Título

ENSAIOS DE IMPACTO CHARPY E IZOD EM COMPÓSITOS DE MATRIZ POLIURETANA DERIVADA DE ÓLEO DE MAMONA REFORÇADOS COM FIBRAS DE EMBIRA

CHARPY AND IZOD IMPACT TESTING ON CASTOR OIL-DERIVED POLYURETHANE MATRIX COMPOSITES REINFORCED WITH EMBIRA FIBERS

Autoria

MAGALHÃES, MARCÔNIO PEREIRA DE

MAGALHÃES, MARCÔNIO PEREIRA DE

Eu sou esse autor

DOI

10.5151/2594-5327-40676

Downloads

Resumo

O PRESENTE ESTUDO INVESTIGA A RESISTêNCIA AO IMPACTO CHARPY E IZOD DE COMPóSITOS DE MATRIZ POLIURETANA – PU, DERIVADA DE óLEO DE MAMONA, REFORçADOS COM FIBRA DE EMBIRA-BRANCA (DAPHNOPSIS UTILIS) UTILIZANDO AS FRAçõES MáSSICAS DE 50%, 60%, 70%, 80% E 90% DE EMBIRA. AS ENERGIAS DE ABSORçãO ESPECíFICA DE IMPACTO E DE ENTALHE CHARPY PERMANECERAM CONSTANTES, COM O AUMENTO DAS FRAçõES MáSSICAS DE EMBIRA. ENQUANTO A RESISTêNCIA ESPECíFICA DE IMPACTO IZOD DOS COMPóSITOS DE 50%, 60% E 90% DE REFORçO, POR NãO APRESENTAREM DIFERENçAS ESTATíSTICAS SIGNIFICATIVAS DE SUAS MéDIAS, FOI CLASSIFICADO COMO GRUPO (A); DA MESMA FORMA, A RESISTêNCIA ESPECíFICA AO IMPACTO IZOD DOS COMPóSITO DE 60%, 70% E 80% DE REFORçO, TAMBéM, POR NãO APRESENTAREM DIFERENçAS ESTATíSTICAS SIGNIFICATIVAS DE SUAS MéDIAS, FOI CLASSIFICADO COMO GRUPO (B), SENDO A FRAçãO DE 60% DE REFORçO COMUM A AMBOS OS GRUPOS. MAS, ENERGIA DE ABSORçãO ESPECíFICA DE IMPACTO IZOD MéDIA DO GRUPO (A) MOSTROU-SE 40% MAIOR QUE A ENERGIA DE ABSORçãO DE IMPACTO IZOD MéDIA DO GRUPO (B). ENQUANTO O GRUPO (A) APRESENTOU ENERGIA DE ABSORçãO ESPECíFICA DE ENTALHE MéDIA 27% MAIOR QUE A DO GRUPO (B), EM QUE AS FRAçõES DE 50% E 60% DE EMBIRA ERAM COMUNS AOS DOIS GRUPOS.

THIS STUDY INVESTIGATES THE CHARPY AND IZOD IMPACT RESISTANCE OF POLYURETHANE MATRIX COMPOSITES DERIVED FROM CASTOR OIL, REINFORCED WITH EMBIRA-BRANCA (DAPHNOPSIS UTILIS) FIBER USING MASS FRACTIONS OF 50%, 60%, 70%, 80%, AND 90% OF EMBIRA. THE SPECIFIC IMPACT ABSORPTION ENERGIES AND CHARPY NOTCH ENERGIES REMAINED CONSTANT WITH INCREASING MASS FRACTIONS OF EMBIRA. WHILE THE SPECIFIC IZOD IMPACT RESISTANCE OF THE COMPOSITES WITH 50%, 60%, AND 90% REINFORCEMENT, DUE TO NO STATISTICALLY SIGNIFICANT DIFFERENCES IN THEIR MEANS, WAS CLASSIFIED AS GROUP (A); SIMILARLY, THE SPECIFIC IZOD IMPACT RESISTANCE OF THE COMPOSITES WITH 60%, 70%, AND 80% REINFORCEMENT, ALSO DUE TO NO STATISTICALLY SIGNIFICANT DIFFERENCES IN THEIR MEANS, WAS CLASSIFIED AS GROUP (B), WITH THE 60% REINFORCEMENT FRACTION COMMON TO BOTH GROUPS. HOWEVER, THE AVERAGE SPECIFIC IZOD IMPACT ABSORPTION ENERGY OF GROUP (A) WAS FOUND TO BE 40% HIGHER THAN THAT OF GROUP (B). ADDITIONALLY, GROUP (A) EXHIBITED AN AVERAGE SPECIFIC NOTCH ABSORPTION ENERGY 27% HIGHER THAN THAT OF GROUP (B), WITH FRACTIONS OF 50% AND 60% OF EMBIRA BEING COMMON TO BOTH GROUPS.

Palavras-chave

Embira; Resina Poliuretana, Compósitos Poliméricos; Resistência ao Impacto Charpy e Izod

Embira; Polyurethane Resin; Polymeric Composites; Charpy and Izod impact resistance