ESTUDO DAS INCLUSÕES NÃO-METÁLICAS NO PROCESSO DE SOLIDIFICAÇÃO DE UM AÇO API X65 SOUR SERVICE HTP: STUDY OF NON-METALLIC INCLUSIONS IN THE PROCESS OF SOLIDIFICATION OF A STEEL API X65 SOUR SERVICE HTP

Escobar, Diana Pérez; Castro, Cynthia Serra Batista; Malynowskyj, Antônio; Camey, Kenji; Taiss, Ed Juarez Mendes; Andrade, Margareth Spangler

doi:10.5151/1982-9345-31830

Anais do Seminário de Aciaria, Fundição e Metalurgia de Não-ferrosos

ISSN 2594-5300

49° Seminário de Aciaria, Fundição e Metalurgia de Não-Ferrosos — vol. 49, num.49 (2018)

Título

ESTUDO DAS INCLUSÕES NÃO-METÁLICAS NO PROCESSO DE SOLIDIFICAÇÃO DE UM AÇO API X65 SOUR SERVICE HTP

STUDY OF NON-METALLIC INCLUSIONS IN THE PROCESS OF SOLIDIFICATION OF A STEEL API X65 SOUR SERVICE HTP

Autoria

Escobar, Diana Pérez; Castro, Cynthia Serra Batista; Malynowskyj, Antônio; Camey, Kenji; Taiss, Ed Juarez Mendes; Andrade, Margareth Spangler

10.5151/1982-9345-31830

Downloads

Baixar Artigo 317 Downloads

Resumo

O presente trabalho estudou a formação de inclusões em um aço HTP (High Temperature Processing) API X65, sour service, submetido ao processo de injeção de Ca e lingotado continuamente com soft reduction dinâmico. Os resultados obtidos na placa foram comparados com uma amostra líquida retirada do distribuidor. A engenharia de inclusões foi respaldada pelo mapeamento com microscópio eletrônico de varredura e metodologia específica. Houve uma diferenciação no nível de limpeza (NL) e tipos de inclusões/partículas entre as amostras, sendo que as relações causa-efeito foram analisadas e discutidas. A maioria das inclusões e partículas detectadas não favorecem trincas induzidas por hidrogênio (HIC).

This paper investigated the formation of inclusions in a steel HTP (High Temperature Processing) API X65, sour service, submitted to the Ca injection process and continuously cast with dynamic soft reduction. The results obtained on the slabs were compared with a liquid sample taken from the tundish. Inclusion engineering was supported by scanning electron microscope mapping and specific methodology. There was a difference in the clean steel level (NL) and types of inclusions / particles between the samples, and the cause-effect relationships were analyzed and discussed. Most inclusions and particles detected do not favor hydrogen-induced cracking (HIC).

Palavras-chave

inclusões não-metálicas; aço HTP; distribuidor; lingotamento contínuo.

non-metallic inclusions; HTP steel; tundish; continuous casting

Como citar

Escobar, Diana Pérez; Castro, Cynthia Serra Batista; Malynowskyj, Antônio; Camey, Kenji; Taiss, Ed Juarez Mendes; Andrade, Margareth Spangler. ESTUDO DAS INCLUSÕES NÃO-METÁLICAS NO PROCESSO DE SOLIDIFICAÇÃO DE UM AÇO API X65 SOUR SERVICE HTP , p. 588-596. In: 49° Seminário de Aciaria, Fundição e Metalurgia de Não-Ferrosos, São Paulo, 2018.
ISSN: 2594-5300 , DOI 10.5151/1982-9345-31830