Título

ESTUDO MORFOLÓGICO DA PASTA GEOPOLIMÉRICA COM ESCÓRIA DE ALTO FORNO (EAF) SUBMETIDA A VARIAÇÃO DE TEMPERATURA

MORPHOLOGICAL STUDY OF GEOPOLIMERICAN PULP WITH BLAST FURNACE SLA (SLA) SUBMITTED TO TEMPERATURE VARIATION

Autoria

Nascimento, Damares da Cruz Barbosa; Ferreira, Paulo Anderson Aranha; Corrêa, Thiago; Porto, Ana Beatriz Rodrigues; Monteiro, Sérgio Neves; Candido, Verônica Scarpini; Silva, Alisson Clay Rios da

DOI

10.5151/2594-5327-34976

Downloads

Baixar Artigo 9 Downloads

Resumo

OS GEOPOLIMEROS SÃO MATERIAIS INORGÂNICOS, ALUMINOSSILICATOS QUE SÃO PRODUZIDOS POR REAÇÃO DE GEOPOLIMERAÇÃO. EM FUNÇÃO DE APRESENTAREM PROPRIEDADES E CARATERÍSTICAS SUPERIORES AO CIMENTO PORTLAND, MUITAS PESQUISAS SÃO REALIZADAS PARA ASSEGURAR A IMPORTÂNCIA DO MATERIAL GEOPOLIMÉRICO NA CONSTRUÇÃO CIVIL. DIANTE DISTO, O OBJETIVO DESTE ESTUDO É PRODUZIR PASTAS GEOPOLÍMÉRICAS COM DIFERENTES FORMULAÇÕES DE ESCÓRIA DE ALTO FORNO (EAF), E POSTERIORMENTE SUBMETE-LAS A VARIAÇÕES DE TEMPERATURA, PARA EM SEGUIDA ANALISAR AS MORFOLOGIAS DOS CORPOS DE PROVA APÓS A FRATURA. PARA ESTE ESTUDO, FORAM UTILIZADOS METACAULIM, ESCÓRIA DE ALTO (EAF) COM FORMULAÇÕES DE 0%, 35%, 45% E 55%, E COMO SOLUÇÃO ATIVADORA FOI UTILIZADO DE HIDRÓXIDO DE POTÁSSIO (KOH) E SILICATO DE SÓDIO (NA2SIO3). POSTERIORMENTE, OS CORPOS DE PROVA OBTIDOS FORAM SUBMETIDOS A 300 ºC E 800 ºC. PARA ATINGIR O OBJETIVO DO ESTUDO, FORAM REALIZADAS CARATERIZAÇÕES DE MICROSCOPIA ÓPTICA (MO) E DIFRATOGRAMA DE RAIO – X PARA O GEOPOLÍMERO E ESCORIA DE ALTO FORNO, RESPECTIVAMENTE. COM ISSO, OS RESULTADOS APRESENTARAM QUE OS CORPOS DE PROVA COM FORMULAÇÃO DE 45% E 55% FORAM SUPERIORES QUE OS DEMAIS EM QUANDO SUBMETIDOS A 800 ºC, POR RESULTAREM EM MENOR QUANTIDADE DE POROS E MENOR QUANDO DE MATERIAL NÃO REAGIDO E TRINCAS.

 

GEOPOLYMERS ARE INORGANIC MATERIALS, ALUMINOSILICATES THAT ARE PRODUCED BY GEOPOLYMERIZATION REACTION. DUE TO THEIR SUPERIOR PROPERTIES AND CHARACTERISTICS TO PORTLAND CEMENT, MANY RESEARCHES ARE CARRIED OUT TO ENSURE THE IMPORTANCE OF GEOPOLYMER MATERIAL IN CIVIL CONSTRUCTION. IN VIEW OF THIS, THE OBJECTIVE OF THIS STUDY IS TO PRODUCE GEOPOLYMERIC PASTES WITH DIFFERENT BLAST FURNACE SLAG (EAF) FORMULATIONS, AND LATER SUBJECT THEM TO TEMPERATURE VARIATIONS, TO THEN ANALYZE THE MORPHOLOGIES OF THE SPECIMENS AFTER FRACTURE. FOR THIS STUDY, METAKAOLIN, HIGH SLAG (EAF) WITH FORMULATIONS OF 0%, 35%, 45% AND 55% WERE USED, AND POTASSIUM HYDROXIDE (KOH) AND SODIUM SILICATE (NA2SIO3) WERE USED AS ACTIVATING SOLUTION. SUBSEQUENTLY, THE SPECIMENS OBTAINED WERE SUBMITTED TO 300 ºC AND 800 ºC. TO ACHIEVE THE OBJECTIVE OF THE STUDY, OPTICAL MICROSCOPY (OM) AND X-RAY DIFFRACTOGRAM CHARACTERIZATIONS WERE PERFORMED FOR THE GEOPOLYMER AND BLAST FURNACE SLAG, RESPECTIVELY. THUS, THE RESULTS SHOWED THAT THE SPECIMENS WITH FORMULATIONS OF 45% AND 55% WERE SUPERIOR TO THE OTHERS WHEN SUBJECTED TO 800 ºC, AS THEY RESULT IN A SMALLER AMOUNT OF PORES AND LESS WHEN THE MATERIAL IS UNREACTED AND CRACKS.

Palavras-chave

Geopolímeros; Escoria de Alto Forno; Morfologia; Temperatura

Geopolymers; Blast Furnace Slag; Morphology; Temperature