÔS A AVALIAR O EFEITO DA TEMPERATURA DE AUSTENITIZAÇÃO INTERCRÍTICA SOBRE AS TEMPERATURAS DE INÍCIO (MS) E FINAL (MF) DE TRANSFORMAÇÃO MARTENSÍTICA DO AÇO UNS S41003, UTILIZANDO COMO TÉCNICA DE ANÁLISE A DILATOMETRIA. NESTE CASO, DIFERENTES AMOSTRAS FORAM AQUECIDAS A UMA TAXA DE 3°C/S PARTINDO DA TEMPERATURA AMBIENTE ATÉ DIFERENTES CONDIÇÕES DE AUSTENITIZAÇÃO INTERCRÍTICA, NAS QUAIS PERMANECERAM POR 5 MINUTOS, SENDO EM SEGUIDA, RESFRIADAS À UMA TAXA DE 100°C/S. OS RESULTADOS MOSTRARAM QUE O AUMENTO DA TEMPERATURA DE AUSTENITIZAÇÃO INTERCRÍTICA DE 850°C PARA 950°C PROMOVEU UM ACRÉSCIMO DE APROXIMADAMENTE 27°C EM MS E 25°C EM MF. PORTANTO, PODE-SE AFIRMAR QUE AS TEMPERATURAS CRÍTICAS (MS E MF) FORAM SIGNIFICATIVAMENTE AFETADAS PELA CONDIÇÃO DE AUSTENITIZAÇÃO. O AUMENTO DA TEMPERATURA DE AUSTENITIZAÇÃO INTERCRÍTICA FAVORECEU A FORMAÇÃO DA MARTENSITA, PROPORCIONANDO UM AUMENTO DA MICRODUREZA DO MATERIAL.

UNS S41003 (410D) FERRITIC STAINLESS STEEL IS BEING OFFERED IN THE MARKET AS A GREAT PERFORMANCE SOLUTION FOR VARIOUS APPLICATIONS. RECENTLY, IT WAS OBSERVED THAT THE USE OF A BIPHASIC MICROSTRUCTURE, COMPOSED OF FERRITE AND MARTENSITE, WAS CONSIDERED AN INTERESTING ALTERNATIVE TO IMPROVE THIS STEEL MECHANICAL PERFORMANCE. IN THIS CONTEXT, THIS WORK PROPOSED TO EVALUATE THE EFFECT OF THE INTERCRITICAL AUSTENITIZING TEMPERATURE ON THE START (MS) AND END (MF) TEMPERATURES ON THE MARTENSITIC TRANSFORMATION OF A UNS S41003 STEEL TYPE, USING DILATOMETRY AS EXPERIMENTAL TOOL. IN THIS CASE, DIFFERENT SAMPLES WERE HEATED AT A RATE OF 3°C/S FROM ROOM TEMPERATURE TO DIFFERENT INTERCRITICAL AUSTENITIZING CONDITIONS, IN WHICH THEY REMAINED FOR 5 MINUTES, AND THEN THEY WERE COOLED AT A RATE OF 100°C/S. THE RESULTS SHOWED THAT THE INCREASE IN THE INTERCRITICAL AUSTENITIZING TEMPERATURE FROM 850°C TO 950°C PROMOTED AN INCREASE OF APPROXIMATELY 27°C IN MS AND 25°C IN MF. THEREFORE, IT CAN BE STATED THAT THE CRITICAL TEMPERATURES (MS AND MF) WERE SIGNIFICANTLY AFFECTED BY THE AUSTENITIZING CONDITION. THE INCREASE IN THE INTERCRITICAL AUSTENITIZING TEMPERATURE FAVORED THE FORMATION OF MARTENSITE, PROVIDING AN INCREASE IN THE MATERIAL MICROHARDNESS.

Palavras-chave

Aço UNS S41003 (410D); Austenitização Intercrítica; Transformação Martensítica, Temperaturas Crítica

UNS S41003 (410D) Steel; Intercritical Austenitizatizing; Martensitic Transformation, Critical Tempe