Título

EFEITO DA TEMPERATURA DE RECOZIMENTO NAS PROPRIEDADES MECÂNICAS E ELETROQUÍMICAS DO AÇO INOXIDÁVEL DUPLEX 2205

EFFECT OF THE ANNEALING TEMPERATURE ON MECHANICAL AND ELECTRICAL PROPERTIES OF THE DUPLEX STAINLESS STEEL 2205

Autoria

Silva, Amanda de Paiva; Assumpção, Raphael França; Santos, Dagoberto Brandão; Sicupira, Dalila Chaves

DOI

10.5151/2594-5327-34371

Downloads

Baixar Artigo 30 Downloads

Resumo

OS AÇOS INOXIDÁVEIS DUPLEX (AID) SÃO UMA CLASSE DE AÇOS INOXIDÁVEIS COMPOSTA POR PROPORÇÕES, APROXIMADAMENTE IGUAIS, DE FERRITA E AUSTENITA, Α E ɤ, RESPECTIVAMENTE. SÃO CAPAZES DE ALIAR ELEVADA RESISTÊNCIA MECÂNICA, DUCTILIDADE, RESISTÊNCIA À CORROSÃO E SOLDABILIDADE. DESSA FORMA, PODEM SER EMPREGADOS EM DIVERSOS SEGMENTOS INDUSTRIAIS, COMO A INDÚSTRIA NUCLEAR, DE CONSTRUÇÃO CIVIL E DE FABRICAÇÃO DE PAPEL. DEPENDENDO DAS CONDIÇÕES A QUE FOR SUBMETIDO, AS PROPORÇÕES DAS FASES FORMADAS PODEM SER ALTERADAS E CONSEQUENTEMENTE SUAS PROPRIEDADES MECÂNICAS E ELÉTRICAS. SENDO ASSIM, SEU HISTÓRICO DE PRODUÇÃO E AS CONDIÇÕES DE TRATAMENTOS TERMOMECÂNICOS AS QUAIS FORAM SUBMETIDOS, DEVEM SER BEM CONHECIDOS. DESSA FORMA, O AID 2205 LAMINADO A FRIO E RECOZIDO A DIFERENTES TEMPERATURAS FOI CARACTERIZADO ATRAVÉS DE MICROSCOPIA ÓTICA (MO) E ELETRÔNICA DE VARREDURA (MEV), MICRODUREZA VICKERS, BEM COMO SEU COMPORTAMENTO ELETROQUÍMICO, EMPREGANDO-SE A TÉCNICA DE ESPECTROSCOPIA DE IMPEDÂNCIA ELETROQUÍMICA (EIE). O TRATAMENTO TERMOMECÂNICO AO QUAL O MATERIAL FOI SUBMETIDO AFETOU AS PROPRIEDADES DA CAMADA PASSIVA FORMADA NO AID 2205. SENDO QUE PARA AS AMOSTRAS RECOZIDAS, O AUMENTO NA TEMPERATURA DE RECOZIMENTO MELHOROU AS PROPRIEDADES DO FILME PASSIVO.

 

DUPLEX STAINLESS STEELS (DSS) ARE A TYPE OF STAINLESS STEELS COMPOSED OF APPROXIMATELY EQUAL PROPORTIONS OF FERRITE AND AUSTENITE, α AND ɤ, RESPECTIVELY. THEY ARE ABLE TO COMBINE HIGH MECHANICAL RESISTANCE, DUCTILITY, CORROSION RESISTANCE AND WELDABILITY. THUS, THEY CAN BE USED IN SEVERAL INDUSTRIAL SEGMENTS, SUCH AS THE NUCLEAR, CIVIL CONSTRUCTION AND PAPERMAKING INDUSTRIES. DEPENDING ON THE CONDITIONS TO WHICH IT IS SUBMITTED, THE PROPORTIONS OF THE PHASES FORMED CAN BE ALTERED AND, CONSEQUENTLY, THEIR MECHANICAL AND ELECTRICAL PROPERTIES. THEREFORE, THEIR PRODUCTION HISTORY AND THE CONDITIONS OF THERMOMECHANICAL TREATMENTS TO WHICH THEY WERE SUBMITTED, MUST BE WELL KNOWN. THUS, THE DSS 2205 COLD ROLLED AND ANNEALED AT DIFFERENT TEMPERATURES WAS CHARACTERIZED BY OPTICAL MICROSCOPY (OM) AND SCANNING ELECTRON MICROSCOPY (SEM), VICKERS MICROHARDNESS, AS WELL AS ITS ELECTROCHEMICAL BEHAVIOR, USING THE ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY TECHNIQUE (EIS). THE THERMOMECHANICAL TREATMENT TO WHICH THE ALLOY IS SUBJECTED AFFECTS THE PASSIVE LAYER FORMED IN THE DSS 2205. FOR THE ANNEALED SAMPLES, THE INCREASE IN THE ANNEALING TEMPERATURE IMPROVED THE PROPERTIES OF THE PASSIVE FILM.

Palavras-chave

Aço inoxidável duplex; Laminação a frio; Recozimento; Corrosão; AID 2205

Duplex stainless steels; Cold rolling, Annealing; Corrosion; DSS 2205