ESTUDO DO ENCRUAMENTO EM UM AÇO INOXIDÁVEL LEAN DUPLEX 2304 APÓS LAMINAÇÃO A FRIO

STUDY OF THE STRAIN HARDENING OF A LEAN STAINLESS STEEL UNS2304 AFTER COLD ROLLING

Autoria

Alves, Davi Silva

DOI

10.5151/2594-5327-34227

Downloads

Baixar Artigo 9 Downloads

Resumo

O MECANISMO DE DEFORMAÇÃO DOS AÇOS INOXIDÁVEIS LEAN DUPLEX É COMPLEXO, NÃO SÓ PELA SUA ESTRUTURA BIFÁSICA, MÁS TAMBÉM DEVIDO A METAESTABILIDADE DA AUSTENITA, A QUAL PODE DEFORMAR POR DIFERENTES MECANISMOS E SE TRANSFORMAR EM MARTENSITA INDUZIDA POR DEFORMAÇÃO, (DIM). O OBJETIVO DESSE TRABALHO FOI INVESTIGAR AS ETAPAS DE DEFORMAÇÃO PLÁSTICA EM BAIXA INTENSIDADE (4 A 22%) EM UM AÇO INOXIDÁVEL LEAN DUPLEX 2204. AS AMOSTRAS FORAM ANALISADAS POR DIFRAÇÃO DE RAIOS-X, MICROSCOPIA ÓPTICA, DE VARREDURA E TRANSMISSÃO E ENSAIO DE TRAÇÃO. FORAM OBSERVADAS MACLAS DE DEFORMAÇÃO, MARTENSITA-Ε E MARTENSITA-Α’, AS QUAIS EVIDENCIARAM O EFEITO TRIP. A TAXA DE ENCRUAMENTO FOI CALCULADA E ANALISADA, BUSCANDO IDENTIFICAR OS MECANISMOS ATUANTES E DETERMINANTES NO COMPORTAMENTO DE ENCRUAMENTO DESSE AÇO, ONDE FOI POSSÍVEL NOTAR DOIS COMPORTAMENTOS DISTINTOS, ESCORREGAMENTO E MACLAÇÃO. OS EXAMES FRACTOGRÁFICOS REVELARAM QUE A FRATURA OCORREU NOS MODOS DE QUASI-CLIVAGEM E FORMAÇÃO DE MICRO CAVIDADES.

 

THE DEFORMATION MECHANISM OF LEAN DUPLEX STAINLESS STEEL IS OVERLY COMPLEX NOT ONLY BY THEIR DUAL PHASE MICROSTRUCTURE, BUT ALSO DUE TO METASTABLE AUSTENITE, WHICH CAN DEFORM BY DIFFERENT MECHANISMS AND TRANSFORM TO MARTENSITE BY STRAIN. THE PURPOSE OF THIS STUDY WAS TO INVESTIGATE THE STEPS OF DEFORMATION ON LOW DEFORMED SAMPLES OF 2204 LEAN DUPLEX STAINLESS STEEL AT LOW DEFORMATION LEVEL (4%-22%). THE MICROSTRUCTURE WAS ANALYZED BY X-RAY DIFFRACTION, OPTICAL MICROSCOPY, ELECTRON BACKSCATTERED DIFFRACTION, TRANSMISSION ELECTRON MICROSCOPY, AND TENSILE TEST. IT WAS OBSERVED MECHANICAL TWINNING, ε-MARTENSITE, AND α’-MARTENSITE WHICH EVIDENCED THE TRIP EFFECT. THE STRAIN HARDENING RATE WAS CALCULATED AND ANALYZED, AND TWO OPERATING MECHANISM WERE OBSERVED, SLIPING AND TWINNING. THE FRACTOGRAPHY ANALYSIS SHOWED A QUASI-CLEAVAGE AND DIMPLES FORMATION BEHAVIOR.

Palavras-chave

Lean-duplex; TRIP; macla; taxa de encruamento; energia de falha de empilhamento.

Lean-duplex; TRIP; twinning; strain-hardening; stacking fault energy.