FILMES DE POLIPROPILENO/ARGILA ORGANOFÍLICA. EFEITO DO TEOR DE ARGILA NA MORFOLOGIA E RESISTÊNCIA MECÂNICA Nanocompósitos PP/ Argila Organofílica

POLYPROPYLENE/ORGANOCLAY FILMS. EFFECT OF THE CLAY CONTENT ON THE MORPHOLOGY AND MECHANICAL PROPERTIES Polypropylene/ Organoclay Nanocomposites

Autoria

Tavares, Albaniza Alves; Silva, Diêgo Fabrício Alcântara; Gama, Débora Braga; Andrade, Daniela de Lourdes Anjos Coutinho Simões; Silva, Suédina Maria de Lima

DOI

10.5151/2594-5327-21409

Downloads

Baixar Artigo 94 Downloads

Resumo

Neste trabalho, filmes de polipropileno/argila organofílica foram preparados pelo processo de intercalação por fusão. O efeito do teor de argila organofílica na morfologia e resistência mecânica dos filmes foi investigado. A argila organofílica Cloisite 20A, da Southern Clay Products (Texas/EUA), foi dispersa na matriz de polipropileno (PP) compatibilizada com 15% em massa de polipropileno modificado com anidrido maléico (PP-g-MA) e filmes planos, preparados em extrusora Chill-Roll 16 da AX Plásticos, foram caracterizados por difratometria de raios X (DRX) e propriedades mecânicas (tração). Os resultados mostram que as cadeias de polipropileno foram intercaladas no espaçamento interlamelar (galerias) da argila organofílica, formando nanocompósitos intercalados. Mostram também que o teor de argila afetou a morfologia e resistência mecânica dos filmes preparados.

 

In this work, polypropylene/organoclay films were prepared by melt intercalation process. The effect of organoclay content on the morphology and strength of the films was investigated. The Cloisite 20A organoclay from Southern Clay Products (Texas/USA) was dispersed in the polypropylene (PP) matrix compatibilized with 15 wt% of polypropylene modified with maleic anhydride (PP-g-MA) and the films prepared in extruder Chill-Roll of 16 AX Plastics, were characterized by X-ray diffraction (XRD) and mechanical properties (tensile). The results show that the polypropylene chains were intercalated in interlayer spacing (gallery) of the organoclay and intercalated nanocomposites were obtained. Also show that the the morphology and strength of films prepared were affected by organoclay content.