ESTUDO DO BANDEAMENTO MICROESTRUTURAL NO AÇO SAE 4140

STUDY OF MICROSTRUCTURAL BANDING IN SAE 4140 STEEL

Autoria

ALMEIDA, MARIANA GOMES DE; JUNIO, ROBERTO AUGUSTO TEIXEIRA FULGÊNCIO

ALMEIDA, MARIANA GOMES DE

1 Artigos, Baixados 2 Vezes

JUNIO, ROBERTO AUGUSTO TEIXEIRA FULGÊNCIO

Eu sou esse autor

DOI

10.5151/2594-5327-41302

Downloads

Resumo

O BANDEAMENTO MICROESTRUTURAL é MUITAS VEZES CORRELACIONADO COM QUEDAS OBSERVADAS NA RESISTêNCIA MECâNICA E NA TENACIDADE DOS AçOS. NESTE TRABALHO é APRESENTADO UM ESTUDO DO BANDEAMENTO MICROESTRUTURAL NO AçO SAE 4140 TEMPERADO E REVENIDO, NO QUAL FOI AVALIADO A INFLUêNCIA DA TAXA DE RESFRIAMENTO DA TêMPERA NA INTENSIDADE DO BANDEAMENTO E NAS PROPRIEDADES MECâNICAS. NO ESTUDO, FORAM REALIZADOS TRATAMENTOS TéRMICOS EXPERIMENTAIS DE TêMPERA E REVENIMENTO EM TARUGOS, PARA POSTERIOR USINAGEM DE CORPOS PARA ENSAIOS MECâNICOS A ANáLISE METALOGRáFICA, VARIANDO APENAS O MEIO DE TêMPERA, ONDE FOI UTILIZADO áGUA, óLEO E AR. ALéM DISSO FORAM REALIZADOS ENSAIOS DE DILATOMETRIA, SIMULANDO O PROCESSO DE AUSTENITIZAçãO SEGUIDO DE TEMPERA EM DIFERENTES TAXAS DE RESFRIAMENTO, PARA POSTERIOR AVALIAçãO DO BANDEAMENTO. OS RESULTADOS MOSTRARAM UMA CORRELAçãO ENTRE A TAXA DE RESFRIAMENTO E O BANDEAMENTO ONDE FOI OBSERVADO QUE QUE QUANTO MAIOR A TAXA, MENOR A INTENSIDADE DO BANDEAMENTO E MAIORES OS VALORES DE RESISTêNCIA MECâNICA E TENACIDADE DO AçO. POR FIM, FOI POSSíVEL OBSERVAR TAMBéM ATRAVéS TéCNICAS DE MICROSCOPIA DIC E CAMPO ESCURO (HRX) A EXISTêNCIA DE DIFERENçA DE RELEVO ENTRE AS DIFERENTES BANDAS PRESENTES NA MICROESTRUTURA.

MICROSTRUCTURAL BANDING IS OFTEN CORRELATED WITH OBSERVED DROPS IN THE MECHANICAL STRENGTH AND TOUGHNESS OF STEELS. THIS WORK PRESENTS A STUDY OF MICROSTRUCTURAL BANDING IN QUENCHED AND TEMPERED SAE 4140 STEEL, IN WHICH THE INFLUENCE OF THE COOLING RATE ON THE BANDING INTENSITY AND MECHANICAL PROPERTIES WAS EVALUATED. IN THE STUDY, EXPERIMENTAL QUENCHING AND TEMPERING HEAT TREATMENTS WERE CARRIED OUT ON BILLETS, FOR SUBSEQUENT MACHINING OF MECHANICAL TESTS AND METALLOGRAPHIC ANALYSIS SPECIMENS, VARYING ONLY THE QUENCHING MEDIUM, WHERE WATER, OIL AND AIR WERE USED. IN ADDITION, DILATOMETRY TESTS WERE CARRIED OUT, SIMULATING THE AUSTENITIZATION PROCESS FOLLOWED BY QUENCHING AT DIFFERENT COOLING RATES, FOR SUBSEQUENT BANDING EVALUATION. THE RESULTS SHOWED A CORRELATION BETWEEN THE COOLING RATE AND BANDING WHERE IT WAS OBSERVED THAT AS HIGHER THE RATE IS, THE LOWER THE BANDING INTENSITY AND THE HIGHER THE MECHANICAL STRENGTH AND TOUGHNESS VALUES OF THE STEEL. FINALLY, IT WAS ALSO POSSIBLE TO OBSERVE, USING DIC AND DARK FIELD (HRX) MICROSCOPY TECHNIQUES, THE EXISTENCE OF A DIFFERENCE IN RELIEF BETWEEN THE DIFFERENT BANDS PRESENT IN THE MICROSTRUCTURE.

Palavras-chave

Bandeamento microestrutural; Tenacidade; Propriedades mecânicas; Tratamento térmico.

Microstructural banding; Toughness; Mechanical properties; Heat treatment.