Título

ESTUDO DA EXTENSÃO DA MISTURA DE AÇO NO LINGOTAMENTO CONTíNUO

STUDY OF THE EXTENSION OF STEEL MIXING IN THE CONTINUOUS CASTING

Autoria

FERREIRA, MATHEUS LOPES; ALVES, CELSO LUIZ MORAES; PEREIRA, LUIS GUSTAVO GOMES; SANTOS, RAFAELA PACHECO MALVÃO DOS

FERREIRA, MATHEUS LOPES

Eu sou esse autor

ALVES, CELSO LUIZ MORAES

Eu sou esse autor

PEREIRA, LUIS GUSTAVO GOMES

Eu sou esse autor

SANTOS, RAFAELA PACHECO MALVÃO DOS

Eu sou esse autor

DOI

10.5151/2594-5300-40942

Downloads

Resumo

NESTE TRABALHO é FEITA UMA ANáLISE DA EXTENSãO DA MISTURA DE AçOS REALIZADA NO PROCESSO CONTíNUO O DISTRIBUIDOR DE LINGOTAMENTO FOI INVESTIGADO NA COMPANHIA SIDERúRGICA NACIONAL (CSN). NA PRESENTE INVESTIGAçãO, RESULTADOS DE AMOSTRAGEM EXPERIMENTAL NO MOLDE, AMOSTRAGEM EXPERIMENTAL EM PLACA E UM MODELO MATEMáTICO DA LITERATURA FORAM COMPARADOS. PARA MEDIR A EXTENSãO DE MISTURA ENTRE DOIS TIPOS DE AçO DIFERENTES, AMOSTRAS DE AçO FORAM TIRADAS NO MOLDE DE LINGOTAMENTO CONTíNUO COM TRêS MINUTOS DE INTERVALO ENTRE ELAS APóS A TROCA DA PANELA. ALéM DISSO, TRêS PLACAS DE MISTURA FORAM SECCIONADAS PARA SEREM CORTADAS E ANALISADAS QUIMICAMENTE A CADA 1000 MM AO LONGO DO COMPRIMENTO. PARA TER UMA MANEIRA DE PREVER A EXTENSãO DE MISTURA DE AçO, O MODELO MATEMáTICO AJUSTADO PROPOSTO POR HUANG AND THOMAS [1] FOI IMPLEMENTADO CONSIDERANDO OS PARâMETROS DO PROCESSO DE LINGOTAMENTO CONTíNUO E OS RESULTADOS OBTIDOS FORAM COMPARADOS COM OS RESULTADOS EXPERIMENTAIS PARA AMBOS OS CASOS AMOSTRAGEM NO MOLDE E AMOSTRAGEM DE PLACAS. COM BASE NOS RESULTADOS COMPLETOS, VERIFICOU-SE QUE A EXTENSãO DE MISTURA DE AçO PODE SER, EM ALGUNS CASOS, SUPERIOR A 8,0 METROS PARA A MISTURA DE AçO INCOMPATíVEL, COMO FOI OBSERVADO NA ANáLISE DE %NB E %TI LEVADOS EM PLACAS DE AçO. OBSERVOU-SE TAMBéM UMA BOA CONVERGêNCIA ENTRE O MODELO MATEMáTICO E OS RESULTADOS EXPERIMENTAIS QUE PERMITEM CONCLUIR QUE O MODELO MATEMáTICO FORNECE UMA BOA REPRESENTAçãO DA EXTENSãO DE MIXAGEM E ABRE UMA BOA PERSPECTIVA PARA SUA APLICAçãO NA CSN.

IN THIS WORK, AN ANALYSIS OF THE EXTENSION OF STEEL MIXING CARRIED OUT IN THE CONTINUOUS CASTING TUNDISH WAS INVESTIGATED AT COMPANHIA SIDERúRGICA NACIONAL (CSN). IN THE PRESENT INVESTIGATION, RESULTS FROM EXPERIMENTAL SAMPLING IN THE MOLD, EXPERIMENTAL SAMPLING IN SLABS AND A MATHEMATICAL MODEL FROM THE LITERATURE WERE COMPARED. TO MEASURE THE MIXING EXTENSION BETWEEN TWO DIFFERENT STEEL GRADES, STEEL SAMPLES WERE TAKEN IN THE CONTINUOUS CASTING MOLD WITH THREE MINUTES OF INTERVAL BETWEEN EACH OTHER AFTER THE LADLE EXCHANGE. ADDITIONALLY, THREE MIXING SLABS WERE SECTIONED TO BE CUT AND CHEMICALLY ANALYZED EACH 1000 MM THOUGH THE LENGTH. TO HAVE A WAY OF PREDICTING THE STEEL MIXING EXTENSION, THE ADJUSTED MATHEMATICAL MODEL PROPOSED BY HUANG AND THOMAS [1] WAS IMPLEMENTED CONSIDERING THE CONTINUOUS CASTING PROCESS PARAMETERS AND THE OBTAINED RESULTS WERE COMPARED WITH THE EXPERIMENTAL RESULTS FOR BOTH CASES MOLD SAMPLING AND SLAB SAMPLING. BASED ON WHOLE RESULTS, IT WAS VERIFIED THAT THE STEEL MIXING EXTENSION CAN BE IN SOME CASES HIGHER THAN 8.0 METERS FOR THE INCOMPATIBLE STEEL MIXING, AS IT WAS OBSERVED IN THE ANALYSIS OF %NB AND %TI TOOK IN STEEL SLABS. IT WAS ALSO OBSERVED A GOOD CONVERGENCE BETWEEN THE MATHEMATICAL MODEL AND THE EXPERIMENTAL RESULTS WHICH ALLOWS TO CONCLUDE THAT THE MATHEMATICAL MODEL PROVIDES A GOOD REPRESENTATION OF THE MIXING EXTENSION AND OPENS A GOOD PERSPECTIVE FOR ITS APPLICATION AT CSN.

Palavras-chave

Lingotamento contínuo, mistura incompatível, Modelo matemático

Continuous casting, incompatible mixing, mathematical modelling.