ENSAIO DE ULTRAMICRODUREZA INSTRUMENTADA NAS LIGAS DE NITI PRODUZIDA POR FUSÃO SELETIVA A LASER: INSTRUMENTED ULTRAMICROHARDNESS TESTING ON NITI ALLOYS PRODUCED BY SELECTIVE LASER MELTING (SLM)

AS LIGAS DE NíQUEL-TITâNIO (NITI), CONHECIDAS POR APRESENTAREM EFEITO MEMóRIA DE FORMA (EMF) E SUPERELASTICIDADE (SE), DESTACAM-SE POR SUA RECUPERAçãO DE FORMA E RESISTêNCIA à CORROSãO. TRADICIONALMENTE, ESSAS LIGAS SãO FABRICADAS POR PROCESSOS INDUSTRIAIS QUE INCLUEM FUSãO, TRABALHO A QUENTE E A FRIO, CONFORMAçãO E TRATAMENTO TéRMICO. RECENTEMENTE, A MANUFATURA ADITIVA (AM) TEM SE DESTACADO NA PRODUçãO DE ESTRUTURAS COMPLEXAS DE NITI. NOS úLTIMOS DEZ ANOS, A AM DE METAIS EVOLUIU RAPIDAMENTE, SENDO ADOTADA POR SETORES COMO OS BIOMéDICO E AEROESPACIAL, QUE DEMONSTRARAM MELHORIAS SIGNIFICATIVAS NO DESEMPENHO DOS COMPONENTES. ENTRETANTO, AINDA Há POUCAS INFORMAçõES DETALHADAS SOBRE A MICROESTRUTURA E AS PROPRIEDADES MECâNICAS DAS LIGAS METáLICAS FABRICADAS POR AM. A FUSãO SELETIVA A LASER (FSL), PERMITE A FUSãO COMPLETA DO Pó METáLICO, RESULTANDO EM PEçAS HOMOGêNEAS. ESTE ESTUDO OBJETIVA AVALIAR A ULTRAMICRODUREZA DA LIGA DE NITI PRODUZIDA POR FSL, USANDO UMA MISTURA DE PóS ELEMENTARES DE NíQUEL OBTIDO POR OXIRREDUçãO E TITâNIO HDH.

NICKEL-TITANIUM ALLOYS (NITI), KNOWN FOR EXHIBITING SHAPE MEMORY EFFECT (SME) AND SUPERELASTICITY (SE), STAND OUT FOR THEIR SHAPE RECOVERY AND CORROSION RESISTANCE. TRADITIONALLY, THESE ALLOYS ARE MANUFACTURED THROUGH INDUSTRIAL PROCESSES INCLUDING MELTING, HOT AND COLD WORKING, SHAPING, AND HEAT TREATMENT. RECENTLY, ADDITIVE MANUFACTURING (AM) HAS EMERGED AS A PROMINENT METHOD FOR PRODUCING COMPLEX NITI STRUCTURES. OVER THE PAST DECADE, METAL AM HAS RAPIDLY ADVANCED, FINDING APPLICATIONS IN SECTORS SUCH AS BIOMEDICAL AND AEROSPACE, WHERE SIGNIFICANT PERFORMANCE ENHANCEMENTS HAVE BEEN DEMONSTRATED. HOWEVER, THERE IS STILL LIMITED DETAILED INFORMATION REGARDING THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF METAL ALLOYS MANUFACTURED BY AM. SELECTIVE LASER MELTING (SLM) ALLOWS FOR THE COMPLETE FUSION OF METAL POWDER, RESULTING IN HOMOGENEOUS PARTS. THIS STUDY AIMS TO EVALUATE THE ULTRAMICROHARDNESS OF NITI ALLOY PRODUCED BY SLM, USING A BLEND OF NICKEL ELEMENTAL POWDERS OBTAINED THROUGH OXIRREDUCTION AND TITANIUM HDH.

Palavras-chave

Fusão Seletiva a Laser; Manufatura Aditiva, NiTi; UltramicrodurezA..

Selective Laser Melting; Additive Manufacturing; NiTi; Ultramicrohardness.

Como citar

GONCALVES, DANILO ABILIO CORREA; SÉNÉCHAL, NAIARA VIEIRA LE; OLIVEIRA3, FÁBIO DA SILVA; RAMOS, RAFAEL; TEIXEIRA, RODOLFO DA SILVA; DYER, PAULO PAIVA OLIVEIRA LEITE; VASCONCELOS, GETÚLIO DE; PAULA, ANDERSAN DOS SANTOS. ENSAIO DE ULTRAMICRODUREZA INSTRUMENTADA NAS LIGAS DE NITI PRODUZIDA POR FUSÃO SELETIVA A LASER , p. 3575-3584. In: _FAUT, São Paulo, 2000.
ISSN: - , DOI 10.5151/Fault-41512