Anais do Congresso Anual da ABM


ISSN 2594-5327

Título

EFEITO DO TEOR DE MOLIBDÊNIO NA MICROESTRUTURA DE JUNTAS SOLDADAS EM LIGAS FE-9CR-5MO

EFFECT OF MOLYBDENUM CONTENT ON JOINT WELDING MICROSTRUCTURE IN FE- 9CR-5MO ALLOY

DOI

10.5151/2594-5327-21074

Downloads

Baixar Artigo 160 Downloads

Resumo

Com o avanço tecnológico o uso de aços ferríticos vem crescendo, dentre eles destaca-se o aço 9Cr-1Mo. Com a adição de elementos de liga tem-se obtido aços com maior resistência e boa soldabilidade. O objetivo deste trabalho é estudar o efeito do teor de Mo nas alterações microestruturais, propriedades mecânicas e soldabilidade de uma nova liga 9Cr-5Mo. Com base na composição foram levantados diagramas para identificar as fases. Amostras da liga solubilizada foram caracterizadas por microscopia ótica e eletrônica de varredura. As propriedades da liga foram determinadas por ensaios mecânicos. Corpos de prova da liga foram soldadas sem e com adição de material pelo processo TIG e MIG. Foi feita análise de tamanho de grão da ZAC das ligas, caracterização microestrutural das regiões da solda, além de microdureza. Os resultados mostraram que a liga 9Cr-5Mo apresenta uma microestrutura ferrítica com grãos grandes e propriedades mecânicas superiores ao da liga 9Cr-1Mo. O teor de molibdênio favoreceu a um comportamento frágil a temperatura ambiente, contudo acima de 60ºC, as ligas tendem a apresentar um comportamento dúctil. Além da microestrutura ferrítica, as ligas apresentaram a formação de carbonetos e de martensita após a realização das soldagens. A martensita formada na liga estudada não comprometeu a soldabilidade.

 

Use of ferritic steels grows up with technological advance. Among this steels stands out 9Cr- 1Mo steel. With addition of alloy elements has been reach steels with bigger resistance and better weldability. The main of goal of this work is study effect of molybdenum content on microstructural changes, mechanical properties and weldability in a novel alloy 9Cr-5Mo. Was plot diagrams with elements presents to identify phases. A sample of solubilized alloy was taking to characterization by optical microscopy and scanning electron microscopy. The properties of alloy were determined by mechanical tests. Samples were welding without and with material addition by TIG and MIG process respectively. Analysis was made of grain size in HAZ’s alloy, microstructural characterization on weld regions and microhardness. The results obtained showed that the alloy 9Cr-5Mo presents a grain ferritic microstructure large and superior mechanical properties of 9Cr-1Mo to alloy the molybdenum content of favored to a fragile behavior at room temperature, however above 60°C, the alloy show a brittle behavior. In addition to ferritic microstructure, this alloy present carbides formation and martensite after welding. The martensite no undermined weldability.

Palavras-chave

Molibdênio; Propriedades mecânicas; Soldagem.

Molybdenum; Mechanical properties; Welding.

Como citar

Guimarães, Rodrigo Freitas; Pinheiro, Víctor Moita; Gomes, Natasha Lopes; Miranda, Hélio Cordeiro de; Abreu, Hamilton Ferreira Gomes de. EFEITO DO TEOR DE MOLIBDÊNIO NA MICROESTRUTURA DE JUNTAS SOLDADAS EM LIGAS FE-9CR-5MO , p. 1402-1414. In: 67º Congresso da ABM - Internacional / 12º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, Rio de Jabeiro, 2012.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-21074