ESTUDO DA INFLUÊNCIA DO GRAU DE CRISTALINIDADE NA RESISTÊNCIA AO IMPACTO DE COMPÓSITOS DE PP/SIC

STUDY OF THE INFLUENCE OF THE DEGREE OF CRYSTALLINITY IN IMPACT STRENGTH OF COMPOSITES OF PP / SIC

Autoria

Dafe, Sara Silva Ferreira de

DOI

10.5151/2594-5327-34115

Downloads

Baixar Artigo 12 Downloads

Resumo

ESTE TRABALHO TEM COMO OBJETIVO AVALIAR A INFLUÊNCIA DE FATORES COMO TAMANHO DE PARTÍCULA E O SEU TEOR NA RESISTÊNCIA AO IMPACTO DE COMPÓSITOS DE POLIPROPILENO (PP) COM CARBETO DE SILÍCIO (SIC). PARA FABRICAÇÃO DOS COMPÓSITOS, FORAM FEITAS EXTRUSÕES DO POLIPROPILENO HOMOPOLÍMERO COM UM AGENTE COMPATIBILIZANTE E TAMBÉM COM AS PARTÍCULAS DE SIC, EM DIFERENTES PROPORÇÕES E TAMANHOS DE PARTÍCULAS. COMO AGENTE COMPATIBILIZANTE FOI UTILIZADO POLIPROPILENO GRAFITIZADO COM ANIDRIDO MALEICO (PP-G-AM). APÓS O PROCESSO DE EXTRUSÃO, OS FIOS EXTRUDADOS FORAM CORTADOS E MOÍDOS PARA SEREM MOLDADOS EM CORPOS DE PROVA DE IMPACTO POR MEIO DE INJEÇÃO. ENTÃO, OS CORPOS DE PROVA DE IMPACTO INJETADOS FORAM TESTADOS CONFORME A NORMA ASTM D256 E SEUS RESULTADOS FORAM ANALISADOS ESTATISTICAMENTE POR MEIO DE ANÁLISE DE VARIÂNCIA (ANOVA) E DO TESTE DE TUKEY PARA AVALIAR QUAIS DOS FATORES INFLUENCIARAM EFETIVAMENTE NA RESISTÊNCIA AO IMPACTO DOS COMPÓSITOS E QUAIS VARIAÇÕES DOS COMPÓSITOS SE DESTACARAM. POR FIM, OS RESULTADOS OBTIDOS NOS ENSAIOS DE IMPACTO FORAM COMPARADOS COM OS DADOS DE GRAU DE CRISTALINIDADE CALCULADOS POR MEIO DOS RESULTADOS DE ANÁLISES DE DSC E MOSTRARAM QUE A REDUÇÃO NO GRAU DE CRISTALINIDADE PROVOCOU UM AUMENTO NA RESISTÊNCIA AO IMPACTO.

 

THIS WORK AIMS TO EVALUATE THE INFLUENCE OF FACTORS SUCH AS PARTICLE SIZE AND ITS CONTENT IN THE IMPACT STRENGTH OF POLYPROPYLENE (PP) COMPOSITES REINFORCED WITH SILICON CARBIDE (SIC). HOMOPOLYMER POLYPROPYLENE, A COUPLING AGENT AND ALSO SIC PARTICLES, IN DIFFERENT PARTICLE SIZES AND PROPORTIONS WERE EXTRUDED TO COMPOSITES MANUFACTURING. MALEIC ANHYDRIDE–GRAFTED POLYPROPYLENE (MAGPP) WAS USED AS COMPATIBILIZER. AFTER THE EXTRUSION PROCESS, THE EXTRUDED WIRES WERE CUT AND GROUND TO BE MOLDED INTO IMPACT TEST SPECIMENS BY MEANS OF INJECTION. THEN, THE INJECTED IMPACT SPECIMENS WERE TESTED ACCORDING TO THE ASTM D256 STANDARD AND THEIR RESULTS WERE STATISTICALLY ANALYZED USING ANALYSIS OF VARIANCE (ANOVA) AND THE TUKEY TEST TO EVALUATE WHICH OF THE FACTORS EFFECTIVELY INFLUENCED THE IMPACT STRENGTH OF COMPOSITES AND WHICH VARIATIONS OF THE COMPOSITES HIGHLIGHTED. FINALLY, THE RESULTS OBTAINED IN THE IMPACT TESTS WERE COMPARED WITH THE DEGREE OF CRYSTALLINITY DATA CALCULATED USING THE DSC ANALYSIS RESULTS AND SHOWED THAT THE REDUCTION IN THE DEGREE OF CRYSTALLINITY CAUSED AN INCREASE IN THE IMPACT STRENGTH

Palavras-chave

Compósitos; Polipropileno, Resistência ao impacto, Grau de cristalinidade

Composites; Polypropylene; Impact strength; Degree of crystallinity