EFEITO DO GÁS DE PROTEÇÃO NAS PROPRIEDADES DE PEÇAS DE ALTO-FORNO EM COBRE SOLDADAS PELO PROCESSO GTAW

EFFECT OF SHIELDING GAS ON THE PROPERTIES OF COPPER BLAST FURNACE PARTS WELDED BY THE GTAW PROCESS

Autoria

MONFRADINI, LUIZ CLAUDIO; TRANCOSO, RAONY COUTINHO; GALDINO, ANDRÉ GUSTAVO DE SOUSA

MONFRADINI, LUIZ CLAUDIO

Eu sou esse autor

TRANCOSO, RAONY COUTINHO

Eu sou esse autor

GALDINO, ANDRÉ GUSTAVO DE SOUSA

Eu sou esse autor

DOI

10.5151/2594-5327-41238

Downloads

Resumo

A SOLDAGEM GAS TUNGSTEN ARC WELDING (GTAW) OU TUNGSTEN INERT GAS (TIG) é UM PROCESSO QUE UTILIZA O ARGôNIO, O HéLIO OU UMA MISTURA DE AMBOS, COMO GáS DE PROTEçãO. PARA SOLDAGEM DE COBRE, UTILIZA-SE UMA MISTURA DE HéLIO E ARGôNIO, NORMALMENTE, COM HéLIO DE ALTA PUREZA, O QUE CONTRIBUI PARA SOLDA DE MELHOR QUALIDADE. ENTRETANTO, PREçOS ALTOS E VOLáTEIS, ALéM DE CRISES CONSTANTES NO FORNECIMENTO E ENTREGA, INCLUSIVE DECORRENTES DE GUERRAS, CAUSAM INSTABILIDADE NA DISPONIBILIDADE DE HéLIO. O OBJETIVO DESTE TRABALHO FOI VERIFICAR O EFEITO DE DIFERENTES MISTURAS DE ARGôNIO E HéLIO NA MICROESTRUTURA E PROPRIEDADES MECâNICAS EM PEçAS DE COBRE APLICADAS à INDúSTRIA SIDERúRGICA E SOLDADAS PELO PROCESSO GTAW, EM ESPECIAL VENTANEIRAS DE ALTOS-FORNOS. FORAM UTILIZADOS CORPOS DE PROVA COM TRêS MISTURAS DIFERENTES, SENDO MISTURA 1 (95%HE + 5%AR); MISTURA 2 (70%HE + 30%AR) E MISTURA 3 (50%HE + 50%AR). INFORMAçõES SOBRE O COMPORTAMENTO MECâNICO RESISTêNCIA A TRAçãO, DOBRAMENTO E O PERFIL DE DUREZA NãO APRESENTARAM ALTERAçõES SIGNIFICATIVAS. TAMBéM NãO FORAM ENCONTRADAS VARIAçõES CONSIDERáVEIS QUANDO AVALIADO COMPORTAMENTO DAS ESTRUTURAS CRISTALINAS

GAS TUNGSTEN ARC WELDING (GTAW) OR TUNGSTEN INERT GAS (TIG) IS A PROCESS THAT USES ARGON, HELIUM OR A MIXTURE OF BOTH AS SHIELDING GAS. FOR COPPER WELDING, A MIXTURE OF HELIUM AND ARGON IS USED, USUALLY WITH HIGH PURITY HELIUM, WHICH CONTRIBUTES TO BETTER WELD QUALITY. HOWEVER, HIGH AND VOLATILE PRICES, IN ADDITION TO CONSTANT CRISES IN SUPPLY AND DELIVERY, INCLUDING THOSE RESULTING FROM WARS, CAUSE INSTABILITY IN THE AVAILABILITY OF HELIUM. THE OBJECTIVE OF THIS STUDY WAS TO VERIFY THE EFFECT OF DIFFERENT MIXTURES OF ARGON AND HELIUM ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF COPPER PARTS APPLIED TO THE STEEL INDUSTRY AND WELDED BY THE GTAW PROCESS, ESPECIALLY TUYERE JOINTS OF BLAST FURNACE . TEST SPECIMENS WITH THREE DIFFERENT MIXTURES WERE USED, BEING MIXTURE 1 (95% HE + 5% AR); MIXTURE 2 (70% HE + 30% AR) AND MIXTURE 3 (50% HE + 50% AR). INFORMATION ON MECHANICAL STRENGTH AND HARDNESS PROFILE DID NOT SHOW SIGNIFICANT CHANGES. NO CONSIDERABLE VARIATIONS WERE FOUND WHEN THE CRYSTALLINE STRUCTURES WERE EVALUATED