ESTUDO DE EVOLUÇÃO MICROESTRUTURAL DURANTE RECOZIMENTO CONTÍNUO DE AÇO MULTIFÁSICO

STUDY OF THE MICROSTRUCTURAL EVOLUTION DURING THE CONTINUOUS ANNEALING OF A COMPLEX PHASE STEEL

Autoria

Lino, Roney Eduardo; Silva, Letícia Barbosa; Brandão, Luiz Paulo; Tolomelli, Flávia Tereza; Iosu, Aramendi; Denis, Jorge-Badiola; Amaia, Iza-Mendia; Gutierrez, Isabel

DOI

10.5151/2594-5327-34982

Downloads

Baixar Artigo 12 Downloads

Resumo

O AÇO É ATUALMENTE A PRINCIPAL SOLUÇÃO EM MATERIAIS PARA A INDÚSTRIA AUTOMOTIVO, QUE DENTRE AS SUAS VANTAGENS DESTACA-SE A ELEVADA RESISTÊNCIA, TENACIDADE E BOA CONFORMABILIDADE. OS AÇOS MULTIFÁSICOS CONCILIAM COMPOSIÇÃO QUÍMICA CUIDADOSAMENTE SELECIONADA E CONDIÇÕES DE PROCESSO OTIMIZADAS PARA ATENDER OS REQUISITOS DO PRODUTO. OS RESULTADOS DE TRANSFORMAÇÃO DE FASE PARA AUSTENITA PREVISTOS PELO MODELO APRESENTARAM BOA CORRELAÇÃO COM OS VALORES MEDIDOS EXPERIMENTALMENTE. PARA CICLOS TÉRMICOS DE ATÉ 60 S NA TEMPERATURA DE ENCHARQUE O MODELO PREVÊ UMA FRAÇÃO MÁXIMA DE RECRISTALIZAÇÃO DE 25%. FRENTE AOS RESULTADOS, MODELO DEMONSTROU TER UM GRANDE POTENCIAL COMO FERRAMENTA DE SUPORTE AO DESENVOLVIMENTO DE NOVOS PRODUTOS INDUSTRIAIS.

 

STEEL IS CURRENTLY THE MAIN SOLUTION IN MATERIALS FOR THE AUTOMOTIVE INDUSTRY, WHICH AMONG ITS ADVANTAGES IS HIGH STRENGTH, TOUGHNESS AND GOOD FORMABILITY. MULTIPHASE STEELS HAVE EMERGED, WHICH COMBINE CAREFULLY SELECTED CHEMICAL COMPOSITION AND OPTIMIZED PROCESS CONDITIONS TO MEET PRODUCT REQUIREMENTS. LABORATORY ANNEALING SIMULATIONS HAVE PRODUCED A SERIES OF MICROSTRUCTURES FOR MONITORING THE DIFFERENT STAGES OF PHASE TRANSFORMATION AND TO OBTAIN INFORMATION ABOUT RECRYSTALLIZATION. DIFFERENT TECHNNIQUES, INCLUDING EBSD, HAVE BEEN USED TO RESOLVE THE FINE AND COMPLEX MICROSTRUCTURES GENERATED, AND THE RESULTS HAVE BEEN COMPARED WITH THE PREDICTION OBTAINED THROUGH THE CONTINUOUS ANNEALING MCASIM MODEL DEVELOPED BY CEIT. THE RESULTS OF PHASE TRANSFORMATION TO AUSTENITE PREDICTED BY THE MODEL SHOWED GOOD CORRELATION WITH THE EXPERIMENTALLY MEASURED VALUES. FOR THERMAL CYCLES OF UP TO 60 S AT THE SOAKING TEMPERATURE, THE MODEL PREDICTS A MAXIMUM RECRYSTALLIZATION FRACTION OF 25%. FACE TO THE EVALUATED RESULTS, HAS SHOWN GREAT POTENTIAL AS A TOOL TO SUPPORT THE DEVELOPMENT OF NEW INDUSTRIAL PRODUCTS.

Palavras-chave

Aço Multifásico; Aço Avançado; Recozimento; Nióbio

Comple-Phase Steel; AHSS; Annealing; Niobium