Título

ESTUDO DA INFLUÊNCIA DA DEFORMAÇÃO A QUENTE NA MICROESTRUTURA DE UMA LIGA DE NITI

STUDY OF THE HOT DEFORMATION INFLUENCE OF THE MICROSTRUCTURE IN NITI ALLOY

Autoria

Sénéchal, Naiara Vieira Le; Rodrigues, Patrícia Freitas; Lima, Ygor Pereira; Teixeira, Rodolfo da Silva; Ferrão, Thiago Henrique Fernandes Dias; Fernandes, Francisco Manuel Braz; Paula, Andersan dos Santos

DOI

10.5151/2594-5327-34241

Downloads

Baixar Artigo 34 Downloads

Resumo

NESTE ESTUDO FORAM UTILIZADAS AMOSTRAS DE UMA LIGA HOMOGENEIZADA DE NITI, RICA EM NI, COM O OBJETIVO DE AVALIAR A INFLUÊNCIA DAS ETAPAS DE DEFORMAÇÃO A QUENTE DA MICROESTRUTURA EM DIFERENTES REGIÕES DO MATERIAL. O HISTÓRICO DE FABRICAÇÃO, AS TAXAS DE DEFORMAÇÃO E TEMPERATURAS EMPREGADAS NO TRATAMENTO TERMOMECÂNICO ALTERAM ALGUNS FATORES COMO A COMPOSIÇÃO QUÍMICA LOCAL, A DIMINUIÇÃO DE DEFEITOS, NAS TEMPERATURAS DE TRANSFORMAÇÃO DIRETA/ TRANSFORMAÇÃO REVERSA E NAS PROPRIEDADES FUNCIONAIS E MECÂNICAS, COMO O EFEITO MEMÓRIA DE FORMA E SUPERELASTICIDADE. A LIGA DESTE ESTUDO FOI SUBMETIDA A DEFORMAÇÃO A QUENTE, POR MEIO DE ENSAIO DE COMPRESSÃO A QUENTE IN-SITU EM SIMULADOR TERMOMECÂNICO, COM TAXAS DE DEFORMAÇÃO DA ORDEM DE 10-1 S-1 E 10-2 S-1, A 850 °C. O USO DA MICROSCOPIA ÓPTICA PERMITIU A ANÁLISE DAS MUDANÇAS ESTRUTURAIS NAS DIFERENTES REGIÕES DE DEFORMAÇÃO DAS AMOSTRAS.

 

IN THIS STUDY, SAMPLES OF A HOMOGENIZED NITI ALLOY, RICH IN NI, WERE USED IN ORDER TO EVALUATE THE HOT DEFORMATION STEPS INFLUENCE IN THE MICROSTRUCTURE IN DIFFERENT REGIONS OF THE MATERIAL. THE MANUFACTURING HISTORY, THE STRAIN RATES AND TEMPERATURES EMPLOYED IN THERMOMECHANICAL TREATMENT ALTER SOME FACTORS SUCH AS THE LOCAL CHEMICAL COMPOSITION, THE REDUCTION OF DEFECTS, THE TEMPERATURES OF DIRECT TRANSFORMATION/ REVERSE TRANSFORMATION AND THE FUNCTIONAL AND MECHANICAL PROPERTIES, SUCH AS THE MEMORY SHAPE EFFECT AND SUPERELASTICITY. THE ALLOY IN THIS STUDY WAS SUBJECTED TO HOT DEFORMATION, BY MEANS OF A HOT COMPRESSION TEST IN-SITU IN A THERMOMECHANICAL SIMULATOR, WITH DEFORMATION RATES IN ORDER OF 10-1 S-1 AND 10-2 S-1, AT 850 °C. THE OPTICAL MICROSCOPY ALLOWED THE ANALYSIS OF STRUCTURAL CHANGES IN THE DIFFERENT REGIONS OF DEFORMATION OF THE SAMPLES.

Palavras-chave

Ligas de NiTi; Deformação a Quente; Processamento Termomecânico.

Niti Alloys; Hot Deformation; Thermomechanical Process