ESTUDO DA FORMAÇÃO DE FASES POR DIFRAÇÃO DE RAIOS X NO COMPOSTO CERÂMICO AL2O3-NB2O5-FE2O3

STUDY OF PHASE FORMATION BY X-RAY DIFFRACTION IN AL2O3-NB2O5-FE2O5 CERAMIC COMPOUND

Autoria

Silveira, Pedro Henrique Poubel Mendonça da; Ribeiro, Matheus Pereira; Silva, Thuane Teixeira da; Santos, Jheison Lopes dos; Figueiredo, André Ben-Hur da Silva; Jesus, Paulo Roberto Rodrigues de; Gomes, Alaelson Vieira

DOI

10.5151/2594-5327-34839

Downloads

Baixar Artigo 23 Downloads

Resumo

NESTE TRABALHO FOI REALIZADO UM ESTUDO DA FORMAÇÃO DE FASES EM CERÂMICAS DE ALUMINA, DOPADAS COM NIÓBIA E HEMATITA, UTILIZANDO A TÉCNICA DE DIFRAÇÃO DE RAIOS X. FOI REALIZADO A SÍNTESE DA HEMATITA PELO MÉTODO DE COMBUSTÃO ESPONTÂNEA, EM SEGUIDA FOI REALIZADO O PROCESSAMENTO DAS CERÂMICAS DE ALUMINA COM E SEM A ADIÇÃO DE 4 %P DE NIÓBIA E TRÊS VARIAÇÕES NO TEOR DE HEMATITA: 0,5, 1,0 E 2,0 %P. AS AMOSTRAS FORAM PREPARADAS POR PRENSAGEM UNIAXIAL A FRIO E SINTERIZAÇÃO CONVENCIONAL. OS RESULTADOS DA DIFRAÇÃO DE RAIO X DOS PÓS INDICOU A FASE ROMBOÉDRICA TANTO PARA A ALUMINA, QUANTO PARA A HEMATITA, E ESTRUTURA MONOCLÍNICA PARA A NIÓBIA. NAS AMOSTRAS SINTERIZADAS, OCORREU A FORMAÇÃO DE TRÊS FASES DISTINTAS: ALFEO3, ALNBO4 E FENBO4. A FORMAÇÃO DESTAS FASES INDICA A INTERAÇÃO DIRETA DA HEMATITA COM A NIÓBIA EM ALTAS TEMPERATURAS, FORMANDO A FASE FENBO4. A FASE ALNBO4 OCORREU DEVIDO A INTERAÇÃO DA ALUMINA COM A NIÓBIA, E A FORMAÇÃO DE ALFEO3 OCORREU PELA A INTERAÇÃO DA ALUMINA COM A HEMATITA.

 

IN THIS WORK, A STUDY OF THE FORMATION OF PHASES IN ALUMINA CERAMICS, DOPED WITH NIOBIUM OXIDE AND HEMATITE, USING X-RAY DIFFRACTION TECHNIQUE. OF ALUMINA WITH AND WITHOUT THE ADDITION OF 4 %WT OF NIOBIUM OXIDE AND THREE VARIATIONS IN THE CONTENT OF HEMATITE: 0.5, 1.0, AND 2.0 %WT. SAMPLES WERE PREPARED BY UNIAXIAL COLD PRESSING AND PRESSURELESS SINTERING. THE X-RAY POWDER DIFFRACTION RESULTS INDICATED THE RHOMBOHEDRAL PHASE FOR BOTH ALUMINA AND HEMATITE, AND THE MONOCLINIC STRUCTURE FOR NIOBIUM OXIDE. IN THE SINTERED SAMPLES, THREE DISTINCT PHASES WERE FORMED: ALFEO3, ALNBO4, AND FENBO4. THE FORMATION OF THESE PHASES INDICATES THE DIRECT INTERACTION OF HEMATITE WITH NIOBIUM OXIDE AT HIGH TEMPERATURES, FORMING THE FENBO4 PHASE. THE ALNBO4 PHASE OCCURRED DUE TO THE INTERACTION OF ALUMINA WITH NIOBIUM OXIDE, AND THE FORMATION OF ALFEO3 OCCURRED DUE TO THE INTERACTION OF ALUMINA WITH HEMATITE

Palavras-chave

Al2O3; Nb2O5; Fe2O3; drx

AL2O3; NB2O5; FE2O3; XRD