EVOLUÇÃO MICROESTRUTURAL DAS LIGAS Al-3,5%Si E Al-4%Cu PRODUZIDAS A PARTIR DE ALUMÍNIO RECICLADO E CONDICIONADAS POR DEFORMAÇÃO: MICROSTRUCTURAL EVOLUTION OF THE ALLOY Al-3,5%Si and Al-4%Cu PRODUCED FROM RECYCLED ALUMINIUM AND CONDTIONED BY DEFORMATION

Alves, Gianni Ferreira; Romagna, Eric Moraes; Andreatta, Vinicius; Oliveira, José Roberto de; Filho, André Itman; Vieira, Estéfano Aparecido

doi:10.5151/2594-5300-20359

Anais do Seminário de Aciaria, Fundição e Metalurgia de Não-ferrosos

ISSN 2594-5300

12º Seminário de Metais Não Ferrosos — vol. 12, num.12 (2011)

Título

EVOLUÇÃO MICROESTRUTURAL DAS LIGAS Al-3,5%Si E Al-4%Cu PRODUZIDAS A PARTIR DE ALUMÍNIO RECICLADO E CONDICIONADAS POR DEFORMAÇÃO

MICROSTRUCTURAL EVOLUTION OF THE ALLOY Al-3,5%Si and Al-4%Cu PRODUCED FROM RECYCLED ALUMINIUM AND CONDTIONED BY DEFORMATION

Autoria

Alves, Gianni Ferreira; Romagna, Eric Moraes; Andreatta, Vinicius; Oliveira, José Roberto de; Filho, André Itman; Vieira, Estéfano Aparecido

10.5151/2594-5300-20359

Downloads

Baixar Artigo 48 Downloads

Resumo

Um dos pré-requisitos para as ligas conformadas na faixa de temperatura semi- sólida é que apresentem microestrutura não dendrítica. O presente trabalho analisa o comportamento microestrutural de duas ligas de alumínio com adições Cu ou Si produzidas a partir de latas recicladas e condicionadas por deformação para posterior processo de tixoconformação. Aqui se estudou a influência da deformação e do tempo de espera no ESS sobre a evolução microestrutural das novas ligas. Amostras foram deformadas de 5% a 30% e aquecidas até o estado semi-sólido (ESS) com o tempo de espera variando de 0 a 60 minutos. As microestruturas foram caracterizadas por microscopia ótica. Os resultados mostram que ambas as ligas sofrem modificações significativas na microestrutura final, em função do tempo de espera, e do nível de deformação imposto.

A requirement for forming alloys in a semi-solid range temperature is a non dendritic microstructure. This paper analyzes the microstructural behaviour of two aluminum alloys with Cu or Si additions produced from recycled cans and conditioned by deformation for later thixoforming. It were studied the deformation and the resting time in semi-solid state influence on the microstructural evolution of new alloys. Samples were worked from 5% to 30% and were taken to the semi solid state (SS) for a resting time ranging between 0 min to 60 min. The microstructures were characterized by optical microscopy. The results show that both alloys have significant changes in the final microstructure, depending on waiting time, and the strain imposed.

Palavras-chave

Tixoconformação; Semi-sólido; Condicionamento; Liga Al-Si; Liga Al-Cu.

Thixoforming; Semi-solid; Conditioning; Al-Si alloy; Al-Cu alloy.

Como citar

Alves, Gianni Ferreira; Romagna, Eric Moraes; Andreatta, Vinicius; Oliveira, José Roberto de; Filho, André Itman; Vieira, Estéfano Aparecido. EVOLUÇÃO MICROESTRUTURAL DAS LIGAS Al-3,5%Si E Al-4%Cu PRODUZIDAS A PARTIR DE ALUMÍNIO RECICLADO E CONDICIONADAS POR DEFORMAÇÃO , p. 273-280. In: 12º Seminário de Metais Não Ferrosos, São Paulo, 2011.
ISSN: 2594-5300 , DOI 10.5151/2594-5300-20359