ESTUDO COMPARATIVO DE RESISTÊNCIA À CORROSÃO ENTRE LIGAS METÁLICAS FERROSAS E NÃO FERROSAS

COMPARATIVE STUDY OF CORROSION RESISTANCE BETWEEN FERROUS AND NONFERROUS METALLIC ALLOYS

DOI

10.5151/1516-392X-27763

Downloads

Baixar Artigo 1191 Downloads

Resumo

A corrosão é um fenômeno que está intimamente ligado à integridade dos metais e de suas ligas. Esta ocorre de diversas formas, uma das principais é a corrosão localizada na forma de pites, objeto de análise desse estudo, que visa estabelecer um comparativo entre as curvas de polarização cíclica de algumas ligas ferrosas e não ferrosas, ensaiadas em solução de NaCl 0,6 M, mostrando a agressividade que a solução exerce sob cada uma das ligas. Os materiais analisados nesse estudo foram os aços inoxidáveis AISI 304, AISI 444, super duplex ASTM A890/A890 M Grau 6A, o aço carbono AISI 1030, o alumínio comercialmente puro, o cobre eletrolítico e a liga zircaloy- 4. Inicialmente foram medidos os potenciais de corrosão (Ec) de cada liga através do monitoramento do potencial de circuito aberto. Foram realizados os ensaios de polarização potenciodinâmica cíclica em cada liga, comparando o aspecto superficial antes e depois do ensaio através de micrografias óticas, possibilitando que fossem observadas as diferenças entre cada material quanto à resistência à corrosão por pites. Observou-se que algumas ligas não apresentam passivação como o caso do alumínio comercialmente puro, e outras apresentaram regiões passivas e histereses bem definidas, ficando evidente que, dentre as ligas analisadas, o aço inoxidável super duplex ASTM A890/A890 M Grau 6A apresentou os melhores resultados frente aos efeitos agressivos dos íons Cl- presentes na solução, sendo o menos suscetível à corrosão por pites.

 

Corrosion is a phenomenon that is closely linked to the integrity of the metal and its alloys. This occurs in many ways, one of the main is localized corrosion in the form of pits, object of analysis in this study, that aims to establish a comparison between the cyclic polarization curves of some ferrous and non-ferrous alloys, tested in 0,6M NaCl solution, showing aggressivity the solution exerts on each of the alloys. The materials analyzed in this study were the stainless steel AISI 304, AISI 444, super duplex ASTM A890 / A890 M Grade 6A, carbon steel AISI 1030, commercially pure aluminum, electrolytic copper and zircaloy-4 alloy. Initially the corrosion potentials were measured (Ec) from each alloy through the open circuit potential monitoring. The cyclic potentiodynamic polarization tests on each alloy were conducted, comparing the surface appearance before and after the test by optical micrographs, enabling that differences were observed between each material for resistance to pitting corrosion. It was observed that some alloys do not exhibit passivation such as the case of commercially pure aluminum, and others showed passive regions and well defined hysteresis, being evident that, among the examined alloys, super duplex stainless steel ASTM A890 / A890 M Grade 6A presented best results against the harsh effects of Cl- ions present in the solution, being less susceptible to pitting corrosion.

Palavras-chave

Corrosão por pites, Polarização cíclica, NaCl 0,6M, Ligas não ferrosas

Pitting corrosion, Cyclic Polarization, 0.6M NaCl, Nonferrous alloys