EFEITO DA TEMPERATURA DE RECOZIMENTO NO COMPORTAMENTO ELETROQUÍMICO DO TITÂNIO CO-MERCIALMENTE PURO EM SOLUÇÃO DE SALIVA ARTI-FICIAL CONTENDO ÍONS FLUORETO: EFFECT OF ANNEALING TEMPERATURE ON THE ELECTROCHEMICAL BEHAVIOR OF COMMERCI-ALLY PURE TITANIUM IN ARTIFICIAL SALIVA SOLUTION CONTAINING FLUORIDE IONS

O TITâNIO é UM METAL RECONHECIDO POR SUA RESISTêNCIA E LEVEZA, ESPECIALMENTE QUAN-DO USADO EM AMBIENTES AGRESSIVOS. SUA CAPACIDADE DE DESENVOLVER NATURALMENTE UMA CAMADA DE óXIDO, O TORNA IDEAL PARA APLICAçõES NA INDúSTRIA QUíMICA, BEM COMO EM PROCEDIMENTOS BIOMéDICOS E ODONTOLóGICOS, NAS QUAIS DURABILIDADE E RESISTêNCIA SãO ESSENCIAIS. NO ENTANTO, QUANDO SUBMETIDO A TRATAMENTOS TERMOMECâNICOS, O MESMO PODE TER SUAS PROPRIEDADES PROTETORAS NATURAIS AFETADAS, IMPACTANDO, AS-SIM, NA SUA RESISTêNCIA à CORROSãO. NESTE TRABALHO AS AMOSTRAS DE TI CP FORAM LA-MINADAS A FRIO ATé 66% DE REDUçãO E RECOZIDAS POR 30 MINUTOS EM TEMPERATURAS DE 400, 500, 600, 700, 800 E 900°C. AS PROPRIEDADES MECâNICAS FORAM QUANTIFICADAS COM BASE NA MICRODUREZA VICKERS. ALéM DISSO, AS TéCNICAS DE DIFRAçãO DE RAIOS-X (DRX) E MICROSCOPIA ELETRôNICA DE VARREDURA (MEV) FORAM UTILIZADAS PARA A DETERMI-NAçãO DAS FASES PRESENTES. POR FIM, AS AMOSTRAS FORAM SUBMETIDAS A ENSAIOS ELE-TROQUíMICOS PARA AVALIAçãO DA RESISTêNCIA à CORROSãO ANTES E APóS O TRATAMENTO TERMOMECâNICO.

TITANIUM IS A METAL KNOWN FOR ITS STRENGTH AND LIGHTNESS, ESPECIALLY WHEN USED IN AGGRESSIVE ENVIRONMENTS. ITS ABILITY TO NATURALLY DEVELOP AN OXIDE LAYER MAKES IT IDEAL FOR APPLICATIONS IN THE CHEMICAL INDUSTRY, AS WELL AS IN BIOMEDICAL AND DENTAL PROCEDU-RES, WHERE DURABILITY AND RESISTANCE ARE ESSENTIAL. HOWEVER, WHEN SUBJECTED TO THER-MOMECHANICAL TREATMENTS, IT MAY HAVE ITS NATURAL PROTECTIVE PROPERTIES AFFECTED, THUS IMPACTING ITS CORROSION RESISTANCE. IN THIS STUDY, THE SAMPLES WERE COLD ROLLED UP TO 66% REDUCTION AND ANNEALED FOR 30 MINUTES AT TEMPERATURES OF 400, 500, 600, 700, 800, AND 900°C. MECHANICAL PROPERTIES WERE QUANTIFIED BASED ON VICKERS MICRO-HARDNESS. ADDITIONALLY, X-RAY DIFFRACTION (XRD) AND SCANNING ELECTRON MICROSCOPY (SEM) TECHNIQUES WERE USED FOR THE DETERMINATION. FINALLY, THE SAMPLES WERE SUBJEC-TED TO ELECTROCHEMICAL TESTS TO EVALUATE CORROSION RESISTANCE BEFORE AND AFTER THE THERMOMECHANICAL TREATMENT.

Palavras-chave

Titânio CP; Flúor; Resistência à corrosão; Recozimento

Titanium CP; Fluoride; Corrosion resistance; Annealing.

Como citar

MARCELINO, STHEFANNY FERREIRA SANTOS; FONSECA, MARIA EDUARDA; CARMO, BRUNA LUIZA SILVA DO; SOUZA, SOFIA DA CRUZ; OLIVEIRA, ANNA JÚLIA CASSIMIRO PRADO MITRE DE; SANTOS, DAGOBERTO BRANDÃO; SICUPIRA, DALILA CHAVES; CAMPIDELLI, VICTOR CARDOSO. EFEITO DA TEMPERATURA DE RECOZIMENTO NO COMPORTAMENTO ELETROQUÍMICO DO TITÂNIO CO-MERCIALMENTE PURO EM SOLUÇÃO DE SALIVA ARTI-FICIAL CONTENDO ÍONS FLUORETO , p. 1837-1851. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-40958