ESTRUTURA, PROPRIEDADES E CARACTERIZAÇÃO DO AÇO INOXIDÁVEL DUPLEX S31803 SUBMETIDO AO MEIO CORROSIVO DE CLORETO FÉRRICO

STRUCTURE, PROPERTIES AND CHARACTERIZATION OF THE DUPLEX S31803 STAINLESS STEEL SUBMITTED TO THE CORROSIVE MEDIA OF FERRIC CHLORIDE

Autoria

Souza, Lucas Menezes de

Souza, Lucas Menezes de

Eu sou esse autor

DOI

10.5151/2594-5327-34148

Downloads

Resumo

NESTE TRABALHO FOI AVALIADA A INFLUÊNCIA DO MEIO CORROSIVO E DA TEMPERATURA NAS PROPRIEDADES DE RESISTÊNCIA À CORROSÃO DO AÇO INOXIDÁVEL DUPLEX S31803. O PROCESSO CORROSIVO FOI REALIZADO UTILIZANDO SOLUÇÃO DE CLORETO FÉRRICO (FECL3) 6%, À 25 E 50 °C QUE É UMA SOLUÇÃO TÍPICA QUANDO SE DESEJA AVALIAR A CORROSÃO PUNTIFORME, POR ENVOLVER ÍONS DE CLORETO. A MICROESTRUTURA DA AMOSTRA CONFORME RECEBIDA FOI ANALISADA ANTES E APÓS PROCESSO CORROSIVO UTILIZANDO AS TÉCNICAS DE MICROSCOPIA ÓTICA E CONFOCAL. EM SEGUIDA, FORAM REALIZADOS OS ENSAIOS MECÂNICOS E DE RESISTÊNCIA À CORROSÃO. A MICROESTRUTURA DO AÇO INOXIDÁVEL DUPLEX S31803 É COMPOSTA DE DUAS FASES, FERRITA E AUSTENITA, ORIENTADAS NO SENTIDO DE LAMINAÇÃO, COM UM BALANÇO APROXIMADO DE 50% EM VOLUME DAS FRAÇÕES DE FASES PRESENTES. O MEIOS CORROSIVO, NAS TEMPERATURAS DE 25 E 50 °C, PROPICIOU O DESENVOLVIMENTO DA CORROSÃO UNIFORME E DA CORROSÃO PUNTIFORME NO MATERIAL. CONSTATOU-SE QUE O AUMENTO EM 25°C NA TEMPERATURA A TAXA DE CORROSÃO POR PITES AUMENTA EM MÉDIA 35X PARA AMOSTRA SUBMETIDA AO MEIO CORROSIVO. AS AMOSTRAS QUANDO SUBMETIDA A SOLUÇÃO DE FECL3 EM DIFERENTES TEMPERATURAS, TENDEM A DIMINUIR SEUS VALORES DE PROPRIEDADES MECÂNICAS QUANDO SOFREM A CORROSÃO PUNTIFORME.

IN THIS STUDY, THE INFLUENCE OF THE CORROSIVE MEDIUM AND TEMPERATURE ON THE CORROSION RESISTANCE PROPERTIES OF S31803 DUPLEX STAINLESS STEEL WAS EVALUATED. THE CORROSIVE PROCESS WAS CARRIED OUT USING A 6% FERRIC CHLORIDE SOLUTION (FECL3), AT 25 AND 50 ° C, WHICH IS A TYPICAL SOLUTION WHEN IT IS DESIRED TO EVALUATE PUNCTIFORM CORROSION, AS IT INVOLVES CHLORIDE IONS. THE MICROSTRUCTURE OF THE SAMPLE AS RECEIVED WAS ANALYZED BEFORE AND AFTER THE CORROSIVE PROCESS USING OPTICAL AND CONFOCAL MICROSCOPY TECHNIQUES. THEN, MECHANICAL AND CORROSION RESISTANCE TESTS WERE PERFORMED. THE MICROSTRUCTURE OF S31803 DUPLEX STAINLESS STEEL IS COMPOSED OF TWO PHASES, FERRITE AND AUSTENITE, ORIENTED IN THE LAMINATION DIRECTION, WITH AN APPROXIMATE BALANCE OF 50% IN VOLUME OF THE PHASE FRACTIONS PRESENT. THE CORROSIVE MEDIUM, AT TEMPERATURES OF 25 AND 50 ° C, FAVORED THE DEVELOPMENT OF UNIFORM CORROSION AND PUNCTIFORM CORROSION IN THE MATERIAL. IT WAS FOUND THAT THE 25 ° C INCREASE IN TEMPERATURE, THE PITTING CORROSION RATE INCREASES ON AVERAGE 35X FOR SAMPLES SUBMITTED TO THE CORROSIVE MEDIUM. THE SAMPLES, WHEN SUBMITTED TO FECL3 SOLUTION AT DIFFERENT TEMPERATURES, TEND TO DECREASE THEIR VALUES ​​OF MECHANICAL PROPERTIES WHEN THEY SUFFER PUNCTIFORM CORROSION.

Palavras-chave

DUPLEX; CORROSÃO; PITES

duplex; corrosion; pites