EFEITOS DA TEMPERATURA DE MS NAS TENSõES RESIDUAIS DURANTE A SOLDAGEM: SIMULAçãO NUMéRICA POR MODELO DE TRêS BARRAS : EFFECTS OF MS TEMPERATURE ON THE RESIDUAL STRESSES DURING WELDING: NUMERICAL SIMULATION BY THE THREE-BAR MODEL

ESSE TRABALHO UTILIZA UM MODELO DE TRêS BARRAS PARA DEMONSTRAR O DESENVOLVIMENTO DE TENSõES RESIDUAIS APóS UM CICLO TéRMICO SEMELHANTE A UMA SOLDAGEM EM AçOS E A INFLUêNCIA DA TRANSFORMAçãO MARTENSíTICA PARA O ALíVIO DE TENSõES. PARA TAL, FORAM CONSTRUíDOS QUATRO MODELOS DE MATERIAIS DESCREVENDO UM AçO USISAR-80T, TRêS CONSIDERANDO A TRANSFORMAçãO MARTENSíTICA PARA DIFERENTES TEMPERATURAS DE PICO DO CICLO TéRMICO (1300°C, 1150°C E 920°C), E UM DESCONSIDERANDO A TRANSFORMAçãO MARTENSíTICA. A TRANSFORMAçãO MARTENSíTICA FOI CONSIDERADA A PARTIR DOS COEFICIENTES INSTANTâNEOS DE EXPANSãO EM FUNçãO DA TEMPERATURA, OBTIDOS A PARTIR DE ENSAIOS DILATOMETRIA DO AçO. CONCLUIU-SE QUE O AUMENTO DA TEMPERATURA DE PICO ESTá DIRETAMENTE RELACIONADO AO AUMENTO DA TEMPERATURA DE TRANSFORMAçãO MARTENSíTICA (MS) E CONSEQUENTEMENTE AO AUMENTO DAS TENSõES RESIDUAIS FINAIS NOS MODELOS. O MODELO DE MATERIAL QUE NãO CONSIDEROU A TRANSFORMAçãO MARTENSíTICA APRESENTOU OS MAIORES VALORES TENSõES RESIDUAIS FINAIS. A ABORDAGEM A PARTIR DO MODELO DE TRêS BARRAS FACILITOU A COMPREENSãO DE COMO AS PROPRIEDADES DO MATERIAL E OS PARâMETROS DO PROCESSO INFLUENCIAM NAS TENSõES RESIDUAIS RESULTANTES DE PROCESSO DE SOLDAGEM.

THIS STUDY UTILIZES A THREE-BAR MODEL TO DEMONSTRATE THE DEVELOPMENT OF RESIDUAL STRESSES AFTER A THERMAL CYCLE SIMILAR TO STEEL WELDING AND THE INFLUENCE OF MARTENSITIC TRANSFORMATION ON STRESS RELIEF. TO THIS END, FOUR MATERIAL MODELS WERE BUILT TO DESCRIBE A USISAR-80T STEEL: THREE CONSIDERING THE MARTENSITIC TRANSFORMATION FOR DIFFERENT PEAK TEMPERATURES OF THE THERMAL CYCLE (1300°C, 1150°C, AND 920°C), AND ONE DISREGARDING THE MARTENSITIC TRANSFORMATION. THE MARTENSITIC TRANSFORMATION WAS CONSIDERED BASED ON THE INSTANTANEOUS EXPANSION COEFFICIENTS AS A FUNCTION OF TEMPERATURE, OBTAINED FROM DILATOMETRY TESTS APPLIED TO THE STEEL. IT WAS CONCLUDED THAT THE INCREASE IN PEAK TEMPERATURE IS DIRECTLY RELATED TO THE INCREASE IN THE MARTENSITIC TRANSFORMATION TEMPERATURE (MS) AND CONSEQUENTLY TO THE INCREASE IN THE FINAL RESIDUAL STRESSES. THE MATERIAL MODEL THAT DID NOT CONSIDER THE MARTENSITIC TRANSFORMATION EXHIBITED THE HIGHEST FINAL RESIDUAL STRESS VALUES. THE APPROACH USING THE THREE-BAR MODEL FACILITATED THE UNDERSTANDING OF HOW MATERIAL PROPERTIES AND PROCESS PARAMETERS INFLUENCE THE RESIDUAL STRESSES RESULTING FROM THE WELDING PROCESS.

Palavras-chave

Tensões Residuais; Simulação de Modelo de Três Barras; Transformação Martensítica; Alívio de Tensões

Residual Stress; Three Bar Model Simulation; Martensitic Transformation; Stress Relief

Como citar

ABREU, SALVATORE GIULIANO PEIXOTO TROPIA DE; PORCARO, RODRIGO RANGEL; FARIA, GERALDO LUCIO DE; SOUZA, SAMUEL DA SILVA DE. EFEITOS DA TEMPERATURA DE MS NAS TENSõES RESIDUAIS DURANTE A SOLDAGEM: SIMULAçãO NUMéRICA POR MODELO DE TRêS BARRAS , p. 2193-2205. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.