ESTUDO COMPARATIVO DA CORROSÃO DO AÇO INOXIDÁVEL DUPLEX UNS32304 EM SOLUÇÕES ÁCIDAS: COMPARATIVE CORROSION STUDY OF DUPLEX STAINLESS STEEL UNS32304 IN ACID SOLUTIONS

A CORROSÃO É EXTREMAMENTE PREJUDICIAL AO MATERIAL, CAUSANDO GRANDES DANOS. UMA VEZ QUE NÃO DETECTADA, ELA PODE OCASIONAR A RUPTURA ABRUPTA DE UMA PEÇA, ESTRUTURA OU TUBULAÇÃO, CAUSANDO GRAVES ACIDENTES. A FIM DE REDUZIR ESSES DANOS FORAM CRIADOS MATERIAIS COM COMPOSIÇÃO QUÍMICA E MICROESTRUTURAS ADEQUADAS PARA SEREM MAIS RESISTENTES À CORROSÃO. É O CASO DOS AÇOS INOXIDÁVEIS, QUE TÊM COMO CARACTERÍSTICA CONTER NO MÍNIMO 10,5% DE CROMO EM SUA COMPOSIÇÃO. ESSE TIPO DE AÇO APRESENTA MELHOR DESEMPENHO EM RELAÇÃO AOS AÇOS COMUNS QUANDO APLICADOS EM MEIOS MAIS AGRESSIVOS, COMO NA INDÚSTRIA PETROQUÍMICA EM QUE É MUITO UTILIZADO. A FIM DE ATESTAR A SUA RESISTÊNCIA E AVALIAR O SEU COMPORTAMENTO DIANTE DE SOLUÇÕES ÁCIDAS, ESTE TRABALHO FOI DESENVOLVIDO UTILIZANDO O AÇO INOXIDÁVEL DUPLEX UNS32304 QUE FOI SUBMETIDO A DOIS TIPOS DE SOLUÇÕES ÁCIDAS, ÁCIDO SULFÚRICO E CLORÍDRICO, EM DIFERENTES CONCENTRAÇÕES. O ENSAIO DE IMERSÃO DUROU 60 DIAS E TEVE PH E DIFERENÇA DE POTENCIAL MEDIDOS SEMANALMENTE. ATRAVÉS DOS DADOS OBTIDOS, FOI POSSÍVEL CALCULAR A TAXA DE CORROSÃO DO AÇO INOXIDÁVEL, AVALIANDO O SEU COMPORTAMENTO E SUSCEPTIBILIDADE À CORROSÃO. CONCLUIU-SE QUE O AÇO INOXIDÁVEL DUPLEX UNS32304 APRESENTOU RESULTADOS SATISFATÓRIOS, COM TAXA ABAIXO DE 5MPY NAS DIFERENTES SOLUÇÕES, SENDO, PORTANTO, RECOMENDADA A SUA UTILIZAÇÃO.

CORROSION IS EXTREMELY HARMFUL TO THE MATERIAL, CAUSING MAJOR DAMAGE. ONCE UNDETECTED, IT CAN CAUSE AN ABRUPT RUPTURE OF A PART, STRUCTURE OR PIPE, CAUSING SERIOUS ACCIDENTS. IN ORDER TO REDUCE THESE DAMAGES, MATERIALS WITH CHEMICAL COMPOSITION AND SUITABLE MICROSTRUCTURES WERE CREATED TO BE MORE RESISTANT TO CORROSION. THIS IS THE CASE OF STAINLESS STEELS, WHICH HAVE THE CHARACTERISTIC OF CONTAINING AT LEAST 10.5% OF CHROMIUM IN THEIR COMPOSITION. THIS TYPE OF STEEL HAS A BETTER PERFORMANCE WHEN COMPARED TO COMMON STEEL WHEN APPLIED IN MORE AGGRESSIVE MEDIA, SUCH AS IN THE PETROCHEMICAL INDUSTRY WHERE IT IS WIDELY USED. IN ORDER TO ATTEST ITS RESISTANCE AND EVALUATE ITS BEHAVIOR IN THE PRESENCE OF ACID SOLUTIONS, THIS WORK WAS DEVELOPED USING THE DUPLEX STAINLESS STEEL UNS32304 WHICH WAS SUBJECTED TO TWO TYPES OF ACID SOLUTIONS, SULFURIC AND HYDROCHLORIC ACID, IN DIFFERENT CONCENTRATIONS. THE IMMERSION TEST LASTED 60 DAYS AND HAD PH AND POTENTIAL DIFFERENCE MEASURED WEEKLY. THROUGH THE DATA OBTAINED, IT WAS POSSIBLE TO CALCULATE THE CORROSION RATE OF STAINLESS STEEL, EVALUATING ITS BEHAVIOR AND SUSCEPTIBILITY TO CORROSION. IT WAS CONCLUDED THAT THE UNS32304 DUPLEX STAINLESS STEEL SHOWED SATISFACTORY RESULTS, WITH A RATE BELOW 5MPY IN THE DIFFERENT SOLUTIONS, THEREFORE, ITS USE IS RECOMMENDED.

Palavras-chave

Corrosão; Aço inoxidável UNS32304; Ácido Clorídrico; Ácido Sulfúrico.

Corrosion; Stainless Steel UNS32304; Hydrochloric Acid; Sulfuric Acid.

Como citar

Ribeiro, Tayná Raizza; Ribeiro, Samya Estevam; Araujo, Athos Fernandes; Sousa, Gustavo Henrique; Bueno, Rafael Ferreira Delfim; Lima, Ermani Vinicius de Oliveira; Ferreira, Marcos Vinicius Fonseca. ESTUDO COMPARATIVO DA CORROSÃO DO AÇO INOXIDÁVEL DUPLEX UNS32304 EM SOLUÇÕES ÁCIDAS , p. 134-143. In: 75° Congresso Anual da ABM, São Paulo, 2022.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-34214