Título

ELETRODEPOSIçõES E CARACTERIZAçõES DE LIGAS ZINCO-NíQUEL A PARTIR DE BANHOS CONTENDO óXIDO DE GRAFENO

ELECTRODEPOSITION AND CHARACTERIZATION OF ZINC-NICKEL ALLOYS FROM BATHS CONTAINING GRAPHENE OXIDE

Autoria

NEVES, NATHÁLIA CRISTINA LEÔNCIO; CORRÊA, SANDRO ROSA; FERREIRA, ELIVELTON ALVES

NEVES, NATHÁLIA CRISTINA LEÔNCIO

Eu sou esse autor

CORRÊA, SANDRO ROSA

Eu sou esse autor

FERREIRA, ELIVELTON ALVES

Eu sou esse autor

DOI

10.5151/2594-4711-41175

Downloads

Resumo

NESTE TRABALHO FOI AVALIADO O EFEITO DA ADIçãO DE óXIDO DE GRAFENO (OG) NO BANHO ELETROLíTICO NA MORFOLOGIA, ESTRUTURA, COMPOSIçãO E RESISTêNCIA à CORROSãO A ALTA TEMPERATURA DOS REVESTIMENTOS DE ZN-NI OBTIDOS POR ELETRODEPOSIçãO. PARA ISTO, AMOSTRAS DE AçO CARBONO FORAM REVESTIDAS A PARTIR DE BANHOS CONTENDO DIFERENTES CONCENTRAçõES DE OG E, EM SEGUIDA, SUBMETIDAS AO TRATAMENTO TéRMICO DE NORMALIZAçãO A 900°C. O EFEITO DA ADIçãO DO OG NA ELETRODEPOSIçãO E DISSOLUçãO DO REVESTIMENTO FOI AVALIADO POR VOLTAMETRIAS CíCLICAS. OS REVESTIMENTOS FORAM CARACTERIZADOS TAMBéM ANTES E APóS O TRATAMENTO TéRMICO, ATRAVéS DAS TéCNICAS DE MICROSCOPIA ELETRôNICA DE VARREDURA, ESPECTROSCOPIA DE ENERGIA DISPERSIVA E DIFRAçãO DE RAIOS X. A RESISTêNCIA à OXIDAçãO DURANTE A NORMALIZAçãO FOI AVALIADA POR MEIO DE ANáLISES TERMOGRAVIMéTRICAS. OS RESULTADOS MOSTRARAM QUE, COM O AUMENTO DA CONCENTRAçãO DE OG NO BANHO, OS REVESTIMENTOS APRESENTARAM MORFOLOGIAS UNIFORMES, COMPACTAS E RESISTENTES à OXIDAçãO, SENDO, DESTA FORMA, ADEQUADOS PARA A PROTEçãO DO AçO EM ALTAS TEMPERATURAS.

IN THIS WORK, THE EFFECT OF ADDING GRAPHENE OXIDE (GO) IN THE ELECTROLYTIC BATH ON THE MORPHOLOGY, STRUCTURE, COMPOSITION, AND RESISTANCE TO CORROSION AT HIGH TEMPERATURES OF ZN-NI COATINGS OBTAINED BY ELECTRODEPOSITION WAS EVALUATED. FOR THIS, CARBON STEEL SAMPLES WERE COATED FROM BATHS CONTAINING DIFFERENT GO CONCENTRATIONS, AND THEN SUBJECTED TO HEAT TREATMENT AT 900°C. THE GO ADDITION EFFECT IN THE ELECTRODEPOSITION AND DISSOLUTION OF THE COATING WAS EVALUATED BY CYCLIC VOLTAMMETRY. THE COATINGS WERE CHARACTERIZED BY SCANNING ELECTRON MICROSCOPY, ENERGY DISPERSIVE SPECTROSCOPY, AND X-RAY DIFFRACTION. THE OXIDATION RESISTANCE DURING HEAT TREATMENT WAS ALSO EVALUATED BY THERMOGRAVIMETRIC ANALYSIS. THE RESULTS SHOWED THAT WITH THE INCREASE OF GO CONCENTRATION IN THE BATH, THE COATINGS PRESENTED A UNIFORM AND COMPACT MORPHOLOGY, AND WERE RESISTANT TO OXIDATION, PROVING SUITABLE FOR PROTECTING THE STEEL AT HIGH TEMPERATURES.

Palavras-chave

Eletrodeposição; Revestimentos Zn-Ni; Óxido de grafeno; Corrosão a altas temperaturas

Electrodeposition; Zn-Ni coatings; Graphene oxide; Corrosion at high temperatures.