Resumo

NESTE ESTUDO, FOI INVESTIGADO O EFEITO DA SOLDAGEM A PONTO DE DUPLO PULSO EM AçO DUAL-PHASE DE 1000 MPA DE LIMITE DE RESISTêNCIA COM ELEVADA DUCTILIDADE ELETROGALVANIZADO (DP1000HF - HIGH FORMABILITY), COM FOCO NA MELHORIA DAS PROPRIEDADES MECâNICAS DE COMPONENTES SOLDADOS PARA O SETOR AUTOMOTIVO. FORAM APLICADAS DUAS CONDIçõES DE SOLDAGEM: CONVENCIONAL (1 PULSO) E DUPLO PULSO DE SOLDAGEM (DPS). OS RESULTADOS MOSTRARAM QUE A CONDIçãO DPS PROPORCIONOU UM AUMENTO DE APROXIMADAMENTE 100% NA CARGA MáXIMA EM TRAçãO CRUZADA, ATRIBUíDO AO REFINAMENTO MICROESTRUTURAL DA MATRIZ E A UMA MAIOR DENSIDADE DE CONTORNOS DE ALTO âNGULO NA REGIãO SOLDADA. ALéM DISSO, AMBAS AS CONDIçõES DE SOLDAGEM APRESENTARAM FRATURAS DO TIPO BOTãO E CARGA SUPERIOR AO ESPECIFICADO PELA NORMA AWS D8.1M:2007, INDICANDO A ADEQUAçãO DOS PARâMETROS PARA A SOLDAGEM DO AçO EM QUESTãO. EM SUMA, OS RESULTADOS APONTAM QUE A APLICAçãO DO DUPLO PULSO DE CORRENTE DE SOLDAGEM PODE SER UMA BOA OPçãO PARA A INDúSTRIA AUTOMOTIVA, PROPORCIONANDO GANHOS SIGNIFICATIVOS DE RESISTêNCIA MECâNICA NAS JUNTAS SOLDADAS DO AçO DP1000HF ELETROGALVANIZADO.

IN THIS STUDY, THE EFFECT OF DOUBLE-PULSE SPOT WELDING ON DUAL-PHASE STEEL WITH 1000 MPA TENSILE STRENGHT WITH HIGH DUCTILITY ELECTROGALVANIZED (DP1000HF - HIGH FORMABILITY) WAS INVESTIGATED, WITH A FOCUS ON IMPROVING THE MECHANICAL PROPERTIES OF WELDED COMPONENTS FOR THE SECTOR AUTOMOTIVE. TWO WELDING CONDITIONS WERE APPLIED: CONVENTIONAL (1 PULSE) AND DOUBLE PULSE WELDING (DPS). THE RESULTS SHOWED THAT THE DPS CONDITION PROVIDED AN INCREASE OF APPROXIMATELY 100% IN THE MAXIMUM CROSS-TENSION LOAD, ATTRIBUTED TO THE MICROSTRUCTURAL REFINEMENT OF THE MATRIX AND A GREATER DENSITY OF HIGH-ANGLE BOUNDARIES IN THE WELDED REGION. FURTHERMORE, BOTH WELDING CONDITIONS PRESENTED BUTTON-TYPE FRACTURES AND A LOAD GREATER THAN THAT SPECIFIED BY THE AWS D8.1M:2007 STANDARD, INDICATING THE ADEQUACY OF THE PARAMETERS FOR WELDING THE STEEL IN QUESTION. IN SHORT, THE RESULTS INDICATE THAT THE APPLICATION OF DOUBLE PULSE WELDING CURRENT CAN BE A GOOD OPTION FOR THE AUTOMOTIVE INDUSTRY, PROVIDING SIGNIFICANT GAINS IN MECHANICAL RESISTANCE IN WELDED JOINTS OF ELECTROGALVANIZED DP1000HF STEEL.

Palavras-chave

Aço DP1000HF; Pulsos de corrente; Resistência mecânica.

DP1000HF steel; Current pulses; Mechanical resistance.