ESTUDO DO COMPORTAMENTO À CORROSÃO EM
DIFERENTES TEMPERATURAS DE LIGAS Al-1,5%Fe EM
MEIO DE H2SO4 0,1 M TRATADAS POR REFUSÃO
SUPERFICIAL A LASER: STUDY OF THE CORROSION RESISTANCE IN SULFURIC ACID 0,1 M OF THE
ALLOY AL-1,5%FE WHEN SUBMITED TO SUPERFICIAL LASER TREATMENT

Teleginski, Viviane; Santos, Kelly dos; Riva, Rudimar; Zara, Alfredo José; Pariona, Moisés Meza

doi:10.5151/2594-5327-21493

Anais do Congresso Anual da ABM

ISSN 2594-5327

67º Congresso da ABM - Internacional / 12º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas — vol. 67, num.67 (2012)

Título

ESTUDO DO COMPORTAMENTO À CORROSÃO EM DIFERENTES TEMPERATURAS DE LIGAS Al-1,5%Fe EM MEIO DE H2SO4 0,1 M TRATADAS POR REFUSÃO SUPERFICIAL A LASER

STUDY OF THE CORROSION RESISTANCE IN SULFURIC ACID 0,1 M OF THE ALLOY AL-1,5%FE WHEN SUBMITED TO SUPERFICIAL LASER TREATMENT

Autoria

Teleginski, Viviane; Santos, Kelly dos; Riva, Rudimar; Zara, Alfredo José; Pariona, Moisés Meza

10.5151/2594-5327-21493

Downloads

Baixar Artigo 141 Downloads

Resumo

Neste trabalho foi estudado o comportamento à corrosão da liga Al-1,5%Fe, tratada e não tratada por refusão superficial a laser. Foi utilizado um laser do tipo Yb: YAG com 600 W de potência e velocidade de deslocamento do laser de 40 mm/min, sendo o ácido sulfúrico (H2SO4 0,1 M) o meio utilizado para estudos de corrosão com variações de temperatura entre 5 e 75°C. Como resultado, foi feita a caracterização microestrutural do material, definidas as taxas de corrosão e resistências à polarização. A microestrutura obtida pela técnica de refusão a laser mostrou-se eficiente para melhorar a resistência à corrosão no meio estudado. Apresentaram-se modificações nas curvas de Tafel, assim como no potencial de corrosão devido às modificações superficiais provocadas pelo tratamento laser.

In this work it has been studied the corrosion behavior of the alloy Al-1.5%Fe, treated by laser surface remelting and untreated. The used laser was Yb: YAG type with 600 W of power and laser scanning speed of 40 mm/min, and the media for corrosion studies was sulfuric acid (H2SO4 0.1 M) with temperatures variations between 5 and 75°C. As a result, it was obtained the material microstructural characterization, defined the corrosion rates and polarization resistances. The microstructure obtained by the technique of laser remelting showed to be efficient to improve the corrosion resistance in the studied media. Changes in Tafel curves, as well as in corrosion potentials were presented due to surface modifications induced by laser treatment.

Palavras-chave

Tratamento superficial a laser; Resistência à corrosão; Ligas de alumínio; Microestrutura.

Surface laser treatment; Corrosion resistance; Aluminum alloys; Microstructure.

Como citar

Teleginski, Viviane; Santos, Kelly dos; Riva, Rudimar; Zara, Alfredo José; Pariona, Moisés Meza. ESTUDO DO COMPORTAMENTO À CORROSÃO EM DIFERENTES TEMPERATURAS DE LIGAS Al-1,5%Fe EM MEIO DE H2SO4 0,1 M TRATADAS POR REFUSÃO SUPERFICIAL A LASER , p. 3541-3548. In: 67º Congresso da ABM - Internacional / 12º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, Rio de Jabeiro, 2012.