INFLUÊNCIA DO CROMO E NIÓBIO NO DESEMPENHO QUANTO AO DESGASTE ABRASIVO EM REVESTIMENTOS DUROS

INFLUENCE OF CHROMIUM AND NIOBIUM IN PERFORMANCE ON ABRASIVE WEAR IN HARD COATINGS.

DOI

10.5151/1516-392X-30835

Downloads

Baixar Artigo 357 Downloads

Resumo

Na indústria da mineração, a liga Fe-Cr-C destaca-se como um revestimento duro em chapas de desgaste objetivando aumentar a vida útil do ativo. Três ligas, duas delas contendo Fe-Cr-C, sendo uma com aproximadamente 28% (p) de Cr e outra com 38% (p) de Cr e uma terceira liga com 24% (p) de Cr e 7,0% (p) de Nb foram levadas a ensaios de desgaste abrasivo roda de borracha conforme norma ASTM G65-04, além de medições de dureza, microdureza e caracterizações microestruturais. Constatou-se que os revestimentos contendo Nb, depositados com uma ou duas camadas de solda, possuem maior resistência ao desgaste abrasivo, seguidos pelos com maior teor de Cr. Os revestimentos que possuem maior fração volumétrica de carbonetos, finamente distribuídos na matriz, apresentaram os melhores resultados na resistência ao desgaste. Analisando no microscópio confocal 3D os revestimentos contendo Cr, notou-se que os mecanismos de desgaste são do tipo microcorte e microssulcamento, enquanto naqueles contendo nióbio prevalece o desgaste por rolamento em boa parte da superfície. A liga contendo Nb apresenta o melhor desempenho na resistência ao desgaste abrasivo em relação às demais, e se torna viável economicamente sua aplicação na indústria.

 

In the mining industry, the Fe-Cr-C alloy stands out as a hard coating on wear plates in order to increase the useful life of the active. Three alloys, two of them containing Fe-Cr-C, one with approximately 28% (p) Cr and another with 38% (p) Cr and one third alloy was specified with 24% (w) of Cr and 7.0% (w) of Nb were subjected to abrasive wear tests rubber wheel according to standard ASTM G65-04, in addition to hardness measurements, microhardness and microstructural characterization by. It was found that Nb coatings deposited with one or two layers of solder have higher resistance to abrasive wear, followed by coatings with higher Cr. The coatings that have the largest volumetric fraction of carbides, finely distributed in the matrix, presented the best results in the resistance to wear. Analyzing the Cr containing coatings on the 3D confocal microscope, it was observed that the mechanisms of wear are of the microccuting and microploughing, while in those containing niobium, the rolling wear prevails in a good part of the surface. The alloy containing Nb presents the best performance in the resistance to abrasive wear in relation to the others and it becomes economically viable its application in the industry.

Palavras-chave

Revestimentos duros, Transferência de minério e pelotas, Mecanismos de desgaste.

Hard coatings, Transfer of ore and pellets, Mechanisms of wear.