ESTUDO DA ESTABILIDADE DE ESTOCAGEM DE CAP 50/70 MODIFICADO COM BORRACHA MOÍDA DE PNEU

STUDY OF STORAGE-STABILITY OF CAP 50/70 MODIFIED WITH GROUND TIRE RUBBER

Autoria

Coelho, Johnny Gilberto Moraes; Souza, José Antônio da Silva; Dias, Carmen Gilda Barroso Tavares

DOI

10.5151/2594-5327-21224

Downloads

Baixar Artigo 333 Downloads

Resumo

Neste trabalho, foi utilizado um ligante cimento asfáltico de petróleo (CAP) acrescido com borracha moída de pneu 80/20 p/p. Para análise de estabilidade à estocagem, as amostras foram armazenadas em um cilindro de alumínio, dimensões 23 mm de diâmetro e 108,12 mm de altura, a 180°C por 24 horas e 48 horas. Em seguida foi feita a reologia de ligante e ligante modificado da parte superior e inferior das amostras após 24 horas, o reômetro utilizado foi de placas paralelas e gap de 15 mm. Foram plotados reogramas de módulo complexo (G*) e ângulo de fase (δ) a varredura de freqüência de 0,01 Hz-100 Hz a 120°C. Os resultados indicam o ganho de rigidez dos materiais nos reogramas analisados, devido a precipitação em consequência da instabilidade das partículas não dissolvidas, que leva a um aumento no módulo elástico das amostras colhidas no fundo do recipiente. Observou-se uma diminuição acentuada dos valores de ângulo de fase δ indicando melhoria das respostas elásticas.

 

In this work the asphalt binder was used CAP 50/70 to penetration 80% w/w plus ground tire rubber with 20% w/w. The order of addition of components may impair the quality of the final product, we adopted a random sequence of addition of components in the quantities set, CAP 50/70 with ground tire rubber. For storagestability, the samples were stored in a cylinder of aluminum 23 mm in size and 108.12 mm diameter high at 180°C for 24 hours and 48 hours. It was then made the rheology of the binder and the binder modificafo top and bottom of the samples after 24 hours, the rheometer was used type Haake RS6000, plate to plate and gap of 15 mm, complex modulus (G*) and the phase angle (δ) scan frequency of 0.01 Hz to 100 Hz at 120°C. The results indicate the stiffness of the material gain in the isotherms analyzed, due to precipitation as a result of instability of the undissolved particles, which leads to an increase in elastic modulus of samples collected at the bottom of the container. There was a marked decrease in δ values indicating improved elastic response.

Palavras-chave

Reologia; Ligante modificado; Módulo complexo; Ângulo de fase.

Rheology; Asphalt modified; Complex modulus; Phase angle.