EFEITO DO ENVELHECIMENTO SOBRE A MICROESTRUTURA E O COMPORTAMENTO DE FLUÊNCIA DO INCONEL 718

THE EFFECT OF AGING IN MICROSTRUCTURES AND CREEP BEHAVIOR OF INCONEL 718

Autoria

Hirschmann, Ana Claudia de Oliveira; Reis, Danieli Aparecida Pereira; Neto, Carlos de Moura; Pinto, Catia; Barbosa, Miguel Justino; Couto, Antônio Augusto

DOI

10.5151/2594-5327-15987

Downloads

Baixar Artigo 71 Downloads

Resumo

Superligas à base de níquel são conhecidas desde a década de 1930, e utilizadas principalmente em aplicações aeroespaciais. Estas aplicações requerem um material com elevada resistência mecânica, boa resistência à fadiga e à fluência, boa resistência à corrosão e capacidade de operar continuamente em temperaturas elevadas. A liga a base de níquel Inconel 718 tem sido investigada, pois é uma das superligas mais utilizadas. O objetivo deste trabalho foi estudar a influência da fase sobre a microestritura do Inconel 718 e o comportamento à fluência da liga. O o teste de fluência foi realizado sobre carga constante a 650 C e 750MPa. As amostras apresentam um comprimento de 18,5 mm e um diâmetro de 3,0 mm, os ensaios foram realizados de acordo com norma ASTM E139.

 

A superalloy is an alloy developed for elevated temperature service, where relatively severe mechanical stressing is encountered, and where high surface stability is frequently required. High temperature deformation of Ni-base superalloys is very important since the blades and discs of aeroengine turbine, because need to work at elevated temperature for an expected long period. The nickel-base alloy Inconel 718 has being investigated because it is one of the most widely used superalloys. This alloy is also competitively priced due to the fact that the alloy contains no cobalt and has a relatively high content of iron. The objective of this work is to evaluate The aim of the work was study the influence of the γ' and γ'' phase on the Inconel 718 microstructure and the creep behavior of the alloy. Constant load creep tests were conducted at 650°C and 750 MPa. Samples with a gage length of 18.5 mm and a 3.0 mm diameter were used for all tests. Creep tests were performed according to ASTM E139 standard.