ELETRODEPOSIÇÃO DE REVESTIMENTO DE CROMO DECORATIVO OBTIDO A PARTIR DE ELETRÓLITO À BASE DE SAIS DE CROMO TRIVALENTE

ELETRODEPOSITION OF DECORATIVE CHROMIUM COATING OBTAINED FROM TRIVALENT CHROMIUM SALTS BASED ELECTROLYTES

DOI

10.5151/2594-5327-21064

Downloads

Baixar Artigo 235 Downloads

Resumo

A eletrodeposição de cromo decorativo tem sido utilizada com sucesso por mais de 80 anos e refere-se a um depósito de multi-camada, ou seja, uma fina camada de cromo é aplicada sobre um revestimento de cobre e/ou níquel. A função da camada de cromo é fornecer propriedades anti-manchas para o revestimento de níquel brilhante. Atualmente, o revestimento de cromo decorativo é utilizado na parte externa de componentes automotivos, rodas de ligas, peças e acessórios sanitários, móveis tubulares, equipamentos e bens de consumo eletrônicos. O depósito de cromo tradicional é obtido a partir de um eletrólito contendo íons de cromo hexavalente e tem uma agradável aparência branca azulada decorativa. Apesar de sua alta eficiência, estas soluções geram resíduos e poluentes cancerígenos e, consequentemente, estes devem ser banidos de uso industrial no futuro próximo. Neste trabalho, o comportamento da resistência à corrosão de revestimento de cromo decorativo, obtido a partir de eletrólitos contendo sais de cromo trivalente, e aplicado sobre depósitos de níquel, foi investigado como uma alternativa à camada decorativa obtida a partir de uma solução à base de sais de cromo hexavalente. A investigação da resistência à corrosão envolveu medidas de espectroscopia de impedância eletroquímica em solução de cloreto. A análise e interpretação dos dados permitiu inferir que o revestimento de cromo decorativo trivalente pode ser considerado promissor para substituição de revestimentos de cromo decorativo obtidos a partir de sais de cromo hexavalente.

 

Decorative chromium electroplating has been successfully used for more than 80 years and it refers to a multi-layer deposit. It consists of a thin layer of chromium applied over a copper and/or nickel coating. The purpose of the chromium layer is to provide a strong, powerful, and efficient anti-tarnish effect to the bright nickel coating. Today, chromium electroplating is used for many different and varied components, including automotive bright exterior trim and wheels, sanitary and bathroom fittings, tubular furniture and consumer electronic goods. The traditional chromium deposit is obtained from an electrolyte with hexavalent chromium ions. It presents a striking bluish white decorative appearance. Despite of its high efficiency, these solutions generate carcinogenic and pollutants residues and, consequently, they must be completed banished from industrial use in the near future. In this work, the corrosion behavior of decorative chromium obtained from trivalent electrolytes applied on nickel deposits was investigated as an alternative to decorative hexavalent chromium layer. The corrosion resistance was evaluated using electrochemical impedance spectroscopy measurements in chloride solution. The analysis and interpretation of the data showed that trivalent chromium plating technology can be considered as a promising and environmentally friendly replacement for decorative hexavalent chromium plating.

Palavras-chave

Cromo decorativo; Cromo trivalente; Eletrodeposição; Corrosão.

Decorative chromium; Trivalent chromium; Electrodeposition; Corrosion.

Como citar

Tomachuk, Célia Regina; Santos, Wagner Izaltino Alves dos; Oliveira, Marcelo; Costa, Isolda. ELETRODEPOSIÇÃO DE REVESTIMENTO DE CROMO DECORATIVO OBTIDO A PARTIR DE ELETRÓLITO À BASE DE SAIS DE CROMO TRIVALENTE , p. 1341-1351. In: 67º Congresso da ABM - Internacional / 12º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, Rio de Jabeiro, 2012.