Título

INFLUÊNCIA DA TEMPERATURA DE TRATAMENTO TÉRMICO NA MORFOLOGIA E FRAÇÃO DE FASES DE UM AÇO INOXIDÁVEL DUPLEX DO TIPO UNS S32304

INFLUENCE OF HEAT TREATMENT TEMPERATURE ON MORPHOLOGY AND PHASE FRACTIONS IN A DUPLEX STAINLESS STEEL TYPE UNS S32304

DOI

10.5151/1516-392X-26175

Downloads

Baixar Artigo 757 Downloads

Resumo

Os Aços Inoxidáveis Duplex possuem uma estrutura constituída basicamente por ferrita e austenita na proporção aproximada de 50%. Este trabalho estudou a influência da temperatura de um tratamento térmico na morfologia e fração de ferrita e austenita no aço UNS S32304. Os tratamentos térmicos realizados consistiram no aquecimento das amostras, desde a temperatura ambiente até a temperatura de 1250°C, seguido de um resfriamento lento em um segundo forno estável em uma determinada temperatura. As amostras permaneceram neste segundo forno por um intervalo de tempo necessário para que suas temperaturas atingissem exatamente um valor desejado, sendo então imediatamente retiradas e resfriadas em água a 20°C para preservar a estrutura resultante do ciclo térmico aplicado. As amostras foram metalograficamente preparadas, atacadas e analisadas com o auxílio de um microscópio ótico. As frações de fases medidas por MO se aproximaram dos resultados obtidos por simulação utilizando o software Thermo-Calc. A morfologia das fases variou significativamente com a diminuição da temperatura de tratamento, uma vez que a austenita se mostrou mais fragmentada nas temperaturas mais baixas, porém o bandeamento não deixou de existir na estrutura.A transformação da ferrita em austenita se mostrou fortemente dependente do tempo.

 

The Duplex Stainless Steels have a structure composed mainly of ferrite and austenite in the approximate ratio of 50%. This work studied the influence of heat treatment temperatureon themorphologies and fractions of ferrite and austenite in the UNS S32304 steel. The applied heat treatment consisted of heating the sample from roomtemperature until 1250°C followed by slow cooling in a second stable furnace at a certain temperature. The samples remained in thisfurnaceuntil their temperatures reacheda desired value, and then they were removed and immediately cooled in water at 20°C aiming to preserve the structuresobtained from the applied treatments. The samples were metallographically prepared and analyzed with the aid of an optical microscope (OM). The phase fraction measurements, done inOM,were close tothe results obtained by computational simulation, using the Thermo-Calc software. The phase morphologies varied significantly as the temperature decreasewith the heat treatment temperature decreasing.At lower temperature, there are more fragmented austenite grains. However, for all studied conditions, the banded structure still exists.The ferrite to austenite transformation were strongly time dependent.

Palavras-chave

Transformação de fases, Morfologia, Aço inoxidável duplex UNS S32304

Phase transformation, Morphology, Duplex stainless steel UNS S32304

Como citar

Magalhães, Charles Henrique Xavier Morais; Faria, Geraldo Lúcio de; Godefroid, Leonardo Barbosa; Lagoeiro, Leonardo Evangelista; Nakamura, Leandro. INFLUÊNCIA DA TEMPERATURA DE TRATAMENTO TÉRMICO NA MORFOLOGIA E FRAÇÃO DE FASES DE UM AÇO INOXIDÁVEL DUPLEX DO TIPO UNS S32304 , p. 55-64. In: 70º Congresso Anual da ABM, Rio de Janeiro, 2015.