EVA E PLA: FABRICAçãO E ADITIVOS DE FILAMENTOS 3D: EVA AND PLA: 3D FILAMENT MANUFACTURING AND ADDITIVES

O DESENVOLVIMENTO DE FILAMENTOS PARA IMPRESSORAS 3D FDM ENVOLVE UM PROCESSO COMPLEXO QUE ENVOLVE MISTURA DE POLíMEROS E ADITIVOS, EXTRUSãO EM ALTA TEMPERATURA E CONTROLE DE FRIO PARA GARANTIR UNIFORMIDADE E CONSISTêNCIA. NOVOS MATERIAIS SãO PROJETADOS PARA AJUDAR A CRIAR PRODUTOS DE PRECISãO COM USOS ESPECíFICOS. O áCIDO POLILáTICO (PLA) é AMPLAMENTE UTILIZADO NA IMPRESSãO 3D DEVIDO à SUA HISTóRIA CONTíNUA, BIODEGRADABILIDADE, BIOCOMPATIBILIDADE E PROPRIEDADES MECâNICAS E TéRMICAS SATISFATóRIAS. O EVA (ETILENO-ACETATO DE VINILA) é UM COPOLíMERO DE ETILENO E ACETATO DE VINILA QUE POSSUI PROPRIEDADES ELéTRICAS E TéRMICAS ADEQUADAS PARA MUITAS APLICAçõES INDUSTRIAIS, MAS APRESENTA DESAFIOS DE USO EM PAPEL DE IMPRESSãO 3D FDM, COMO BAIXA TEMPERATURA DE FUSãO E ALTA ELASTICIDADE. ESTA PESQUISA FOI DESENHADA PARA CRIAR UM FILAMENTO COMBINANDO EVA COM PLA PARA CONTROLAR A FLEXIBILIDADE DO EVA ATRAVéS DE UM PROCESSO DE EXTRUSãO A QUENTE COM UMA MINI-EXTRUSORA. OS FILAMENTOS RESULTANTES FORAM TESTADOS QUANTO à DENSIDADE E RESISTêNCIA à TRAçãO. A COMBINAçãO DE EVA E PLA CAUSA UM CONTROLE DA CADEIAS POLIMéRICAS, DIMINUINDO A CAPACIDADE ELáSTICA DO MATERIAL, A ANALISE DE MICROSCOPIA DE VARREDURA( MEV) MOSTRA NA SUPERFíCIE DE FRATURA NA PARTE EXTERNA UMA SUPERFíCIE DE FRATURA FRáGIL E NA PARTE INTERNA UMA SUPERFíCIE DE FRATURA DúCTIL.

THE DEVELOPMENT OF FILAMENTS FOR FDM 3D PRINTERS INVOLVES A COMPLEX PROCESS THAT INVOLVES MIXING POLYMERS AND ADDITIVES, HIGH-TEMPERATURE EXTRUSION AND COLD CONTROL TO ENSURE UNIFORMITY AND CONSISTENCY. NEW MATERIALS ARE DESIGNED TO HELP CREATE PRECISION PRODUCTS WITH SPECIFIC USES. POLYLACTIC ACID (PLA) IS WIDELY USED IN 3D PRINTING DUE TO ITS CONTINUOUS HISTORY, BIODEGRADABILITY, BIOCOMPATIBILITY, AND SATISFACTORY MECHANICAL AND THERMAL PROPERTIES. EVA (ETHYLENE VINYL ACETATE) IS A COPOLYMER OF ETHYLENE AND VINYL ACETATE THAT HAS ELECTRICAL AND THERMAL PROPERTIES SUITABLE FOR MANY INDUSTRIAL APPLICATIONS, BUT PRESENTS CHALLENGES FOR USE IN FDM 3D PRINTING PAPER, SUCH AS LOW MELTING TEMPERATURE AND HIGH ELASTICITY . THIS RESEARCH WAS DESIGNED TO CREATE A FILAMENT COMBINING EVA WITH PLA TO CONTROL THE FLEXIBILITY OF EVA THROUGH A HOT EXTRUSION PROCESS WITH A MINI-EXTRUDER. THE RESULTING FILAMENTS WERE TESTED FOR DENSITY AND TENSILE STRENGTH. THE COMBINATION OF EVA AND PLA CAUSES CONTROL OF THE POLYMER CHAINS, REDUCING THE ELASTIC CAPACITY OF THE MATERIAL. SCANNING MICROSCOPY ANALYSIS (SEM) SHOWS A FRAGILE FRACTURE SURFACE ON THE EXTERNAL PART AND A FRACTURE SURFACE ON THE INTERNAL PART. DUCTILE.

Palavras-chave

Manufatura aditiva; FusedDepositionModeling;Impressão 3D.

Additive manufacturing; Fused Deposition Modeling; 3D printing.

Como citar

GONCALVES, VICTOR PAES DIAS; LIMA, ELLEN BERNARDES DE; OLIVEIRA, JÚLIA AUDREM GOMES DE; FREITAS, LUIS FERNANDO FORTUNATO DE; VIEIRA, CARLOS MAURÍCIO FONTES; LOPES, FELIPE PERISSÉ DUARTE; LOPERA, HENRY ALONSO COLORADO. EVA E PLA: FABRICAçãO E ADITIVOS DE FILAMENTOS 3D , p. 3505-3514. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-41481