ESPUMAÇÃO DE ESCÓRIAS EM AÇOS ALTA LIGA

FOAMING SLAG PRACTICE FOR HIGH ALLOYED STEELS

Autoria

MANTOVANI, MARIO CESAR; JR, LUIZ ROBERTO MORAES

MANTOVANI, MARIO CESAR

Eu sou esse autor

JR, LUIZ ROBERTO MORAES

Eu sou esse autor

DOI

10.5151/2594-5300-41182

Downloads

Resumo

ESTE ARTIGO DESCREVE OS PRINCíPIOS E DIFERENçAS DA PRáTICA DE ESPUMAçãO DE ESCóRIAS EM FORNOS ELéTRICOS A ARCO (FEA) ENVOLVENDO AçOS DE BAIXA E ALTA LIGA. OS TRABALHOS ACERCA DA PRáTICA DA ESPUMAçãO DA ESCóRIA E RECUPERAçãO DOS ELEMENTOS DE LIGA A PARTIR DA ESCóRIA, FORAM EXECUTADOS EM ESCALA INDUSTRIAL. O íNDICE DE ESPUMAçãO DE ESCóRIA FOI MEDIDO ATRAVéS DE UM DISPOSITIVO QUE CONSIDERA OS SINAIS DAS CORRENTES DOS ELETRODOS DO FEA. FORAM COLETADAS AMOSTRAS DE AçO E ESCóRIA DURANTE E APóS O PERíODO DE SOPRO (OXIGêNIO MAIS INJEçãO DE FESI). INDEPENDENTEMENTE DO TEOR NOMINAL DE CROMO DO AçO O íNDICE DE ESPUMAçãO DA ESCóRIA AUMENTA COM A DIMINUIçãO DO TEOR DE óXIDO DE CROMO DA ESCóRIA. CASO O TEOR DE CR2O3 DA ESCóRIA SUPERE 10%, TORNA-SE DIFíCIL, MESMO COM MAIS ADIçãO DE AGENTE REDUTOR, DE MANTER O PROCESSO DE ESPUMAçãO DA ESCóRIA. ALéM DISSO, OS RESULTADOS MOSTRAM QUE A BASICIDADE DA ESCóRIA E O TEOR DE SILíCIO DO AçO (APóS O PERíODO DE SOPRO) APRESENTA UMA RELAçãO DIRETA COM RECUPERAçãO DOS ELEMENTOS DE LIGA A PARTIR DA ESCóRIA.

THIS PAPER DESCRIBES THE PRINCIPLES AND THE DIFFERENCES BETWEEN THE FOAMING SLAG PRACTICES IN ELECTRIC ARC FURNACE (EAF) FOR LOW AND HIGH ALLOYED STEELS. THE INVESTIGATIONS ABOUT THE FOAMING SLAG BEHAVIOR AND ALLOY RECOVERY FROM SLAG WERE PERFORMED IN THE INDUSTRIAL PRACTICE. THE FOAMING SLAG INDEX WAS MEASURED BY MEANS A DATA ACQUISITION ADAPTER, WHICH CONSIDERS THE CURRENT SIGNALS FROM THE ELECTRODES OF THE EAF. STEEL AND SLAG SAMPLES WERE TAKEN DURING AND AFTER THE BLOWING PERIOD (OXYGEN PLUS FESI INJECTION). INDEPENDENT ON THE CHROMIUM CONTENT OF THE STEEL THE FOAMING SLAG INDEX INCREASES AS THE CHROMIUM OXIDE CONTENT IN THE SLAG DECREASES. IF THE CHROMIUM OXIDE CONTENT IN THE SLAG IS HIGHER THAN 10 WT% CR2O3, IT BECOMES DIFFICULT EVEN WITH FURTHER REDUCING AGENT ADDITION TO GET A SUITABLE FOAMING SLAG PROCESS. IN ADDITION, THE RESULTS SHOW THAT THE SLAG BASICITY AND THE SILICON CONTENT IN THE STEEL (AFTER BLOWING PERIOD) PRESENT A DIRECT RELATION ON ALLOYING ELEMENTS RECOVERY FROM THE SLAG.

Palavras-chave

Forno elétrico a arco; escória espumante; rendimento; redução.

Electric arc furnace; foaming slag; yield; reduction.