EFEITO DO NIÓBIO NO COMPORTAMENTO MICROESTRUTURAL DO AÇO INOXIDÁVEL ASTM 409 BI ESTABILIZADO AO Ti E Nb EM COMPARAÇÃO A UM AÇO ASTM 409 MONO-ESTABILIZADO AO Ti

EFFECT OF NIOBIUM IN THE MICROSTRUCTURAL BEHAVIOUR IN THE STAINLESS STEEL ASTM 409 DUAL-STABILIZED BY TI AND NB COMPARED TO STEEL ASTM 409 SINGLE-STABILIZED BY TI

DOI

10.5151/1516-392X-27983

Downloads

Baixar Artigo 540 Downloads

Resumo

A estabilização do aço inoxidável ferrítico ASTM 409 na aplicação em sistemas de exaustão de automóveis é cada vez mais exigida em função do aumento das garantias e de desempenho neste sistema, particularmente em temperaturas mais elevadas dos gases de escape. O Ti é um dos elementos mais utilizado como estabilizante da estrutura ferrítica. No entanto, teores elevados deste elemento pioram as condições de lingotabilidade durante a produção do aço, aumentando a sua suscetibilidade a problemas de qualidade superficial. Desta forma, a dupla estabilização com Ti e Nb é uma solução para reduzir o teor de titânio. Assim, o objetivo deste trabalho foi investigar o efeito da adição de Nb na microestrutura por meio da comparação entre o aço ferrítico estabilizado ao Ti (409H) e bi-estabilizado ao Ti e Nb (409S). Os resultados deste trabalho mostraram que o aço 409S é afetado diretamente pela microestrutura mais deformada após laminação a quente em relação ao aço 409H, gerando maior força motriz para recristalização no recozimento final.

 

The stabilization of the ferritic stainless steel ASTM 409 in the application in automobile exhaust systems are increasingly demanded due to the increase of the performance guarantees and this system particularly at higher exhaust gas temperatures. Ti is one of the most used elements such as stabilizing the ferritic structure. However, high contents of this element worsen the conditions of castability during steel production, increasing their susceptibility to surface quality problems. Thus, the dual stabilized with Ti and Nb is a solution to reduce the titanium content. The objective of this study was to investigate the effect of adding Nb in the microstructure by comparing the ferritic steel stabilized Ti (409H) and bi-stabilized Ti and Nb (409S). The results of this study showed that 409S steel is directly affected by the more deformed microstructure after hot rolling against the 409H steel, creating greater driving force for recrystallization in the final annealing.

Palavras-chave

Aços inoxidáveis, Estabilização, ASTM 409, Recristalização

Stainless steel, Stabilization, ASTM 409, Recrystallization

Como citar

Costa, Ricardo José Gonçalves; Alves, Hélio José Batista; Oliveira, Tarcísio Reis de; Gonzalez, Berenice Mendonça. EFEITO DO NIÓBIO NO COMPORTAMENTO MICROESTRUTURAL DO AÇO INOXIDÁVEL ASTM 409 BI ESTABILIZADO AO Ti E Nb EM COMPARAÇÃO A UM AÇO ASTM 409 MONO-ESTABILIZADO AO Ti , p. 1197-1205. In: 71th ABM Annual Congress, Rio de Janeiro, 2016.