EFEITO DO ENCHARQUE APÓS AQUECIMENTO INDUTIVO NA FORMAÇÃO DE REVESTIMENTO GALVANNEALED EM AÇOS BAKE HARDENABLE: EFFECT OF THE SOAKING AFTER THE INDUCTION HEATING ON THE GALVANNEALED COATING FORMATION ON BAKE HARDENABLE STEELS

Os modelos de tratamento de galvannealing, com encharque isotérmico após o aquecimento indutivo, permitem otimizar o aporte térmico para a formação de compostos intermetálicos Fe-Zn, o que contribui significativamente para a obtenção de revestimentos galvannealed-GA de elevada qualidade. Nesse estudo foi avaliado o efeito das condições de galvannealing na formação do revestimento GA sobre aços bake hardenable-BH. Foram realizadas, em escala de laboratório, simulações variandose o modelo de galvannealing, com ciclos isotérmicos e resfriamento imediatamente após o aquecimento indutivo, a temperatura de aquecimento, entre 525°C e 570°C, e o tempo de encharque, até 20 segundos. Em todas as simulações, além dos ciclos completos foram realizadas, também, interrupções do tratamento ao longo da etapa de encharque, através de resfriamento brusco das amostras, com o objetivo de se avaliar a microestrutura do revestimento ao longo de todo o tratamento. Para a caracterização dos revestimentos foram realizadas análises de composição química, microestrutura, perfil de composição ao longo da camada e de aderência. Os resultados permitiram determinar as características da formação do revestimento GA sobre os aços BH e estabelecer condições de galvannealing para o processamento desses aços, de forma a obter microestruturas otimizadas para as aplicações mais exigentes.

The galvannealing treatment models, with isothermal soaking after the induction heating, enables the optimization of the heat input to form Fe-Zn intermetallic compounds, which contributes significantly to obtain high quality GA coatings. In this study, the effects of galvannealing conditions in the GA coating formation on BH steels were evaluated. Simulations varying the galvannealing model with isothermal and cooling cycles immediately after the induction heating, the heating temperature between 570°C and 525°C and the soaking time until 20 seconds were performed in laboratory scale. In all simulations, in addition to the complete cycles, incomplete cycles were also performed with discontinuations during the soaking step, by quenching the samples in order to evaluate the coating microstructure throughout treatment. To characterize the coatings, analysis of chemical composition, microstructure, quantitative depth profile and adhesion were performed. The results showed the characteristics of the GA coating formation on BH steels and established the galvannealing conditions for processing these steels, in order to obtain optimized microstructures for the most demanding applications.

Palavras-chave

Aço galvannealed, Tratamento de galvannealing, Galvanização a quente

Galvannealed steel, Galvannealing treatment, Hot dip galvanizing

Como citar

Barbosa, Aldo Henrique de Almeida; Goulart-Santos, Sandra; Eleutério, Henrique Lacerda. EFEITO DO ENCHARQUE APÓS AQUECIMENTO INDUTIVO NA FORMAÇÃO DE REVESTIMENTO GALVANNEALED EM AÇOS BAKE HARDENABLE , p. 279-287. In: 52º Seminário de Laminação, Rio de Janeiro, 2015.
ISSN: 2594-5297 , DOI 10.5151/1983-4764-26676