EFEITO DAS ALTAS TEMPERATURAS NA ESTRUTURA DE POROS DE ARGAMASSAS DE CIMENTO PORTLAND REFORÇADAS POR FIBRAS POLIMÉRICAS: EFFECT OF HIGH TEMPERATURE ON PORE STRUCTURE OF PORTLAND CEMENT MORTARS REINFORCED BY POLYMERIC FIBERS

Botelho, Ramón Alves; Tolentino, Evandro; Lameiras, Fernando Soares; Reis, Sérgio Carneiro dos

doi:10.5151/2594-5327-14925

Anais do Congresso Anual da ABM

ISSN 2594-5327

64º Congresso Anual da ABM — vol. 64, num.64 (2009)

Título

EFEITO DAS ALTAS TEMPERATURAS NA ESTRUTURA DE POROS DE ARGAMASSAS DE CIMENTO PORTLAND REFORÇADAS POR FIBRAS POLIMÉRICAS

EFFECT OF HIGH TEMPERATURE ON PORE STRUCTURE OF PORTLAND CEMENT MORTARS REINFORCED BY POLYMERIC FIBERS

Autoria

Botelho, Ramón Alves; Tolentino, Evandro; Lameiras, Fernando Soares; Reis, Sérgio Carneiro dos

10.5151/2594-5327-14925

Downloads

Baixar Artigo 108 Downloads

Resumo

A degradação térmica a 300°C e 600°C de argamassas de cimento Portland foi investigada. O traço utilizado na produção das argamassas foi 1:3 e o fator água cimento foi 0,48. Análises de adsorção de nitrogênio e picnometria a hélio foram utilizadas. Foi utilizado também um modelo computacional para a avaliação qualitativa da conectividade da estrutura de poros. O modelo considera que os poros são cilíndricos. Os resultados de superfície específica obtidos por adsorção de nitrogênio revelaram a degradação das argamassas com a temperatura dos tratamentos térmicos. A amostra com fibra submetida a 300°C apresentou um maior valor de superfície específica se comparada com a amostra sem fibra. A conectividade das amostras aumentou com a temperatura dos tratamentos térmicos.

Thermal degradation of Portland cement mortars was investigated. The thermal treatment temperatures were 300°C and 600°C. The mix proportion was 1:3 and w/c ratio was 0.48. Nitrogen sorption and helium picnometry analyses were used. A geometric modeling considering pore with cylindrical shape was also used in order to do quantitative evaluation of pore structure’s connectivity. The nitrogen sorption surface area showed thermal degradation of the mortars by high temperature. The mortar produced with fiber and submitted to 300°C presented higher surface area results when compared to the mortar produced without fiber. The samples connectivity increased with thermal treatment temperature.

Palavras-chave

Adsorção de nitrogênio; Argamassa; Conectividade; Fibras; Picnometria a hélio.

Nitrogen sorption; Mortar; Connectivity; Fiber; Helium picnometry.