ENSAIO DE FLEXÃO EM COMPÓSITOS DE FIBRA LONGA E ALINHADA DE PIASSAVA COM MATRIZ EPÓXI

FLEXURAL TEST IN COMPOSITES USING LONG AND ALIGNED PIASSAVA FIBERS WITH EPOXY MATRIX

Autoria

Carvalho, Juliana Peixoto Rufino Gazem de; Ribeiro, Amanda Mendes; Loyola, Rômulo Leite; Simonassi, Noan Tonini; Lopes, Felipe Perisse Duarte; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34489

Downloads

Baixar Artigo 18 Downloads

Resumo

OS MATERIAIS COMPÓSITOS TÊM SIDO AMPLAMENTE ESTUDADOS, PRINCIPALMENTE POR SEREM MUITO UTILIZADOS EM PRODUTOS DE DIVERSOS SETORES INDUSTRIAIS. DEVIDO A ESTA AMPLA UTILIZAÇÃO, PESQUISAS TÊM SIDO REALIZADAS COM O OBJETIVO DE SUBSTITUIR O USO DE FIBRAS SINTÉTICAS POR FIBRAS NATURAIS, NESTES PRODUTOS. PORTANTO, ESTE TRABALHO VISOU O ESTUDO DE FIBRAS DE PIASSAVA RECOLHIDAS DE UMA FÁBRICA DE VASSOURAS DE CAMPOS DOS GOYTACAZES-RJ COMO RESÍDUO INDUSTRIAL, EM MATRIZ EPÓXI. INICIALMENTE, AS FIBRAS FORAM LAVADAS E SECAS EM ESTUFA E, POSTERIORMENTE, TIVERAM SUA MORFOLOGIA ANALISADA COM O AUXÍLIO DE MEV. POR FIM, PLACAS DE COMPÓSITO FORAM PRODUZIDAS E CORTADAS EM DIMENSÕES RECOMENDADAS POR NORMA PARA EXECUÇÃO DE ENSAIO DE FLEXÃO ESTÁTICA. COMO RESULTADO, OBTEVE-SE O VALOR DE RESISTÊNCIA À FLEXÃO DE, APROXIMADAMENTE, 60MPA PARA 60% DE REFORÇO DE FIBRA. LOGO, CONFIRMANDO A POSSIBILIDADE DE UTILIZAÇÃO DE UM RESÍDUO PARA PRODUÇÃO DE COMPÓSITO DE QUALIDADE.

 

COMPOSITE MATERIALS HAVE BEEN WIDELY STUDIED, MAINLY BECAUSE THEY ARE WIDELY USED IN PRODUCTS FROM SEVERAL INDUSTRIAL SECTORS. DUE TO THIS WIDE USE, RESEARCH HAS BEEN CARRIED OUT WITH THE OBJECTIVE OF REPLACING THE USE OF SYNTHETIC FIBERS WITH NATURAL FIBERS, IN THESE PRODUCTS. THEREFORE, THIS WORK AIMED AT THE STUDY OF PIASSAVA FIBERS COLLECTED FROM A BROOM FACTORY IN CAMPOS DOS GOYTACAZES-RJ AS INDUSTRIAL WASTE, IN AN EPOXY MATRIX. INITIALLY, THE FIBERS WERE WASHED AND DRIED IN A STOVE AND, SUBSEQUENTLY, THEIR MORPHOLOGY WAS ANALYZED WITH THE AID OF SEM. FINALLY, COMPOSITE PLATES WERE PRODUCED AND CUT TO DIMENSIONS RECOMMENDED BY THE STANDARD FOR PERFORMING STATIC FLEXURAL TESTS. AS A RESULT, THE FLEXURAL STRENGTH VALUE OF APPROXIMATELY 60MPA WAS OBTAINED FOR 60% FIBER REINFORCEMENT. THEREFORE, CONFIRMING THE POSSIBILITY OF USING A RESIDUE FOR THE PRODUCTION OF QUALITY COMPOSITE.

Palavras-chave

Piassava; resina epóxi; ensaio de flexão; materiais compósitos.

Piassava; epoxy resin; flexural test; composite materials