INCORPORAÇÃO DO GESSO DE FGD EM CERÂMICA VERMELHA: INCORPORATION OF FGD GYPSUM IN RED CERAMICS

O AUMENTO DO CONSUMO POPULACIONAL E DA CULTURA DO PRODUTO DESCARTÁVEL, TEM DEMANDADO CADA VEZ MAIS A BUSCA POR PROCESSOS EFICIENTES E TECNOLOGIAS LIMPAS, BUSCANDO EVITAR UM CRESCIMENTO DESCONTROLADO NA GERAÇÃO DE RESÍDUOS SÓLIDOS. UMA ALTERNATIVA É A INCORPORAÇÃO DE RESÍDUOS NAS MASSAS ARGILOSAS UTILIZADAS NA INDÚSTRIA DA CERÂMICA VERMELHA. O OBJETIVO DESSE TRABALHO FOI DE AVALIAR OS EFEITOS DA INCORPORAÇÃO DE RESÍDUO GESSO DE FGD EM CERÂMICA VERMELHA VISANDO UMA DESTINAÇÃO AMBIENTALMENTE CORRETA. A FLUORESCÊNCIA DE RAIOS-X VERIFICOU QUE A ARGILA É COMPOSTA POR ALUMINO-SILICATOS, POSSUI ALTA PERDA AO FOGO E BAIXO TEOR DE ÓXIDOS ALCALINOS FUNDENTES. O RESÍDUO É BASICAMENTE UM SULFATO DE CÁLCIO. PARA A RETRAÇÃO LINEAR, OS MAIORES VALORES FORAM ENCONTRADOS NAS FORMULAÇÕES QUEIMADAS À TEMPERATURA DE 900°C. TODAS AS FORMULAÇÕES PROPORCIONARAM REDUÇÃO DA ABSORÇÃO DE ÁGUA ONDE OS VALORES ENCONTRADOS FICARAM ENTRE 8 A 25%. FOI VERIFICADO QUE HOUVE UM AUMENTO DA RESISTÊNCIA MECÂNICA COM O INCREMENTO DO GESSO DE FGD NA FORMULAÇÃO DAS MASSAS CERÂMICAS. DESTA FORMA, PODE-SE CONCLUIR QUE O RESÍDUO GESSO DE FGD TEM UM ENORME POTENCIAL PARA SER UTILIZADO COMO MATÉRIA-PRIMA EM MASSAS ARGILOSAS, SENDO ESTA UMA DESTINAÇÃO MAIS ADEQUADA E AMBIENTALMENTE CORRETA PARA ELE

THE INCREASE IN POPULATION CONSUMPTION AND THE CULTURE OF THE DISPOSABLE PRODUCT, HAS INCREASINGLY DEMANDED THE SEARCH FOR EFFICIENT PROCESSES AND CLEAN TECHNOLOGIES, SEEKING TO AVOID AN UNCONTROLLED GROWTH IN THE GENERATION OF SOLID WASTE. AN ALTERNATIVE IS THE INCORPORATION OF RESIDUES IN THE CLAY MASSES USED IN THE RED CERAMIC INDUSTRY. THE OBJECTIVE OF THIS WORK WAS TO EVALUATE THE EFFECTS OF INCORPORATING FGD GYPSUM WASTE INTO RED CERAMICS, AIMING AT AN ENVIRONMENTALLY CORRECT DESTINATION. THE X-RAY FLUORESCENCE VERIFIED THAT THE CLAY IS COMPOSED OF ALUMINOSILICATES, HAS HIGH LOSS ON FIRE AND LOW CONTENT OF ALKALINE OXIDES. THE RESIDUE IS BASICALLY CALCIUM SULFATE. FOR LINEAR SHRINKAGE, THE HIGHEST VALUES WERE FOUND IN ALL FORMULATIONS THAT WERE BURNED AT 900 ° C. ALL FORMULATIONS PROVIDED A REDUCTION IN WATER ABSORPTION WHERE THE VALUES FOUND WERE BETWEEN 8 TO 25%. IT WAS VERIFIED THAT THERE WAS AN INCREASE OF THE MECHANICAL RESISTANCE WITH THE INCREASE OF THE PLASTER OF FGD IN THE FORMULATION OF THE CERAMIC MASSES. IN THIS WAY, IT CAN BE CONCLUDED THAT FGD GYPSUM WASTE HAS ENORMOUS POTENTIAL TO BE USED AS RAW MATERIAL IN CLAY MASSES, WHICH IS A MORE SUITABLE AND ENVIRONMENTALLY CORRECT DESTINATION FOR IT.

Palavras-chave

Cerâmica vermelha; Gesso de FGD; Resíduos sólidos

Red ceramics; FGD gypsum; Solid waste

Como citar

Gallo, Daniel Passos; Delaqua, Geovana Carla Girondi; Lopera, Henry Alonso Colorado; Vieira, Carlos Maurício Fontes. INCORPORAÇÃO DO GESSO DE FGD EM CERÂMICA VERMELHA , p. 2515-2527. In: 75° Congresso Anual da ABM, São Paulo, 2022.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-34406