EVOLUÇÃO ESTRUTURAL DURANTE A DEFORMAÇÃO A QUENTE DE LIGA DE NITI INVESTIGADA POR DIFRAÇÃO DE RAIOS-X COM RADIAÇÃO DE SÍNCROTRON

STRUCTURAL EVOLUTION DURING HOT DEFORMATION OF NITI ALLOY INVESTIGATED BY X-RAY SYNCHROTRON DIFFRACTION

Autoria

Ferrão, Thiago Henrique Fernandes Dias; Rodrigues, Patrícia Freitas; Teixeira, Rodolfo da Silva; Santos, Fabiana da Silva; Sénéchal, Naiara Vieira Le; Casanova, Andrey de Moraes Barcelos; Paula, Andersan dos Santos; Fernandes, Francisco Manuel Braz

DOI

10.5151/1516-392X-266

Downloads

Baixar Artigo 185 Downloads

Resumo

As ligas de NiTi apresentam grande interesse devido as suas propriedades funcionais, tais como: efeito de memória de forma e superelasticidade. Tais propriedades são obtidas a partir dos processamentos termomecânicos. Esses processamentos permitem produzir materiais com formas adequadas de acordo com as aplicações finais e ainda controlar as temperaturas de transformação de fase, para aprimorar as características do material bem como suas propriedades funcionais. Ao aplicar o trabalho a quente no processamento deste tipo de liga adquirimos a microestrutura desejada para garantir o comportamento mecânico e propriedades funcionais adequados. Neste estudo o comportamento durante a deformação de uma amostra de NiTi rica em Ni, na condição bruta de fusão, foi investigado usando o ensaio de compressão a quente (850 ºC) com uma taxa de deformação 10-1 s-1. Os experimentos de difração de raio-x (DRX) e simulação termomecânica foram realizados na linha XRD1, LNLS – CNPEM, Campinas – Brasil. Os testes de compressão uniaxial foram realizados em um simulador termomecânico avançado, pelo sistema Gleeble® Synchrontron.

 

NiTi alloys have attractive functional properties as shape memory effect and the superelasticity appropriated to be used in different segments. These functional properties are obtained through the thermomechanical process. Thermomechanical processes aim to obtain the appropriate shape of the material, to control phase transformation temperatures, to improve the alloy characteristics, and refine shape memory effect or superelasticity. To obtain the desired microstructure the hot work should be performed to assure the mechanical and functional properties adequate. In this study, the hot deformation of NiTi was investigated using high-resolution in-situ synchrotron x-ray diffraction method. Diffraction patterns were recorded at four moments; prior at room temperature (as-cast condition); at 850 ºC (before deformation); under applied deformation at 850 ºC with a deformation rate of 10-1 s-1 and after cooling at room temperature. Thus, analyzed and interpreted in view of the evolution of structure and mechanical behavior. The X-ray scattering and Thermomechanical simulation (XTMS) experiment were carried out the XRD1 beamline, LNLS - CNPEM, Campinas - Brazil. The uniaxial compression tests were carried out on an advanced thermomechanical simulator, the Gleeble® Synchrotron system.

Palavras-chave

Processamento Termomecânico; Radiação de Síncrotron; NiTi Alloy.

Thermomechanical Process; Synchrotron Radiation; NiTi SMA.