ESTUDO DE NOVAS PERSPECTIVAS TECNOLÓGICAS DO APROVEITAMENTO DO PÓ DE ACIARIA ELÉTRICA

STUDY OF NEW TECHNOLOGICAL PERSPECTIVES IN THE USE OF ELECTRIC ARC FURNACE DUST FURNACE

DOI

10.5151/2594-4711-33156

Downloads

Baixar Artigo 134 Downloads

Resumo

Em virtude da periculosidade do Pó de aciaria (PAE), práticas alternativas, como a reinserção do resíduo no processo produtivo, ou sua incorporação em outros materiais fizeram com que a reciclagem tenha se tornado uma via para este subproduto. O presente trabalho tem como objetivo identificar as áreas de desenvolvimento tecnológico de utilização do PAE, avaliar a potencialidade de reaproveitamento e reciclagem do resíduo oriundo do processo de produção do aço carbono, comparando as características obtidas do PAE analisado com os requisitos indicados através da análise de patentes. O PAE produzido no estado de Pernambuco foi caracterizado pelas técnicas de Fluorescência de raios X (FRX), separação granulométrica via peneiramento, distribuição do tamanho de partículas, Difração de raios X (DRX), Microscopia eletrônica de varredura (MEV) e Espectroscopia por energia dispersiva (EDS). A prospecção tecnológica foi realizada nas bases de patentes europeia EPO e na base nacional de patentes nacional do INPI. As análises realizadas mostraram que o material apresentou aproximadamente 28,5% de suas partículas com granulometria inferior a 53μm, composto em sua maioria por ferro e zinco presentes na forma de óxidos, organizados nas fases franklinita, zincita e magnetita. A baixa granulometria e composição química possibilitam a sua aplicação no campo dos materiais cerâmicos, bem como sua reinserção no processo de fabricação. O resíduo estudado apresentou características similares com os demais resíduos observados nas patentes.

 

Due to the hazardousness nature of the electric arc furnace dust (EAFD), alternative practices, as reinsertion of waste into the steelmaking process, or its incorporation into other materials, have led the recycling has become a route for this by-product. The aim of this work was to identify technological development areas of the use of EAFD, evaluate the potential of reuse and recycling of waste arising from production of carbon steel, comparing the characteristics obtained from EAFD examined with requirements indicated by an analysis of patents. EAFD generated in the state of Pernambuco was characterized by X-ray fluorescence (XRF), size separation of particles by sieving, X-ray diffraction (XRD), Scanning electron microscope (SEM) plus Energy dispersive spectroscopy (EDS) analysis technique. Technology prospecting was con-ducted in EPO European international patent databases and INPI national databases. The analysis carried out show that waste had approximately 28,5% of particle size less than 53μm, composed in its majority by iron and zinc in the form of oxides, present as phases franklinite, zincite and magnetite. The small particle size and chemical composition allow its application in the field of ceramic materials, and reinsertion into the steelmaking process. The waste studied had similar characteristics with other wastes observed in patents.

Palavras-chave

Resíduo siderúrgico; Pó de aciaria; reciclagem, prospecção tecnológica.

Steelmaking waste; Electric arc furnace dust; Recycling; Technology prospecting.

Como citar

Alves, Elizeth Oliveira; Vasconcelos, Cleiton Rodrigues de; Alves, Kleber Gonçalves Bezerra. ESTUDO DE NOVAS PERSPECTIVAS TECNOLÓGICAS DO APROVEITAMENTO DO PÓ DE ACIARIA ELÉTRICA , p. 1-12. In: 19° Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas (ENEMET), São Paulo, 2019.