O TRATAMENTO TÉRMICO DE TÊMPERA E PARTIÇÃO TEM SIDO ESTUDADO COMO UMA ALTERNATIVA PARA A OBTENÇÃO DE PROPRIEDADES ANTAGÔNICAS, COMO ELEVADA RESISTÊNCIA MECÂNICA E BOA TENACIDADE EM AÇOS. UM DOS ASPECTOS DE GRANDE RELEVÂNCIA PARA A OBTENÇÃO DAS PROPRIEDADES MECÂNICAS INDICADAS, ASSOCIA-SE A PRESENÇA DE ELEVADOS TEORES DE SILÍCIO, NA COMPOSIÇÃO QUÍMICA, DE ALGUMAS CLASSES DE AÇOS E FERROS FUNDIDOS. O SILÍCIO INIBE A FORMAÇÃO DE CARBONETOS CONTRIBUINDO PARA A POSTERIOR PARTIÇÃO DE CARBONO DA MARTENSITA PARA A AUSTENITA, ESTABILIZANDO A MESMA, APÓS TRATAMENTO ISOTÉRMICO. NESTE ESTUDO VERIFICOU-SE O EFEITO DO TEMPO DE PARTIÇÃO NA MICROESTRUTURA E MICRODUREZA DOS AÇOS SAE 9254 OS RESULTADOS DEMOSTRARAM, APÓS A AUSTENITIZAÇÃO E RESFRIAMENTO, ENTRE O INÍCIO E FINAL DA TRANSFORMAÇÃO MARTENSÍTICA OBTEVE-SE MARTENSITA E AUSTENITA RETIDA. POSTERIORMENTE COM A PARTIÇÃO A AUSTENITA APRESENTOU ESTABILIDADE. PODE-SE CONCLUIR QUE A APLICAÇÃO DE TÊMPERA COM RESFRIAMENTO ISOTÉRMICO NA TEMPERATURA DE 220 ˚C E PARTIÇÃO NA TEMPERATURA DE 360 ˚C REPRESENTA ROTA EFETIVA PARA A OBTENÇÃO DA MICROESTRUTURA BIFÁSICA ESTABILIZADA.
THE QUENCHING AND PARTITIONING HEAT TREATMENT HAS BEEN STUDIED AS AN ALTERNATIVE TO OBTAIN ANTAGONISTIC PROPERTIES, SUCH AS HIGH MECHANICAL STRENGTH AND GOOD TOUGHNESS IN STEELS. ONE OF THE ASPECTS OF GREAT RELEVANCE FOR OBTAINING THE MECHANICAL PROPERTIES INDICATED IS ASSOCIATED WITH THE PRESENCE OF HIGH SILICON CONTENT IN THE CHEMICAL COMPOSITION OF SOME CLASSES OF STEELS AND CAST IRONS. THE SILICON INHIBITS THE FORMATION OF CARBIDES CONTRIBUTING TO THE SUBSEQUENT PARTITION OF CARBON FROM MARTENSITE TO AUSTENITE, STABILIZING THE LATTER, AFTER ISOTHERMAL TREATMENT. IN THIS STUDY THE EFFECT OF PARTITIONING TIME ON THE MICROSTRUCTURE AND MICROHARDNESS OF SAE 9254 STEELS WAS VERIFIED. THE RESULTS SHOWED THAT AFTER AUSTENITIZING AND COOLING, BETWEEN THE BEGINNING AND END OF THE MARTENSITIC TRANSFORMATION, MARTENSITE AND RETAINED AUSTENITE WERE OBTAINED. LATER, WITH THE PARTITIONING, THE AUSTENITE SHOWED STABILITY. IN CONCLUSION, QUENCHING WITH ISOTHERMAL COOLING AT A TEMPERATURE OF 220 ˚C AND PARTITIONING AT A TEMPERATURE OF 360 ˚C REPRESENTS AN EFFECTIVE ROUTE TO OBTAIN STABILIZED TWO-PHASE MICROSTRUCTURE.
Palavras-chave
Têmpera; Partição; Aço SAE 9254
Quenching; Partitioning; Steel SAE 9254
Como citar
Souza, Pablo Hernandes Medeiros;
Medeiros, Jorge Luis Braz;
Biehl, Luciano Volcanoglo;
Souza, José de;
Moraes, Carlos Alberto Mendes.
ESTUDO DO EFEITO DO TEMPO NO PROCESSO DE TÊMPERA E PARTIÇÃO APLICADOS AO AÇO SAE 9254
,
p. 401-413.
In: 75° Congresso Anual da ABM,
São Paulo,
2022.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-34549