FRATURA DE INSTRUMENTOS DE NITI PARA TRATAMENTO DE CANAIS DENTÁRIOS

FRACTURE OF NiTi ROTATORY INSTRUMENTS

Autoria

Elias, Carlos Nelson; Moreira, Edson Jorge Lima; Lopes, Hélio Pereira

DOI

10.5151/2594-5327-0342

Downloads

Baixar Artigo 38 Downloads

Resumo

O objetivo do presente trabalho foi determinar a vida média para ocorrer a fratura por flexão em rotação de instrumentos endodônticos de NiTi usados para tratamento de canais dentários. Foram utilizadas 40 limas de NiTi Profile .04 (Maillefer SA, Switzerland) e 40 limas SC Quantec (Analytic Endodontics, México). Dois tubos de náilon foram dobrados na forma de arcos com 90 e 135 graus para simular os canais dentários curvos. Os instrumentos foram inseridos nos tubos e acionados a 185 rpm até a fratura. A análise estatística ANOVA e o teste de Student indicaram que houve diferença significativa no tempo de fratura entre as marcas de instrumentos e com o tamanho do arco do canal simulado. Os instrumentos fraturaram com menor tempo em canais com arco de 135°. Os instrumentos Profile apresentaram vida média superior em relação aos instrumentos Quantec. O local de fratura dos instrumentos, independentemente da marca comercial, sempre ocorreu junto ao ponto médio do segmento curvo do canal. As superfícies apresentaram características de fratura dúctil.

 

This study evaluated the influence of angle (90 and 135 degree) of a curved canal to fracture NiTi rotatory instruments. NiTi Profile (Maillefer SA, Switzerland) and Quantec (Analytic Endodontics, Mexico) files were driven at 185 rpm in two simulated canals that measured 20 mm in length. The canals had the same radius (6mm) but different curved angle (90 and 135 degrees). The fracture surfaces were analyzed by scanning electron microscope. The results allowed conclude that the number of the cycles to induce fracture in the instruments was influenced by the angle and manufacturer. Profile rotatory instruments were more resistant than Quantec. Furthermore, by SEM it was observed that the helixes of the instruments. around the fracture point did not present plastic deformation and the surface of the fracture exhibited morphologic characteristics of ductile type fracture.

Palavras-chave

Instrumentos endodônticos; NiTi; Biomateriais; Canais dentários.

Rotatory instruments; NiTi; Biomaterials; Root canal