INCORPORAÇÃO DE RESÍDUOS DE VIDRO E DE QUARTZO EM ROCHA ARTIFICIAL PRODUZIDA COM RESINA EPÓXI

INCORPORATION OF GLASS AND QUARTZ WASTE IN ARTIFICIAL ROCK PRODUCED WITH EPOXY RESIN

Autoria

Barreto, Gabriela Nunes Sales

DOI

10.5151/2594-5327-34247

Downloads

Baixar Artigo 21 Downloads

Resumo

O PRESENTE TRABALHO APRESENTA COMO OBJETIVO O DESENVOLVIMENTO DE ROCHA ARTIFICIAL ATRAVÉS DO MÉTODO DE VIBRAÇÃO, COMPRESSÃO E VÁCUO A PARTIR DE RESÍDUOS DE QUARTZO E DE VIDRO DE EMBALAGENS TRANSPARENTES AGLOMERADOS POR RESINA EPÓXI. OS RESÍDUOS FORAM PREPARADOS E DISTRIBUÍDOS GRANULOMETRICAMENTE PELO MÉTODO DE PENEIRAMENTO FINO. POSTERIORMENTE, FORAM FEITOS TESTES QUE INDICARAM QUE A MISTURA DE MAIOR EMPACOTAMENTO CONTINHA 33,33% DE PARTÍCULAS FINAS, 33,33% DE PARTÍCULAS MÉDIAS E 33,33% DE PARTÍCULAS GROSSEIRAS E FOI CALCULADO O TEOR MÍNIMO DE RESINA EM 15%. AS PLACAS DE ROCHA ARTIFICIAL FORAM PREPARADAS COM 15 (RAVQ 15) E 20% (RAVQ 20) EM PESO DE RESINA EPÓXI COM VÁCUO DE 600 MMHG POR 20MIN A 90ºC E 10T DE PRESSÃO DE COMPACTAÇÃO. AS PLACAS FORAM LIXADAS E CORTADAS NAS DIMENSÕES ADEQUADAS PARA QUE FOSSE REALIZADOS ENSAIOS PARA DETERMINAR OS ÍNDICES FÍSICOS (DENSIDADE APARENTE, ABSORÇÃO DE ÁGUA E POROSIDADE APARENTE) E A RESISTÊNCIA A FLEXÃO EM 3 PONTOS. OS RESULTADOS ENCONTRADOS SÃO SIMILARES AOS ENCONTRADOS POR OUTROS AUTORES E COMPARÁVEIS A ROCHAS ARTIFICIAIS COMERCIAIS. ALÉM DISSO, CLASSIFICARAM AS ROCHAS PRODUZIDAS COMO MATERIAIS DE REVESTIMENTO DE ALTA QUALIDADE.

 

THE PRESENT WORK’S MAIN GOAL IS THE DEVELOPMENT OF ARTIFICIAL STONE THROUGH VIBRATION, COMPRESSION AND VACUUM METHOD, FROM QUARTZ WASTE AND GLASS WASTE FROM TRANSPARENT PACKAGING, AGGLOMERATED BY EPOXY RESIN. WASTES WERE PREPARED AND DISTRIBUTED GRANULOMETRICALLY BY THE FINE SIEVING METHOD. SUBSEQUENTLY, TESTS INDICATED THAT THE MOST CLOSED-PACKED MIXTURE CONTAINED 33.33% OF FINE PARTICLES, 33.33% OF MEDIUM PARTICLES AND 33.33% OF COARSE PARTICLES AND THE MINIMUM RESIN CONTENT WAS CALCULATED AT 15%. THE ARTIFICIAL STONE PLATES WERE PREPARED WITH 15 (RAVQ 15) AND 20% (RAVQ 20) WEIGHT OF EPOXY RESIN BY THE VIBRATION, COMPRESSION AND VACUUM METHOD (600MMHG FOR 20MIN AT 90ºC AND 10T OF COMPACTION PRESSURE). THE PLATES WERE SANDED AND CUT TO THE APPROPRIATE DIMENSIONS SO THAT TESTS COULD BE PERFORMED IN ORDER TO DETERMINE THE PHYSICAL INDICES (APPARENT DENSITY, WATER ABSORPTION AND APPARENT POROSITY) AND 3 POINT BEND STRENGTH. THE RESULTS ARE WITHIN THE RANGE OF VALUES FOUND BY OTHER AUTHORS, IN ADDITION TO BEING COMPARABLE TO COMMERCIAL ARTIFICIAL STONE. BESIDES, THEY CLASSIFIED THE STONE PRODUCED AS HIGH QUALITY COATING MATERIALS.

Palavras-chave

Rocha artificial; Resíduos; Vidro; Quartzo; Resina epóxi.

Artificial stone; Wastes; Glass; Quartz; Epoxy resin