EFEITO DO RECOZIMENTO EM UMA LIGA NITICUNB LAMINADA A QUENTE NA TRANSFORMAÇÃO DE FASE E NA DUREZA

EFFECT OF ANNEALING IN A HOT ROLLED NITICUNB ALLOY ON PHASE TRANSFORMATION AND HARDNESS

Autoria

CUNHA, LUDMILA DE SOUZA; Ferreira, Maria Mariana Simões; Santos, Leandro Arruda dos

CUNHA, LUDMILA DE SOUZA

Eu sou esse autor

Ferreira, Maria Mariana Simões

Eu sou esse autor

Santos, Leandro Arruda dos

Eu sou esse autor

DOI

10.5151/2594-4711-40682

Downloads

Resumo

ESTE TRABALHO APRESENTA OS RESULTADOS DE UMA LIGA DE NITICUNB QUE FOI LAMINADA à QUENTE E POSTERIORMENTE TRATADA TERMICAMENTE. AS ANáLISES FORAM FEITAS POR MEIO DE MICROSCOPIA óPTICA DE VARREDURA (MEV), ESPECTROSCOPIA POR DISPERSãO DE ELéTRONS (EDS), DIFRAçãO DE RAIOS X (DRX), CALORIMETRIA DIFERENCIAL EXPLORATóRIA (DSC) E MICRODUREZA VICKERS. FORAM INVESTIGADAS, RESPECTIVAMENTE, AS ALTERAçõES MICROESTRUTURAIS, DISTRIBUIçãO DE ELEMENTOS QUíMICOS DAS FASES SóLIDAS, AS FASES PRESENTES E AS TRANSFORMAçõES DE FASES ASSOCIADOS à AMOSTRA LAMINADA A QUENTE E RECOZIDA. A INFLUêNCIA DO TRATAMENTO TéRMICO DIMINUI A TEMPERATURA DE TRANSFORMAçãO AUSTENíTICA DA LIGA, ALéM AUMENTAR A SOLUBILIDADE NO NB NAS FASES SóLIDAS PRESENTES E DIMINUIR A SOLUBILIDADE DO CU NA MATRIZ E NA β-NB. O RESULTANDO é UM MATERIAL MAIS DúCTIL, QUE POSSUI MAIOR CAPACIDADE DE TRABALHABILIDADE

IN THIS RESEARCH, THE RESULTS OF A NITICUNB ALLOY THAT WAS HOT ROLLED AND SUBSEQUENTLY HEAT TREATED ARE PRESENTED. THE ANALYZES WERE CARRIED OUT USING SCANNING ELECTRICAL MICROSCOPY (SEM), ELECTRON SCATTERING SPECTROSCOPY (EDS), X-RAY DIFFRACTION (XRD), DIFFERENTIAL SCANNING CALORIMETRY (DSC), AND VICKERS MICROHARDNESS, WHICH WERE USED TO INVESTIGATE, RESPECTIVELY, MICROSTRUCTURAL CHANGES, DISTRIBUTION OF CHEMICAL ELEMENTS OF SOLID PHASES, IDENTIFICATION OF PHASES PRESENT AND PHASE TRANSFORMATIONS ASSOCIATED WITH THE HOT ROLLED AND ANNEALED SAMPLE. THE INFLUENCE OF HEAT TREATMENT DECREASES THE MARTENSITIC TRANSFORMATION TEMPERATURE OF THE ALLOY, IN ADDITION TO INCREASING NB SOLUBILITY IN THE SOLID PHASES PRESENT AND DECREASING CU SOLUBILITY IN THE MATRIX AND β-NB. RESULTING IN A MORE DUCTILE MATERIAL, WHICH HAS GREATER WORKABILITY CAPACITY.

Palavras-chave

Efeito memória de forma; Recozimento; Transformação de fase.

Shape memory effect; annealing; Phase transformation.