EFEITO DO CAMINHO DE SOLIDIFICAÇÃO NA MICROESTRUTURA E NA PRECIPITAÇÃO DE (Ti,Nb)(C,N) EM UM AÇO HTP COM BAIXO Mn-ALTO Nb : EFFECT OF THE SOLIDIFICATION PATH ON THE MICROSTRUTURE AND (Ti,Nb)(C,N) PRECIPITATION ON A HTP WITH LOW Mn HIGH Nb STEEL

Escobar, Diana Pérez; Castro, Cynthia Serra Batista; Borba, Elenice Cavichioli; Oliveira, Alisson Paulo de; Camei, Kenji; Taiss, Ed Juarez Mendes; Silva, André Luiz Vasconcellos da Costa e; Andrade, Margareth Spangler

doi:10.5151/1516-392X-30739

Anais do Congresso Anual da ABM

ISSN 2594-5327

72nd ABM Annual Congress — vol. 72, num.72 (2017)

Título

EFEITO DO CAMINHO DE SOLIDIFICAÇÃO NA MICROESTRUTURA E NA PRECIPITAÇÃO DE (Ti,Nb)(C,N) EM UM AÇO HTP COM BAIXO Mn-ALTO Nb

EFFECT OF THE SOLIDIFICATION PATH ON THE MICROSTRUTURE AND (Ti,Nb)(C,N) PRECIPITATION ON A HTP WITH LOW Mn HIGH Nb STEEL

Autoria

Escobar, Diana Pérez; Castro, Cynthia Serra Batista; Borba, Elenice Cavichioli; Oliveira, Alisson Paulo de; Camei, Kenji; Taiss, Ed Juarez Mendes; Silva, André Luiz Vasconcellos da Costa e; Andrade, Margareth Spangler

Silva, André Luiz Vasconcellos da Costa e

27 Artigos, Baixados 17194 Vezes

10.5151/1516-392X-30739

Downloads

Baixar Artigo 426 Downloads

Resumo

O efeito do caminho de solidificação de um aço High Temperature Processing (HTP) API 5L X65 com 0,09 %Nb, 0,039%C e 0,54% Mn (percentagem em massa) na segregação, microestrutura e distribuição dos precipitados de Ti,Nb(C,N) foi estudado por microscopia ótica, eletrônica de varredura (MEV) e simulação computacional (ThermoCalc e DICTRA). Os resultados foram comparados com os de um aço microligado comercial com 0,04 %Nb, 0,09%C e 0,97 %Mn. Foi encontrado que o principal parâmetro que influencia no caminho de solidificação é o teor de C, o que está de acordo com a maior micro e macrossegregação observada no aço microligado comercial, em comparação ao aço HTP.

The effect of the solidification path of a High Temperature Processing (HTP) steel API 5L X65 with 0,09 %Nb, 0,039%C and 0,54% of Mn (weight percent) on the segregation, as-cast microstructure and precipitation distribution of Ti,Nb(C,N) was studied by means of optical, scanning electron microscopy (SEM) and computational simulation (ThermoCalc and DICTRA). The results were compared with those obtained for a commercial microalloyed steel, containing 0.04 %Nb, 0,09%C and 0.97 %Mn. The results indicate that the main parameter that influences in the solidification path is the C content, which concurs with the higher micro and macrosegregation observed for the commercial microalloyed steel, compared to the HTP steel.

Palavras-chave

Caminho de solidificação, Segregação, Aços microligados, Precipitação de (Ti,Nb)(C,N).

Solidification path, Segregation, Microalloyed steels, (Ti,Nb)(C,N) precipitation.

Como citar

Escobar, Diana Pérez; Castro, Cynthia Serra Batista; Borba, Elenice Cavichioli; Oliveira, Alisson Paulo de; Camei, Kenji; Taiss, Ed Juarez Mendes; Silva, André Luiz Vasconcellos da Costa e; Andrade, Margareth Spangler. EFEITO DO CAMINHO DE SOLIDIFICAÇÃO NA MICROESTRUTURA E NA PRECIPITAÇÃO DE (Ti,Nb)(C,N) EM UM AÇO HTP COM BAIXO Mn-ALTO Nb , p. 2598-2609. In: 72nd ABM Annual Congress, São Paulo, 2017.