EFEITO DA TEMPERATURA DE ENVELHECIMENTO E TEMPO NA MICROESTRUTURA E PROPRIEDADES MECÂNICAS DO AÇO INOXIDAVEL DUPLEX 2205 DE GRÃO ULTRAFINO APÓS LAMINAÇÃO A FRIO

EFFECT OF AGEING TEMPERATURE AND TIME ON MICROSTRUCTURE AND MECHANICAL PROPERTIES IN AN ULTRAFINE GRAINED 2205 DUPLEX STAINLESS STEEL AFTER COLD ROLLING

DOI

10.5151/2594-5327-33197

Downloads

Baixar Artigo 175 Downloads

Resumo

Os aços inoxidáveis duplex combinam as propriedades mecânicas da ferrita com a resistência à corrosão da austenita. Quando submetido a tratamentos térmicos, pode haver precipitação de fases secundárias que prejudicam a resistência mecânica e à corrosão. O objetivo desse trabalho é avaliar a ocorrência de fases secundárias em um aço inoxidável duplex 2205 de grão ultrafino laminado a frio e submetido a temperaturas de recozimento de 600°C a 950°C por diferentes tempos (300-86400 s). Para identificação e quantificação das fases, foram utilizados microscopia eletrônica de varredura, difração de elétrons retroespalhados e difração de raios-x. As propriedades mecânicas foram avaliadas através de ensaios de tração e teste de microdureza Vickers. A presença de fase  e  foi observada junto ao carboneto de cromo, M23C6. A fase  foi confirmada apenas depois do tratamento à 800°C. De modo geral, o aumento do tempo de recozimento leva à uma maior precipitação das fases secundárias. À medida que a precipitação ocorreu, houve aumento da fração volumétrica de austenita e redução da fração de ferrita. Embora a resistência mecânica tenha aumentado, no geral, as propriedades mecânicas, como ductilidade, são prejudicadas pela precipitação.

 

Duplex stainless steels combine the mechanical properties of ferrite with the corrosion resistance of austenite. When this material is subjected to heat treatments, secondary phases may precipitate, resulting in severe deterioration of corrosion and mechanical properties. The goal of this work was to evaluate the occurrence of secondary phases in a cold rolled 2205 duplex stainless steel with an ultrafine grain after aging at temperatures ranging from 600°C to 950°C for different times (300-86400 s). Scanning electron microscopy (SEM) coupled with electron backscattered diffraction (EBSD) and x-ray diffraction (XRD) were used for phase identification and quantification. Mechanical properties were evaluated using tensile and Vickers microhardness tests. The presence of  and  phases was observed together chromium carbide, M23C6, and  were confirmed only after 800ºC ageing treatment. In a general way, an increase in the aging time led to a greater precipitation of the secondary phases. As precipitation occurred, there was an increase in the austenite and a decrease in the ferrite volume fractions. Although mechanical strength has increased, the overall mechanical properties, such as ductility, were impoverished as the precipitation proceeded.

Palavras-chave

Aço inoxidável duplex; Fase sigma; Recozimento; Textura.

Duplex; stainless steel; Sigma phase; Aging; Texture.

Como citar

Maria, Graziele Gianini Braga; Viana, Nayara Aparecida Lopes; Inácio, Lóren Kelly de Paula; Melo, Renata de Oliveira; Wolf, Witor; Santos, Dagoberto Brandão. EFEITO DA TEMPERATURA DE ENVELHECIMENTO E TEMPO NA MICROESTRUTURA E PROPRIEDADES MECÂNICAS DO AÇO INOXIDAVEL DUPLEX 2205 DE GRÃO ULTRAFINO APÓS LAMINAÇÃO A FRIO , p. 368-378. In: 74º Congresso Anual da ABM, São Paulo, 2019.